From Poly(glycerol itaconate) Gels to Novel Nonwoven Materials for Biomedical Applications

Electrospinning is a process that has attracted significant interest in recent years. It provides the opportunity to produce nanofibers that mimic the extracellular matrix. As a result, it is possible to use the nonwovens as scaffolds characterized by high cellular adhesion. This work focused on the synthesis of poly(glycerol itaconate) (PGItc) and preparation of nonwovens based on PGItc gels and polylactide. PGItc gels were synthesized by a reaction between itaconic anhydride and glycerol. The use of a mixture of PGItc and PLA allowed us to obtain a material with different properties than with stand-alone polymers. In this study, we present the influence of the chosen ratios of polymers and the OH/COOH ratio in the synthesized PGItc on the properties of the obtained materials. The addition of PGItc results in hydrophilization of the nonwovens' surface without disrupting the high porosity of the fibrous structure. Spectral and thermal analyzes are presented, along with SEM imagining. The preliminary cytotoxicity research showed that nonwovens were non-cytotoxic materials. It also helped to pre-determine the potential application of PGItc + PLA nonwovens as subcutaneous tissue fillers or drug delivery systems.

Optimization of the Poly(glycerol citraconate) Synthesis Using the Box-Behnken Design

This work aimed to obtain poly(glycerol citraconate) (PGCitrn) for biomedical applications, analyze the obtained polyester by spectroscopic methods, and optimize its preparation. Polycondensation reactions of glycerol and citraconic anhydride were carried out. It was provided that the results in the reaction are oligomers of poly(glycerol citraconate). Optimization studies were carried out based on the Box-Behnken design. The input variables in this plan were the ratio of functional groups, temperature, and time and occurrence in coded form: -1, 0, or 1. Three output variables were optimized: the degree of esterification, the percentage of Z-mers, and the degree of carboxyl group conversion; they were determined by titration and spectroscopic methods. The optimization criterion was to maximize the values of output variables. A mathematical model and an equation describing it were determined for each output variable. The models predicted the experimental results well. An experiment was conducted under determined optimal conditions. The experimental results were very close to the calculated values. Poly(glycerol citraconate) oligomers with an esterification degree of 55.2%, a Z-mer content of 79.0%, and a degree of rearrangement of carboxyl groups of 88.6% were obtained. The obtained PGCitrn can serve as a component of an injectable implant. The obtained material can be used to produce nonwoven fabrics (with the addition of PLLA, for example), which can be subjected to a cytotoxicity test which can then serve as a dressing material.

Optimisation of Glycerol and Itaconic Anhydride Polycondensation

Glycerol polyesters have recently become objects of interest in tissue engineering. Barely known so far is poly(glycerol itaconate) (PGItc), a biocompatible, biodegradable polyester. Due to the presence of a C=C electron-acceptor moiety, it is possible to post-modify the product by Michael additions to change the properties of PGItc. Thus, using PGItc as one of the elements of cellular scaffold crosslinked in situ for bone tissue regeneration seems to be a very attractive yet unexplored solution. This work aims to optimize the synthesis of PGItc to obtain derivatives with a double bond in the side chain with the highest conversion rates. The experiments were performed with itaconic anhydride and glycerol using mathematical planning of experiments according to the Box-Behnken plan without solvent and catalyst. The input variables of the process were the ratio of the OH/COOH, temperature, and reaction time. The optimised output variables were: the degree of esterification (EDtitr), the degree of esterification calculated from the analysis of 1H NMR spectra (EDNMR), and the degree of itaconic anhydride conversion—calculation based on 13C NMR spectra (%X13CNMR). In each of statistical models, the significance of the changed synthesis parameters was determined. Optimal conditions are when OH/COOH ratio is equal to 1.5, temperature is 140 °C and time of reaction is 5 h. The higher OH/COOH ratio, temperature and longer the experiment time, the higher the value of the degree of esterification and the degree of anhydride conversion.