Modulating Carrier Type for Enhanced Thermoelectric Performance of Single-Walled Carbon Nanotubes/Polyethyleneimine Composites

Thermoelectric (TE) generators consisting of flexible and lightweight p- and n-type single-walled carbon nanotube (SWCNT)-based composites have potential applications in powering wearable electronics using the temperature difference between the human body and the environment. Tuning the TE properties of SWCNTs, particularly p- versus n-type control, is currently of significant interest. Herein, the TE properties of SWCNT-based flexible films consisting of SWCNTs doped with polyethyleneimine (PEI) were evaluated. The carrier type of the SWCNT/PEI composites was modulated by regulating the proportion of SWCNTs and PEI using simple mixing techniques. The as-prepared SWCNT/PEI composite films were switched from p- to n-type by the addition of a high amount of PEI (>13.0 wt.%). Moreover, interconnected SWCNTs networks were formed due to the excellent SWNT dispersion and film formation. These parameters were improved by the addition of PEI and Nafion, which facilitated effective carrier transport. A TE generator with three thermocouples of p- and n-type SWCNT/PEI flexible composite films delivered an open circuit voltage of 17 mV and a maximum output power of 224 nW at the temperature gradient of 50 K. These promising results showed that the flexible SWCNT/PEI composites have potential applications in wearable and autonomous devices.

Fabrication of Porous Polyvinylidene Fluoride/Multi-Walled Carbon Nanotube Nanocomposites and Their Enhanced Thermoelectric Performance

In this paper, a solvent vapor-induced phase separation (SVIPS) technique was used to create a porous structure in polyvinylidene fluoride/Multi-walled carbon nanotube (PVDF/MWNTs) composites with the aim of increasing the electrical conductivity through the incorporation of MWNTs while retaining a low thermal conductivity. By using the dimethylformamide/acetone mixture, porous networks could be generated in the PVDF/MWNTs composites upon the rapid volatilization of acetone. The electrical conductivity was gradually enhanced by the addition of MWNTs. At the same time, the thermal conductivity of the PVDF film could be retained at 0.1546 W·m⁻¹·K⁻¹ due to the porous structure being even by loaded with a high content of MWNTs (i.e., 15 wt.%). Thus, the Seebeck coefficient, power factor and figure of merit (ZT) were subsequently improved with maximum values of 324.45 μV/K, 1.679 μW·m⁻¹·K⁻², and 3.3 × 10⁻³, respectively. The microstructures, thermal properties, and thermoelectric properties of the porous PVDF/MWNTs composites were studied. It was found that the enhancement of thermoelectric properties would be attributed to the oxidation of MWNTs and the porous structure of the composites. The decrease of thermal conductivity and the increase of Seebeck coefficient were induced by the phonon scattering and energy-filtering effect. The proposed method was found to be facile and effective in creating a positive effect on the thermoelectric properties of composites.