Preparation of solution-processable colorless polyamide-imides with extremely low thermal expansion coefficients through an in-situ silylation method for potential space optical applications

Several tough and flexible fluorinated polyamide-imide films were prepared from trimellitic anhydride chloride and 2,2′-bis(trifluoromethyl)benzidine through a facile one-pot in-situ silylation method. By incorporating fluorinated side groups, the solubility of the prepared polyamide-imide was greatly enhanced. Meanwhile, due to their linear chain configuration and the existence of hydrogen bonding, the prepared polyamide-imide films revealed high tensile strength, high tensile modulus, high glass transition temperature (Tg) and most interestingly, very low coefficient of thermal expansion (CTE) of 11 ppm/°C. Copolymerization with pyromellitic dianhydride (PMDA) led to an extremely low CTE of 4 ppm/°C which should be among the lowest values available for soluble polyamide-imides. The optical homogeneity and stress homogeneity of the obtained polyamide-imide films were also tested. After non-contact with substance and thermal treatment at 300°C, they revealed a better optical homogeneity and stress homogeneity than that of the commercially available Kapton polyimide (PI) films, with a PV value of 0.915 λ and RMS value of 0.163 λ. Thus, these colorless and soluble polyamide-imide films simultaneously possessing promising optical imaging performance are good candidates as novel diffractive membrane optical system architectures.

Rubbed Thin Films of Well-defined Brush Polyimides for Flat-Panel Liquid Crystal Displays: Surface Morphology, Molecular Orientation, and Liquid Crystal Alignability

A series of well-defined brush polyimide (PI) composed of two 4- n-alkyloxyphenyloxy bristles per repeat unit on a semi-rigid poly(4,4′-methylenyldiphenylene pyromellitimide), Cm-PMDA-MDA PIs, were synthesized and their nanoscale thin films prepared by conventional spin-coating of their soluble poly(amic acid) precursor solutions and subsequent drying and thermal imidization in a nitrogen atmosphere. All the PIs were determined to be a positively birefringent polymer. The surface morphology and molecular orientation of each PI in films before and after rubbing were investigated in detail by atomic force microscopy, optical retardation analysis, and linearly polarized infrared spectroscopy. The sequence of the rubbing-induced polymer segmental orientations was further investigated in detail. In addition, the liquid crystal alignment and pretilt ability of the rubbed PI films were examined, and their thermal stability investigated. The present study provides important information on the sequence of the polymer segmental orientations induced by rubbing and additionally the mechanisms of the alignment and pretilt of liquid crystal molecules in contact with the rubbed PI film surface.