Experimental Design and Statistical Analysis of AGET ATRP of MMA in Emulsion Polymer Reactor

Experimental Investigation of Methyl Methacrylate in Stirred Batch Emulsion Reactor: AGET ATRP Approach

This study examines the ab initio emulsion atom transfer radical polymerization (ATRP) initiated by an eco-friendly reducing agent to produce poly(methyl methacrylate) (PMMA) polymer with controlled characteristics in a 2 L stirred batch reactor. The effect of the reaction temperature, surfactant concentration, monomer to water ratio, and stirring speed was thoroughly investigated. The results showed that PMMA coagulation becomes quite severe at a certain temperature threshold. However, the coagulation could be avoided at mild reaction temperature, since the outcomes showed that loading more surfactant to the system under high mixing speed has balanced the polymer mixture and yielded high monomer conversion. The PMMA product was analyzed by gravimetry and GPC measurements and after 5 h of polymerization at a reaction temperature of 50 °C, monomer conversion of 64.1% was obtained, and PMMA polymer samples produced had an average molar mass of 4.5 kg/mol and a polydispersity index of 1.17. The structure of the PMMA polymer was successfully proved by FTIR and nuclear magnetic resonance (NMR) spectroscopy. The results confirm the living feature of MMA AGET ATRP in emulsion medium and recommend further investigation for other types of surfactant.

Emulsifier-Free Acrylate-Based Emulsion Prepared by Reverse Iodine Transfer Polymerization

The self-emulsifying acrylate-based emulsions with solid content 45 wt.% were prepared in 3.5 h by reverse iodine transfer polymerization (RITP), and the polymer molecular weight (Mn) could be 30,000 g·mol-1. The influences of methacrylic acid (MAA) amount, soft/hard monomer mass ratio, and iodine amount on polymerization and latex were investigated. A moderate amount of ionized MAA was needed to stabilize the emulsion. Glass transition temperature (Tg) was decreased with the increasing mass ratio of soft/hard monomer. A higher iodine amount resulted in lower Mn. The increased Mn after chain extension of the polymer with water-insoluble monomers in iterative one-pot method proved the living of polymer. Compared with conventional emulsion polymerization, molecular weight (Mn) could be controlled, and Mn of polymer synthesized in RITP emulsion polymerization is higher; emulsion of polyacrylate-containing hydroxyl monomer units prepared by RITP emulsifier-free radical polymerization is more stable. Good properties, such as hardness, water resistance, adhesion, and increased value of maximum tensile of films modified by reaction of polyacrylate with melamine-formaldehyde (MF) resin, indicated potential application in baking coating.