Recent advances on melt-spun fibers from biodegradable polymers and their composites

Biodegradable polymers have become important in different fields of application, where biodegradability and biocompatibility are required. Herein, the melt spinning of biodegradable polymers including poly(lactic acid), poly(butylene succinate), polyhydroxyalkanoate (PHA), poly(ɛ-caprolactone) and their biocomposites is critically reviewed. Biodegradable polymer fibers with added functionalities are in high demand for various applications, including biomedical, textiles, and others. Melt spinning is a suitable technique for the development of biodegradable polymer fibers in a large-scale quantity, and fibers with a high surface area can be obtained with this technique. The processing variables during spinning have a considerable impact on the resulting properties of the fibers. Therefore, in this review, the processing-property relationship in biodegradable polymers, blends, and their composites is provided. The morphological characteristics, load-bearing properties, and the potential application of melt-spun biodegradable fibers in various sectors are also provided.

Influence of Myrrh Extracts on the Properties of PLA Films and Melt-Spun Multifilament Yarns

A possible approach for providing new properties for textiles is the insertion of natural ingredients into the textile product during the process of its manufacture. Myrrh has long been used in medicine as an antibacterial and antifungal material. Polylactide (PLA) is a thermoplastic synthetic biopolymer obtained from renewable resources-and due its biodegradability, is also widely used in medicine. In this study, films and multifilament yarns from modified biodegradable PLA granules with ethanolic and aqueous myrrh extracts were developed and characterized. Optical microscopy was used to determine the surface morphology of PLA/myrrh multifilament yarns. Tensile tests, ultraviolet-visible (UV-vis), differential scanning calorimetry (DSC) were applied to determine, consequently, mechanical, optical properties and degree of crystallinity of PLA/myrrh films and multifilament yarns. The chemical composition of PLA/myrrh multifilament yarns was estimated by Fourier-transform infrared (FTIR) spectroscopy method. The results showed that it is possible to form PLA melt-spun multifilament yarns with myrrh extract. The type of myrrh extract (ethanolic or aqueous) has a significant influence on the mechanical and optical properties of the PLA films and melt-spun yarns. The mechanical properties of PLA films and melt-spun multifilament yarns formed from PLA granules with aqueous myrrh extract decreased 19% and 21% more than PLA with ethanolic extract, respectively. Analysis of UV-vis spectra showed that, due to the yellow hue, the reflectance of PLA films and melt-spun PLA multifilament yarns modified with myrrh extracts decreased exponentially. The DSC test showed that multifilament yarns from PLA modified with aqueous extract had the highest degree of crystallization.