Synthesis and properties of new aromatic polyimides containing redox-active anthraquinone moieties

Synthesis and characterization of new poly(diketone imide)s derived from 1,4-bis(3,4-dicarboxybenzoyl)benzene dianhydride and various diamines

1,4-Bis(3,4-dicarboxybenzoyl)benzene dianhydride, an aromatic bis(ketone anhydride) monomer, was synthesized by the Friedel–Crafts reaction of terephthaloyl dichloride and o-xylene, followed by the oxidation of the intermediate tetramethylated compound and cyclodehydration of the resulting tetraacid. A series of new poly(diketone imide)s (PDKIs) were prepared from this dianhydride with various aromatic diamines via a conventional two-stage process that included ring-opening polyaddition to form the poly(amic acid)s followed by thermal or chemical imidization. Most of the PDKIs through chemical imidization were soluble in aprotic amide solvents, such as N, N-dimethylacetamide, N-methyl-2-pyrrolidone, m-cresol, and so on. The resulting PDKIs had good thermal property with the glass transition temperature of 203–275°C, the temperature at 5% weight loss of 500–539°C, and the residue of 51–60% at 800°C in nitrogen. Additionally, strong and flexible PDKI films obtained by thermal imidization exhibited outstanding mechanical property with the tensile strength of 88.8–158.5 MPa, tensile modulus of 1.9–3.5 GPa, and elongation at breakage of 7–21%.

Synthesis and characterization of novel fluorinated poly(ether imide)s containing pyridine and/or phenylphosphine oxide moieties

4-(4-Trifluoromethylphenyl)-2,6-bis[4-(4-amino-2-trifluoromethylphenoxy)phenyl]pyridine (9FPBAPP), as a new aromatic diamine, was prepared by a modified Chichibabin reaction of 4-(4-nitro-2-trifluoromethylphenoxy)acetophenone with 4-triflouromethylbenzaldehyde, followed by a catalytic reduction. A series of fluorinated poly(ether imide)s containing pyridine and/or phenylphosphine oxide moieties were prepared from bis(3-aminophenyl)phenylphosphine oxide (BAPPO), 2,2′-bis(3,4-dicarboxyphenyl)hexafluoropropane dianhydride (6FDA), and 9FPBAPP via a conventional two-step thermal imidization procedure with various mole ratios of BAPPO and 9FPBAPP. All the polymers were amorphous and soluble in common organic solvents such as N, N-dimethylacetamide and N-methyl-2-pyrrolidone and had Tg’s of 277–285°C, 5% weight loss temperature of 521–550°C in nitrogen. Furthermore, high char yields and good limited oxygen index values indicated that these polymers exhibited good thermal stability and flame-retardant property. Tough and flexible polymer films also had good mechanical properties with tensile strengths of 75–99 MPa, tensile moduli of 1.1–1.6 GPa, and elongations at break of 12%–24% and low dielectric constants of 2.81–3.53 (1 MHz), as well as high optical transparency with the ultraviolet cutoff wavelength in the range of 350–384 nm.

Synthesis and characterization of novel fluorinated pyridine-based polyimides derived from 4-(4-trifluoromethylphenyl)-2,6-bis(4-aminophenyl)pyridine and dianhydrides

A series of new fluorinated pyridine-based polyimides (PIs) was synthesized by polycondensation of 4-(4-trifluoromethylphenyl)-2,6-bis(4-aminophenyl)pyridine with various aromatic dianhydrides in N, N-dimethylacetamide (DMAc) via the conventional two-step method. The inherent viscosities of the resulting poly(amic acid)s and PIs were 0.54–0.94 and 0.58–0.88 dLg−1, respectively. The obtained PIs were predominantly amorphous and soluble in polar solvents such as N-methyl-2-pyrrolidone, N, N-dimethylformamide, and DMAc at room temperature or upon heating at 70°C. They also displayed good thermal stability with the glass transition temperature of 324–416°C, the temperature at 5% weight loss of 546–584°C, and the residue of 58–69% at 750°C under nitrogen, as well as outstanding mechanical properties with tensile strengths of 69132 MPa, tensile moduli of 1.1–2.0 GPa, and elongations at break of 7–27%. Meanwhile, these PI films had dielectric constants of 2.95–3.22 (1 MHz), low water uptake 0.44–0.71%, and high optical transparency with the ultraviolet cutoff wavelength in the 388–406 nm range and the wavelength of 80% transparency in the range of 550–680 nm.