The study of cationic waterborne polyurethanes modified by two different forms of polydimethylsiloxane

Two kinds of dimethylpolysiloxane, KF-6001 and X-22-176-DX, were used to modify polyurethane. The effects of KF-6001 and X-22-176-DX on the colloidal, physico-chemical and surface properties were studied for polydimethylsiloxane modified cationic waterborne polyurethanes (SiCWPUs). The chemical structures and the surface morphologies of the SiCWPUs are characterized via Fourier transform infrared spectrometry and scanning electron microscopy. The results showed that the addition of siloxane changes the structure and surface morphology of the polyurethane. The element distributions in the polymer films were tested via X-ray photoelectron spectroscopy, and the effect of the hydrophobicity of the surfaces of the polymer films of the cationic waterborne polyurethanes was demonstrated via water contact angle tests on the surfaces of the films. As the amount of siloxane added increases, the silicon content on the surfaces of the SiCPWU1 films increases from 0% to 17.92%, and the actual silicon content on the surfaces of the films was much larger than the theoretical value. Therefore, the hydrophobicity of the membrane surface increases sharply, and the contact angle increases from 63.0° to 105.3°. Dynamic mechanical analysis indicates that the introduction of polydimethylsiloxane into the cationic aqueous polyurethane chain increases microphase separation in the polymer films. Stress–strain data showed that the mechanical properties of SiCPWU1 films were better than those of SiCPWU2 films when the same amounts of PDMS were added.

Two kinds of dimethylpolysiloxane, KF-6001 and X-22-176-DX, were used to modify polyurethane.

Superhydrophobic hierarchical arrays fabricated by a scalable colloidal lithography approach

Here we report an unconventional colloidal lithography approach for fabricating a variety of periodic polymer nanostructures with tunable geometries and hydrophobic properties. Wafer-sized, double-layer, non-close-packed silica colloidal crystal embedded in a polymer matrix is first assembled by a scalable spin-coating technology. The unusual non-close-packed crystal structure combined with a thin polymer film separating the top and the bottom colloidal layers render great versatility in templating periodic nanostructures, including arrays of nanovoids, nanorings, and hierarchical nanovoids. These different geometries result in varied fractions of entrapped air in between the templated nanostructures, which in turn lead to different apparent water contact angles. Superhydrophobic surfaces with >150° water contact angles and <5° contact angle hysteresis are achieved on fluorosilane-modified polymer hierarchical nanovoid arrays with large fractions of entrapped air. The experimental contact angle measurements are complemented with theoretical predictions using the Cassie's model to gain insights into the fundamental microstructure-dewetting property relationships. The experimental and theoretical contact angles follow the same trends as determined by the unique hierarchical structures of the templated periodic arrays.