Synthesis of magnetic, reactive, and thermoresponsive Fe3O4nanoparticles via surface-initiated RAFT copolymerization ofN-isopropylacrylamide and acrolein

Recyclable magnetic Fe3O4@C for methylene blue removal under microwave-induced reaction system

The reclamation and removal of organic pollutants are difficult issues of world concern. In this study, a microwave-induced reaction system (MIRS) is applied to synthesize the multifunctional composite of Fe₃O₄@C, which is employed to adsorb, separate and catalytic oxide the typical organic dye of methylene blue (MB). SEM, TEM, VSM, XPS, pHpzc, and N₂ adsorption performances are carried out to characterize the Fe₃O₄@C. Results show that the Fe₃O₄@C mainly consists of activated Fe-O-C microspheres, which possess plentiful mesopore and macropore structures on surfaces. Batch adsorption experiments were carried out by varying key reaction conditions to optimize these. The maximum adsorption capacity of MB onto the Fe₃O₄@C was 305.0 mg g^-1 in 120 min, at pH 10, and at a temperature of 323 K. MIRS was also assisted to regenerate the spent Fe₃O₄@C which presented good regeneration efficiency by sustaining 16 regeneration cycles without any oxidizing agent. SEM images and FTIR spectrum verified that MB would translate into greater or smaller-sized carbon microspheres. What's more, the adsorption of MB onto both initial and the 16th regenerated Fe₃O₄@C obeyed the Langmuir isotherm model and followed the pseudo-second-order adsorption kinetics, indicating the adsorptive stability after regeneration. In this study, the Fe₃O₄@C combined with MIRS may be one innovative strategy for organic pollutants' complete removal in the future.

Effect of the microstructure of n-butyl acrylate/N-isopropylacrylamide copolymers on their thermo-responsiveness, self-organization and gel properties in water

HYPOTHESIS

Polymer composition, microstructure, molar mass, architecture… critically affect the properties of thermoresponsive polymers in aqueous media.

EXPERIMENTS

The behaviour of n-isopropylacrylamide and n-butyl acrylate-based copolymers of variable composition and structure (statistical, diblock or triblock) was studied in solution at different temperatures and concentrations with turbidimetry measurements, differential scanning calorimetry, electronic microscopy, rheology and scattering experiments.

FINDINGS

This study illustrates how it is possible through chemical engineering of the microstructure of amphiphilic thermoresponsive polymers to modulate significantly the self-assembly, morphological and mechanical properties of these materials in aqueous media. Statistical structures induced a strong decrease of cloud point temperature compared to block structures with similar composition. Moreover, block structures lead below the transition temperature to the formation of colloidal structures. Above the transition temperature, the formation of colloidal aggregates is observed at low concentrations, and at higher concentrations the formation of gels. Neutron scattering and light scattering measurements show that for a given composition diblock structures lead to smaller colloids and mesoglobules than their triblock counterparts. Moreover, diblock structures, compared to triblock analogs, allow the formation of gels that do not demix with time (no synaeresis) but that are softer than triblock gels.

pH and thermal dual-responsive poly(NIPAM-co-GMA)-coated magnetic nanoparticles via surface-initiated RAFT polymerization for controlled drug delivery

Herein, a novel type of multifunctional magnetic nanoparticles with dual thermal and pH-responsive behavior was fabricated as the carrier for delivery of doxorubicin (DOX). Fe₃O₄@SiO₂ magnetic nanoparticles, were grafted with polymer brushes consisting of poly (NIPAM-co-GMA) (PNG) chains via surface initiated reversible addition-fragmentation chain transfer (SI-RAFT) polymerization. The polymer brushes were then modified with hydrazine groups as DOX binding sites. The prepared multifunctional magnetic nanoparticles were characterized by FT-IR, ¹H NMR, XPS, TGA, DLS, VSM, GPC, TEM, and XRD analysis. The in vitro drug release of the multifunctional magnetic nanoparticles was examined at 37 °C (above LCST) and 25 °C (below LCST) in different pH media and exhibited excellent pH- and thermo-sensitive behavior. The results show that the Fe₃O₄@SiO₂@PNG-Hy fabricated via SI-RAFT polymerization is a viable candidate material for tumor treatment studies.

Poly(glycidyl methacrylate)-coated magnetic graphene oxide as a highly efficient nanocarrier: preparation, characterization, and targeted DOX delivery

Herein, we report the preparation of novel magnetic graphene oxide grafted with brush polymer via SI-RAFT polymerization and its application as a nanocarrier for magnetic and pH-triggered delivery of DOX anticancer drug.

Surface-Initiated Controlled Radical Polymerization: State-of-the-Art, Opportunities, and Challenges in Surface and Interface Engineering with Polymer Brushes

The generation of polymer brushes by surface-initiated controlled radical polymerization (SI-CRP) techniques has become a powerful approach to tailor the chemical and physical properties of interfaces and has given rise to great advances in surface and interface engineering. Polymer brushes are defined as thin polymer films in which the individual polymer chains are tethered by one chain end to a solid interface. Significant advances have been made over the past years in the field of polymer brushes. This includes novel developments in SI-CRP, as well as the emergence of novel applications such as catalysis, electronics, nanomaterial synthesis and biosensing. Additionally, polymer brushes prepared via SI-CRP have been utilized to modify the surface of novel substrates such as natural fibers, polymer nanofibers, mesoporous materials, graphene, viruses and protein nanoparticles. The last years have also seen exciting advances in the chemical and physical characterization of polymer brushes, as well as an ever increasing set of computational and simulation tools that allow understanding and predictions of these surface-grafted polymer architectures. The aim of this contribution is to provide a comprehensive review that critically assesses recent advances in the field and highlights the opportunities and challenges for future work.

The effect of polymer branching and average molar mass on the formation, stabilization and thermoresponsive properties of gold nanohybrids stabilized by poly(N-isopropylacrylamides)

The architecture of PNIPAM based polymers strongly influences both their thermoresponsiveness and their abilities to control and stabilize AuNP formation.

CO2-switchable drug release from magneto-polymeric nanohybrids

A CO₂-responsive well-defined magneto-polymeric drug delivery system has been developed. A dosage release of doxorubicin (DOX) in vitro in a time-controllable manner can be easily executed with alternate CO₂/N₂ treatment by these smart nanocarriers.

Stabilization and functionalization of iron oxide nanoparticles for biomedical applications

Superparamagnetic iron oxide nanoparticles (NPs) are used in a rapidly expanding number of research and practical applications in the biomedical field, including magnetic cell labeling separation and tracking, for therapeutic purposes in hyperthermia and drug delivery, and for diagnostic purposes, e.g., as contrast agents for magnetic resonance imaging. These applications require good NP stability at physiological conditions, close control over NP size and controlled surface presentation of functionalities. This review is focused on different aspects of the stability of superparamagnetic iron oxide NPs, from its practical definition to its implementation by molecular design of the dispersant shell around the iron oxide core and further on to its influence on the magnetic properties of the superparamagnetic iron oxide NPs. Special attention is given to the selection of molecular anchors for the dispersant shell, because of their importance to ensure colloidal and functional stability of sterically stabilized superparamagnetic iron oxide NPs. We further detail how dispersants have been optimized to gain close control over iron oxide NP stability, size and functionalities by independently considering the influences of anchors and the attached sterically repulsive polymer brushes. A critical evaluation of different strategies to stabilize and functionalize core-shell superparamagnetic iron oxide NPs as well as a brief introduction to characterization methods to compare those strategies is given.