Temperature triggered alternating copolymerization of epoxides and lactones via pre-sequenced spiroorthoester intermediates

We report the alternating copolymerization of caprolactone and epoxide through the in situ formation of pre-sequenced spiroorthoester monomer. The reaction is catalyzed by the temperature triggered, bifunctional cationic indium complex (±)-[(NN_iO_tBu)In(CH₂SiMe₃)][B(C₆F₅)₄] (1). 1 can catalyze the coupling of epoxide and lactone to form spiroorthoester at 60 °C and its double ring-opening polymerization at 110 °C to form poly(ether-alt-ester). The post-polymerization modification and degradation of the poly(ether-alt-ester) are further investigated.

We report the alternating copolymerization of caprolactone and epoxide through the in situ formation of pre-sequenced spiroorthoester monomer.

Expanding Monomers as Anti-Shrinkage Additives

Commonly, volumetric shrinkage occurs during polymerizations due to the shortening of the equilibrium Van der Waals distance of two molecules to the length of a (significantly shorter) covalent bond. This volumetric shrinkage can have severe influence on the materials’ properties. One strategy to overcome this volumetric shrinkage is the use of expanding monomers that show volumetric expansion during polymerization reactions. Such monomers exhibit cyclic or even oligocyclic structural motifs with a correspondingly dense atomic packing. During the ring-opening reaction of such monomers, linear structures with atomic packing of lower density are formed, which results in volumetric expansion or at least reduced volumetric shrinkage. This review provides a concise overview of expanding monomers with a focus on the elucidation of structure-property relationships. Preceded by a brief introduction of measuring techniques for the quantification of volumetric changes, the most prominent classes of expanding monomers will be presented and discussed, namely cycloalkanes and cycloalkenes, oxacycles, benzoxazines, as well as thiocyclic compounds. Spiroorthoesters, spiroorthocarbonates, cyclic carbonates, and benzoxazines are particularly highlighted.

Characterization of a low shrinkage dental composite containing bismethylene spiroorthocarbonate expanding monomer

In this study, a novel dental composite based on the unsaturated bismethylene spiroorthocarbonate expanding monomer 3,9-dimethylene-1,3,5,7-tetraoxa-spiro[5,5]undecane (BMSOC) and bisphenol-S-bis(3-meth acrylate-2-hydroxypropyl)ether (BisS-GMA) was prepared. CQ (camphorquinone) of 1 wt % and DMAEMA (2-(dimethylamino)ethyl methacrylate) of 2 wt % were used in a photoinitiation system to initiate the copolymerization of the matrix resins. Distilled water contact angle measurements were performed for the wettability measurement. Degree of conversion, volumetric shrinkage, contraction stress and compressive strength were measured using Fourier Transformation Infrared-FTIR spectroscopy, the AccuVol and a universal testing machine, respectively. Within the limitations of this study, it can be concluded that the resin composites modified by bismethylene spiroorthocarbonate and BisS-GMA showed a low volumetric shrinkage at 1.25% and a higher contact angle. The lower contraction stress, higher degree of conversion and compressive strength of the novel dental composites were also observed.

New Trends in Reaction and Resistance to Fire of Fire-retardant Epoxies

This paper focuses on current trends in the flame retardancy of epoxy-based thermosets. This review examines the incorporation of additives in these polymers, including synergism effects. Reactive flame-retardants—which are incorporated in the polymer backbone—are reported and the use of fire-retardant epoxy coatings for materials protection is also considered.