Development of new poly(ϵ-caprolactone)/chitosan films

PVA/Chitosan Thin Films Containing Silver Nanoparticles and Ibuprofen for the Treatment of Periodontal Disease

Local delivery of drugs or antimicrobial agents is a suitable approach in the management of periodontitis when the infection is localized deep in the pockets and does not adequately respond to mechanical debridement and/or systemic antibiotic treatment. In this context, the objective of this study was to prepare new biocomposite films with antimicrobial, anti-inflammatory, and good mechanical properties to be applied in periodontal pockets. The composite film is eco-friendly synthesized from poly(vinyl alcohol) (PVA) cross-linked with oxidized chitosan (OxCS). Silver nanoparticles (AgNps) were inserted during film synthesis by adding freshly chitosan-capped AgNps colloidal solution to the polymer mixture; the addition of AgNps up to 1.44 wt.% improves the physico-chemical properties of the film. The characterization of the films was performed by FT-IR, atomic mass spectrometry, X-ray spectroscopy, and SEM. The films displayed a high swelling ratio (162%), suitable strength (1.46 MPa), and excellent mucoadhesive properties (0.6 N). Then, ibuprofen (IBF) was incorporated within the best film formulation, and the IBF-loaded PVA/OxCS-Ag films could deliver the drug in a sustained manner up to 72 h. The biocomposite films have good antimicrobial properties against representative pathogens for oral cavities. Moreover, the films are biocompatible, as demonstrated by in vitro tests on HDFa cell lines.

Biocompatibility and biodegradation properties of polycaprolactone/polydioxanone composite scaffolds prepared by blend or co-electrospinning

Electrospun polymer scaffolds are regarded as an ideal tissue engineering scaffold due to similar morphological properties with the native extracellular matrix. Among these, polycaprolactone is widely used to fabricate electrospun fibrous scaffolds due to its excellent biocompatibility, good mechanical properties, and ease of manufacture. However, its low biodegradation rate has a negative influence on its application in tissue engineering scaffold. To address this issue, this study prepared hybrid scaffolds composed of polycaprolactone and polydioxanone (a fast-degrading polyether-ester) via either the blend or co-electrospinning. Subsequently, the structural characteristics, mechanical strength, in vitro/vivo degradation, cellularization, and vascularization of two kinds of hybrid scaffolds were evaluated to decide which method is more suitable for producing tissue engineering scaffolds. The incorporation of polydioxanone increased the mechanical strength of both composite scaffolds. Moreover, co-electrospun scaffolds exhibited improved hydrophilicity compared to blend scaffolds. The results of in vitro and in vivo degradation studies showed that the degradation rate of both composite scaffolds was faster than that of neat polycaprolactone scaffolds due to the incorporated polydioxanone component. Especially in co-electrospun scaffolds, the fast degradation of polydioxanone fiber gave rise to larger pore size, thus leading to faster cellularization and better vascularization compared to blend scaffolds. Therefore, co-electrospinning was demonstrated to be superior to blend electrospinning for the preparation of composite scaffolds. Co-electrospun polycaprolactone–polydioxanone scaffolds may be promising candidates for tissue engineering.

Nanostructured Hydrogels by Blend Electrospinning of Polycaprolactone/Gelatin Nanofibers

Nanofibrous membranes based on polycaprolactone (PCL) have a large potential for use in biomedical applications but are limited by the hydrophobicity of PCL. Blend electrospinning of PCL with other biomedical suited materials, such as gelatin (Gt) allows for the design of better and new materials. This study investigates the possibility of blend electrospinning PCL/Gt nanofibrous membranes which can be used to design a range of novel materials better suited for biomedical applications. The electrospinnability and stability of PCL/Gt blend nanofibers from a non-toxic acid solvent system are investigated. The solvent system developed in this work allows good electrospinnable emulsions for the whole PCL/Gt composition range. Uniform bead-free nanofibers can easily be produced, and the resulting fiber diameter can be tuned by altering the total polymer concentration. Addition of small amounts of water stabilizes the electrospinning emulsions, allowing the electrospinning of large and homogeneous nanofibrous structures over a prolonged period. The resulting blend nanofibrous membranes are analyzed for their composition, morphology, and homogeneity. Cold-gelling experiments on these novel membranes show the possibility of obtaining water-stable PCL/Gt nanofibrous membranes, as well as nanostructured hydrogels reinforced with nanofibers. Both material classes provide a high potential for designing new material applications.