Thermal and optical properties of some phosphorus-containing poly(1,3,4-oxadiazole-ester-imide)s

Liquid crystalline hyperbranched polyesters with phosphorus functional groups

Liquid crystalline hyperbranched poly(aryl ester)s (A2B3) were prepared by polycondensation reaction of 2-(6-oxido-6H-dibenz<c,e><1,2>oxaphosphorin-6-yl)1,4-naphthalene diol with 1,3,5-benzenetricarbonyl trichloride, taken in two different molar ratios. The chemical structure of the newly synthesized hyperbranched polymers was confirmed by FTIR, 1H NMR, 13C NMR spectroscopy. The polymers exhibited high thermal stability with initial decomposition temperature above 410–435°C and char yield at 700°C higher than 40%. Combined differential scanning calorimetry, polarized optical microscopy and wide-angle X-ray diffraction measurements were carried out to closely examine their thermal behavior and phase transitions.

Synthesis and photophysical study of new blue fluorescent poly(azomethine-1,3,4-oxadiazole)s containing dimethylamino groups

New aromatic polyazomethines were synthesized by polycondensation reaction of a diamine containing 1,3,4-oxadiazole ring, namely, 4,4′-diamino-4″-[2-(4-phenoxy)-5-(4-dimethylaminophenyl)-1,3,4-oxadiazole)]triphenylmethane, with terephthalic aldehyde or bis(4-formylphenoxyphenyl)fluorene, by using N-methyl-2-pyrrolidinone (NMP) as solvent. The polymers were easily soluble in polar solvents, such as NMP, N, N-dimethylacetamide, or chloroform, and showed high thermal stability with the initial decomposition temperature above 415°C and the temperature of 10% weight loss in the range of 450–460°C. They exhibited high char yield at 800°C in the range of 52–56%. Optical properties were studied by absorption and photoluminescence spectra. In solution, the polymers presented two absorption maxima in the ranges 273–278 and 330–346 nm and emitted violet-blue light in the range of 413–468 nm, depending on the solvent polarity. The Stokes shift and emission quantum yield values depend on the polymer structure and solvent polarity. The emission intensity in NMP solution was enhanced upon increasing the HCl concentration, while the absorption spectral profile was slightly influenced.

Phosphorus-containing polyimide fibers and their thermal properties

Submicron fibers based on phosphorus-containing polyimide were successfully prepared and characterized for their thermal properties.

Physical and thermal properties of poly(ethylene terephthalate) fabric coated with electrospun polyimide fibers

Two analogous polyimides (PIs) containing flexible isopropylidene units were prepared. One was based on 4,4′-oxydiphthalic anhydride and 4,4′-(4,4′-isopropylidenediphenyl-1,1′-diyldioxy) dianiline and the other was based on 4,4′-(4,4′-isopropylidenediphenoxy) bis(phthalic anhydride) and bis(3-aminophenyl) methyl phosphine oxide. The ability of these two PIs to form uniform nanoscaled fibers was investigated by electrospinning technique. At optimal spinning conditions, PI fibers were electrospun onto the surface of woven poly(ethylene terephthalate) (PET) support to form a bilayer composite structure. These new fabric systems were analyzed regarding morphology, air permeability, wetting properties, and thermal stability. It was expected that the new PET/PI mats would possess enhanced properties compared with the initial woven PET fibers due to the excellent properties of PIs. Experimental results showed that PET woven substrate coated with electrospun PI fibers had improved values of air permeability, water contact angle and thermal stability when compared with the initial woven PET fibers.