Characterization of biodegradable poly( l ‐lactide) tube over accelerated degradation

An experimental investigation into the physical, thermal and mechanical degradation of a polymeric bioresorbable scaffold

This study presents a comprehensive evaluation of the mechanical, micro-mechanical and physical properties of Reva Medical Fantom Encore Bioresorbable Scaffolds (BRS) subjected to a thermally-accelerated degradation protocol. The Fantom Encore BRS were immersed in phosphate buffered saline solution at 50 °C for 112 days with radial compression testing, nanoindentation, differential scanning calorimetry, gel permeation chromatography and mass loss characterisation performed at consecutive time points. In the initial stages of degradation (Days 0-21), the Fantom Encore BRS showed increases in radial strength and stiffness, despite a substantial reduction in in molecular weight, with a slight increase in the melt temperature also observed. In the second phase (Days 35-54), the radial strength of the BRS samples were maintained despite a continued loss in molecular weight. However, during this phase, the ductility of the stent showed a reduction, with stent fracture occurring earlier in the crimp process and with lower amounts of plastic deformation evident under visual examination post-fracture. In the final phase (Days 63-112), the load-bearing capacity of the Fantom Encore BRS showed continued reduction, with decreases in radial stiffness and strength, and drastic reduction in the work-to-fracture of the devices. Throughout each phase, there was a steady increase in the relative crystallinity, with limited mass loss until day 112 and only minor changes in glass transition and melt temperatures. Limited changes were observed in nano-mechanical properties, with measured local elastic moduli and hardness values remaining largely similar throughout degradation. Given that the thermally-accelerated in vitro conditions represented a four-fold acceleration of physiological conditions, these results suggest that the BRS scaffolds could exhibit substantially brittle behaviour after ∼ one year of implantation.

Physical and mechanical degradation behaviour of semi-crystalline PLLA for bioresorbable stent applications

This study presents a systematic evaluation of the physical, thermal and mechanical performance of medical-grade semi-crystalline PLLA undergoing thermally-accelerated degradation. Samples were immersed in phosphate-buffered saline solution at 50 °C for 112 days and mass loss, molecular weight, thermal properties, degree of crystallinity, FTIR and Raman spectra, tensile elastic modulus, yield stress and failure stress/strain were evaluated at consecutive time points. Samples showed a consistent reduction in molecular weight and melting temperature, a consistent increase in percent crystallinity and limited changes in glass transition temperature and mass loss. At day 49, a drastic reduction in tensile failure strain was observed, despite the fact that elastic modulus, yield and tensile strength of samples were maintained. Brittleness increase was followed by rapid increase in degradation rate. Beyond day 70, samples became too brittle to test indicating substantial deterioration of their load-bearing capacity. This study also presents a computational micromechanics framework that demonstrates that the elastic modulus of a semi-crystalline polymer undergoing degradation can be maintained, despite a reducing molecular weight through compensatory increases in percent crystallinity. This study presents novel insight into the relationship between physical properties and mechanical performance of medical-grade PLLA during degradation and could have important implications for design and development of bioresorbable stents for vascular applications.