Enhancing the Interfacial Properties of Composites by Grafting Polyethylene Glycol and Polyvinyl Alcohol Onto a CF Surface

Quantitative Analysis of Morphology and Surface Properties of Poly(lactic acid)/Poly(ε-caprolactone)/Hydrophilic Nano-Silica Blends

A quantitative analysis of the morphology, as well as an analysis of the distribution of components and surface/interfacial properties in poly(lactic acid)(PLA) InegoTM 3251D, poly(ε-caprolactone) (PCL) Capa 6800 and nano-silica (SiO2) Aerosil®200 blends, was conducted in this research. The study aimed to improve the understanding of how PLA, PCL, and nano-SiO2 interact, resulting in the specific morphology and surface properties of the blends. Samples were produced by varying the concentration of all three components. They were analyzed using SEM, EDS mapping, water contact angle measurements, surface free energy calculation, adhesion parameter measurements, and FTIR-ATR spectroscopy. The results showed that the addition of SiO2 nanoparticles led to an increase in the contact angle of water, making the surface more hydrophobic. SEM images of the blends showed that increasing the PCL content reduced the size of spherical PCL elements in the blends. FTIR-ATR analysis showed that SiO2 nanoparticles influenced the structure ordering of PLA in the blend with equal portions of PLA and PCL. In the samples with a higher PCL content, the spherical elements present in the samples with a higher PLA/PCL ratio have been reduced, indicating better interactions at the interface between PLA, PCL, and SiO2. SEM-EDS mapping of the PLA/PCL 100/0 blend surfaces revealed the presence of SiO2 clusters and the silicon (Si) concentration reaching up to ten times higher than the nominal concentration of SiO2. However, with the addition of 3% SiO2 to the blend containing PCL, the structure became more granular. Specifically, Si protrusions in the sample PLA/PCL 90/10 with 3% SiO2 displayed 29.25% of Si, and the sample PLA/PCL 70/30 with 3% SiO2 displayed an average of 10.61% of Si at the protrusion locations. The results confirmed the affinity of SiO2 to be encapsulated by PCL. A better understanding of the interactions between the materials in the presented blends and the quantitative analysis of their morphology could improve the understanding of their properties and allow the optimization of their application for different purposes.

Slow-release lubrication of artificial joints using self-healing polyvinyl alcohol/polyethylene glycol/ graphene oxide hydrogel

New fabrication methods and lubrication materials must be developed to improve the lubrication performance of artificial joints and increase the lubrication duration. Herein, a novel polyvinyl alcohol/polyethylene glycol/graphene oxide (PVA/PEG/GO) hydrogel was prepared by a physical cross-linking method, and then the hydrogel and its sustained-release solution were used as lubricant for friction evaluation. The results demonstrated that the slow-release gel solution has good lubrication performance, and coefficient of friction (COF) is only 0.04, which is much lower than the COF of distilled water (about 0.08) under the same conditions. The structure characterization results revealed that no new materials are formed in the gel. The results of thermogravimetric analyses and differential scanning calorimetry demonstrated that the addition of GO may improve the network crosslinking structure of the PVA/PEG hydrogel and improve its mechanical strength. In addition, PVA/PEG/GO hydrogel has superior self-healing function. The self-healing hydrogel did not break again after being pulled under 200 G of weights. The PVA/PEG/GO hydrogel with excellent slow-release lubricating performance and self-healing properties provides a novel candidate for design of long-term lubricating artificial joints, and is expected to promote the progress of artificial joint lubrication applications.