Dynamic intratubular biomineralization following root canal obturation with pozzolan-based mineral trioxide aggregate sealer cement

Evaluation of the root dentin bond strength and intratubular biomineralization of a premixed calcium aluminate-based hydraulic bioceramic endodontic sealer

PURPOSE

This study evaluated the dentin bonding strength and biomineralization effect of a recently developed premixed calcium aluminate-based endodontic sealer (Dia-Root Bio Sealer) in comparison with existing calcium silicate-based sealers.

METHODS

The root canals of 80 mandibular premolars were filled with Dia-Root Bio Sealer, Endoseal MTA, EndoSequence BC Sealer, and AH Plus Bioceramic Sealer. Medial and apical specimens were then obtained by sectioning. The push-out bond strength was measured using the medial specimens, and the failure mode was recorded. Intratubular biomineralization in the apical specimens was analyzed using scanning electron microscopy and energy-dispersive X-ray spectroscopy (EDS). The data were analyzed using one-way analysis of variance followed by the Tukey test (P < 0.05).

RESULTS

The push-out bond strength of Dia-Root Bio Sealer was significantly higher than that of the other tested materials, and a cohesive failure pattern was observed in all groups. Dia-Root Bio Sealer also exhibited a significantly higher degree of biomineralization than the other groups, and EDS analysis indicated that the biomineralized precipitates were amorphous calcium phosphate.

CONCLUSION

The results of this study indicate that Dia-Root Bio Sealer has the potential to be used as an adequate root canal sealer due to its favorable bonding performance.

Intratubular crystal formation in the exposed dentin from nano-sized calcium silicate for dentin hypersensitivity treatment

The aim of this study is to evaluate intratubular crystal formation from the experimental material consisting of dicalcium silicate (C2S) and tricalcium silicate (C3S) with nano-scaled particle size. A total of twenty-four specimens were made by isolating 8 mm of the cervical part centered at the cementoenamel junction of extracted premolars. Twelve specimens were not treated and considered as control. The experimental material was applied to the other twelve specimens by brushing for 10,000 strokes. Each group was randomly divided into four subgroups according to the period of immersion in phosphate buffer saline (PBS) for 1, 30, 60, and 90 days each. The specimens were sectioned longitudinally and examined with scanning electron microscopy and energy dispersion X-ray spectroscopy. The intratubular crystal were formed in PBS and densely filled the dentinal tubules over time. The crystal formation occurred at a depth of more than 50 μm from the dentin surface. The Ca/P ratio of formed intratubular crystals was 1.68 after 3 months. The experimental material consisting of C2S and C3S with a nanoscale particle size can form hydroxyapatite-like crystals in dentinal tubules in PBS, and there is a possibility of reducing dentin hypersensitivity by blocking the dentinal fluid flow.

Push-out bond strength and intratubular biomineralization of a hydraulic root-end filling material premixed with dimethyl sulfoxide as a vehicle

Objectives

This study was designed to evaluate the parameters of bonding performance to root dentin, including push-out bond strength and dentinal tubular biomineralization, of a hydraulic bioceramic root-end filling material premixed with dimethyl sulfoxide (Endocem MTA Premixed) in comparison to a conventional powder-liquid-type cement (ProRoot MTA).

Materials and Methods

The root canal of a single-rooted premolar was filled with either ProRoot MTA or Endocem MTA Premixed (n = 15). A slice of dentin was obtained from each root. Using the sliced specimen, the push-out bond strength was measured, and the failure pattern was observed under a stereomicroscope. The apical segment was divided into halves; the split surface was observed under a scanning electron microscope, and intratubular biomineralization was examined by observing the precipitates formed in the dentinal tubule. Then, the chemical characteristics of the precipitates were evaluated with energy-dispersive X-ray spectroscopic (EDS) analysis. The data were analyzed using the Student's t-test followed by the Mann-Whitney U test (p < 0.05).

Results

No significant difference was found between the 2 tested groups in push-out bond strength, and cohesive failure was the predominant failure type. In both groups, flake-shaped precipitates were observed along dentinal tubules. The EDS analysis indicated that the mass percentage of calcium and phosphorus in the precipitate was similar to that found in hydroxyapatite.

Conclusions

Regarding bonding to root dentin, Endocem MTA Premixed may have potential for use as an acceptable root-end filling material.

Evaluation of dentin penetration of three different endodontic sealers in the presence and absence of the smear layer

INTRODUCTION

A sealer's ability to effectively and stably penetrate the dentinal tubules is an essential factor for selecting an effective root canal obturation material. Evaluation of the sealers' penetration into the dentinal tubules provides valuable data in the endodontic treatment outcome.

Evaluation of Bond Strength of Four Different Root Canal Sealers

The purposes of the study were to evaluate the influence of the sealer’s chemical composition on the interfacial strength between root canal dentin and root filling material, for two different classes of endodontic sealers, and to assess their failure modes. Methods: Forty extracted single-rooted teeth were randomly divided into four groups using the following endodontic sealers: RealSeal SE and Resilon (RSSE); EndoSequence BC sealer and BC Point (EBCS); Endoseal MTA and gutta-percha (EDS); Bioroot RCS and gutta-percha (BRS). Teeth were embedded in acrylic resin, and the roots were sectioned horizontally into 1 mm slices. For each slice, the perimeter was measured. A push-out test was performed using an Instron universal testing machine. For each sample, bond strength was calculated. Specimens were examined by SEM investigation in order to analyze the dentin−sealer−core interface. Results were assessed using analysis of variance (ANOVA) and Tukey and Bonferroni test. Results: Statistical analysis revealed that EDS and gutta-percha had significantly higher resistance to dislodgement compared to the other three groups (p < 0.05). EBCS and BC Point showed significantly greater push-out bond strength values compared to RSSE and Resilon (p < 0.05). Conclusions: Bioceramic endodontic sealers showed a higher bond strength to root dentin than methacrylate resin-based endodontic sealer.

Methodological proposal for evaluation of adhesion of root canal sealers to gutta-percha

AIM

To compare the bond strength of an epoxy resin-based sealer and two calcium silicate-based sealers (CSS) to gutta-percha discs using a new method.

METHODOLOGY

Round discs of gutta-percha (n = 60), measuring 10 mm in diameter and 2 mm in thickness, were placed on a glass plate and a drop of each sealer (AH Plus, EndoSequence BC Sealer and EndoSeal MTA) was placed on their surface. Another identical disc was placed onto the first one and a standardized weight (0.0981 N) applied over them using a specially developed apparatus. Ten samples prepared for each sealer were submitted to a microshear bond strength test accomplished by a specially designed set-up coupled to a universal testing machine. The Kruskal-Wallis test followed by a post hoc procedure was used to compare groups considering the preliminary analysis of the raw data had indicated the nonadherence to a Gaussian distribution (Shapiro-Wilk, p < .05). Alpha error was set at 5%.

RESULTS

Overall, no premature failure occurred. All sealers had some degree of adhesiveness to gutta-percha discs but with a significant difference amongst them (Kruskal-Wallis, p = .019). The epoxy resin-based sealer (AH Plus) had significantly higher median shear bond strength values (1.43 MPa; 1.40-1.83) compared to EndoSeal MTA (0.53 MPa; 0.46-0.73) (p = .021) and EndoSequence BC Sealer (0.45 MPa; 0.34-0.46) (p = .023), whilst the lowest median value was observed with EndoSequence BC Sealer (0.45 MPa; 0.34-0.46) (p < .05).

CONCLUSIONS

CSS sealers had weaker bonding to gutta-percha when compared to the epoxy resin-based AH Plus sealer. The proposed methodology is an innovative and reproducible method for testing the bond strength of root canal sealers to gutta-percha.

iRoot SP Promotes Osteo/Odontogenesis of Bone Marrow Mesenchymal Stem Cells via Activation of NF-κB and MAPK Signaling Pathways

The regeneration of bone and tooth tissues, and related cellular therapies, has attracted widespread attention. Bone marrow mesenchymal stem cells (BMSCs) are potential candidates for such regeneration. iRoot SP is a premixed bioceramic root canal sealer widely used in clinical settings. However, the effect of iRoot SP on the biological features of BMSCs has not been elucidated. In the present study, we found that 0.2 mg/ml iRoot SP conditioned medium promoted osteo/odontogenic differentiation and enhanced mineralization of BMSCs without affecting the proliferative ability. Mechanistically, the NF-κB and MAPK signaling pathways were activated in SP-treated BMSCs, and differentiation was inhibited when cultured with the specific inhibitor. Taken together, these findings demonstrate that iRoot SP promotes osteo/odontogenic differentiation of BMSCs via the NF-κB and MAPK signaling pathways, which could provide a new theoretical basis for clinical applications of iRoot SP and a new therapeutic target for the regeneration of bone and tooth tissue in the future.

Effect of apexification on occlusal resistance of immature teeth

Background

Strain distribution was investigated to assess the occlusal resistance alterations in immature teeth under different occlusal force.

Methods

In vitro apexification models of teeth with a funnel-shaped immature apex were obturated with mineral trioxide aggregate (MTA; ProRoot MTA) using different combinations of core materials (10/group): group 1, full-length orthograde obturation of MTA; group 2, a 5-mm MTA apical plug with a composite core; group 3, a 5-mm MTA apical plug and back-filling with warm gutta-percha. Teeth with calcium hydroxide (CH)-medicated canals and untreated teeth with normal apices were tested as controls. The teeth were arranged between two adjacent normal-apex teeth, embedded in a resin mold with a simulated periodontal ligament space. Strain data were recorded from the 3-unit teeth assembly under static compressive occlusal forces (50, 100, 200, and 300 N). Measurements were repeated 20 times for each condition, and the data were statistically analyzed.

Results

The immature teeth showed altered occlusal force resistance, placing increased strain on adjacent teeth. Teeth with CH-medicated canals showed significantly inferior occlusal resistance under all tested forces (P < 0.05). Application of an MTA plug with deep composite resin core resulted in significantly better stress-bearing capacity especially under forces of 50 and 300 N (P < 0.05).

Conclusions

The pattern of occlusal force distribution in immature teeth differed according to the canal obturation materials used for apexification. Immature teeth with an MTA apical plug showed more favorable occlusal force resistance than those with CH-medicated canals.

Calcium silicate-based root canal sealers: a literature review

Epoxy resin-based sealers are currently widely used, and several studies have considered AH Plus to be the gold-standard sealer. However, it still has limitations, including possible mutagenicity, cytotoxicity, inflammatory response, and hydrophobicity. Drawing upon the advantages of mineral trioxide aggregate, calcium silicate-based sealers were introduced with high levels of biocompatibility and hydrophilicity. Because of the hydrophilic environment in root canals, water resorption and solubility of root canal sealers are important factors contributing to their stability. Sealers displaying lower microleakage and stronger push-out bond strength are also needed to endure the dynamic tooth environment. Although the physical properties of calcium silicate-based sealers meet International Organization for Standardization recommendations, and they have consistently reported to be biocompatible, they have not overcome conventional resin-based sealers in actual practice. Therefore, further studies aiming to improve the physical properties of calcium silicate-based sealers are needed.

Different Application Methods for Endoseal MTA Sealer: A Comparative Study

Introduction

The aim of present ex vivo study was to investigate the filling quality and voids, using Endoseal mineral trioxide aggregate (Endoseal MTA) with a single-cone technique with and without ultrasonic application and to compare these methods with lateral compaction technique.

Methods and Materials

Thirty-six extracted human anterior single-root teeth were prepared and assigned to 3 groups: Group 1: EMS group was Endoseal MTA+ single-cone; Group 2: EMSU group was Endoseal MTA+ single-cone with ultrasonic activation; and Group 3: LC group was Endoseal MTA+ lateral condensation technique. Teeth were sectioned transversely in coronal, middle and apical of the teeth and the existence of voids and their areas in the slices were measured and scored under a dental microscope. One-way analysis of variance and Post Hoc test were used for statistical analysis and also to detect any significance (α=0.05).

Results

EMS group showed significantly more void area than lateral compaction group (P<0.05), but the difference between the EMSU group and the other two groups were not significant (P>0.05). Also, EMS group had significantly higher void score than the other two groups (P<0.017).

Conclusion

Endoseal MTA as a premixed calcium silicate sealer has a better performance when used with gutta-percha cone-mediated ultrasonic activation, so we suggest gentle ultrasonic activation for applying Endoseal MTA in the clinical use.

Volume of Voids in Retrograde Filling: Comparison between Calcium Silicate Cement Alone and Combined with a Calcium Silicate-based Sealer

INTRODUCTION

The aim of this study was to compare the volume of voids between retrograde filling using calcium silicate cement alone and retrograde filling using a combination of calcium silicate cement with a calcium silicate-based sealer.

METHODS

Twenty single-rooted, extracted human teeth were instrumented with nickel-titanium files and obturated with gutta-percha. We resected the roots at a point 3 mm from the apex, prepared the root ends, and filled the root-end cavities with Endocem Zr (Maruchi, Wonju, Korea) or Endoseal MTA (Maruchi) plus Endocem Zr. Then, we scanned the prepared samples using micro-computed tomographic imaging and performed 3-dimensional reconstruction. The percentage volume of the gap between the canal wall and root-end filling was calculated along with the percentage volume of voids in the filling materials. All data were analyzed using the Mann-Whitney U test. Selected specimens were further observed using scanning electron microscopy.

RESULTS

There were no significant differences in the percentage volumes of the gaps and internal voids between the 2 groups. Both calcium silicate and the calcium silicate-based sealer exhibited good adaptation to the cavity wall.

CONCLUSIONS

The findings of our micro-computed tomographic and scanning electron microscopic analyses suggested that the volume of voids in retrograde filling using a combination of calcium silicate cement and calcium silicate-based sealer was comparable with that in retrograde filling using calcium silicate cement only. Calcium silicate-based sealers could be used in retrograde filling for clinical convenience without harmful effects on the quality of filling.

Evaluation of the Dislodgement Resistance of a New Pozzolan-Based Cement (EndoSeal MTA) Compared to ProRoot MTA and Biodentine in the Presence and Absence of Blood

INTRODUCTION

This in vitro study investigated the dislodgement resistance of EndoSeal MTA, a new pozzolan-containing calcium silicate-based material, in comparison with ProRoot MTA and Biodentine in the presence and absence of contamination with blood.

METHODS

Standard furcal perforations were created in 180 human mandibular first molars. The teeth were randomly allocated to 12 groups of 15 each. ProRoot MTA, Biodentine, and EndoSeal MTA were used to repair the perforations. In half of the samples, the walls of the perforated areas were contaminated with blood, whereas saline was injected into the other half. A push-out test was performed using a universal testing machine after 24 hours or 7 days. To evaluate failure patterns, the samples were split into half and were examined under a stereomicroscope at a 20x magnification. Data were analyzed using three-way analysis of variance, Tukey test, and Student's t-test.

RESULTS

At both time intervals and in the presence and absence of contamination with blood, ProRoot MTA and Biodentine had significantly higher retention values than EndoSeal MTA (p < 0.001). Contamination with blood had no effect on EndoSeal MTA; however, it negatively affected the dislodgement resistance of Biodentine at 24 hours and ProRoot MTA at both time intervals (p < 0.05). Time significantly affected only the bond strength of the uncontaminated groups (p > 0.001). The most common type of failure was mixed for ProRoot MTA and Biodentine, whereas it was cohesive for EndoSeal MTA.

CONCLUSIONS

ProRoot MTA and Biodentine showed higher values of bond strength than EndoSeal MTA and may thus be better options for the repair of root perforations.

A micro-computed tomographic study of remaining filling materials of two bioceramic sealers and epoxy resin sealer after retreatment

Objective

This study evaluated the presence of residual root canal filling material after retreatment using micro-computed tomography (micro-CT).

Materials and Methods

Extracted human teeth (single- and double-rooted, n = 21/each; C-shaped, n = 15) were prepared with ProFile and randomly assigned to three subgroups for obturation with gutta-percha and three different sealers (EndoSeal MTA, EndoSequence BC sealer, and AH Plus). After 10 days, the filling material was removed and the root canals were instrumented one size up from the previous master apical file size. The teeth were scanned using micro-CT before and after retreatment. The percentage of remaining filling material after retreatment was calculated at the coronal, middle, and apical thirds. Data were analyzed using the Kruskal-Wallis test and Mann-Whitney U test with Bonferroni post hoc correction.

Results

The tested sealers showed no significant differences in the percentage of remaining filling material in single- and double-rooted teeth, although EndoSeal MTA showed the highest value in C-shaped roots (p < 0.05). The percentage of remaining filling material of AH Plus and EndoSeal MTA was significantly higher in C-shaped roots than in single- or double-roots (p < 0.05), while that of BC sealer was similar across all root types. EndoSeal MTA showed the highest values at the apical thirds of single- and double-roots (p < 0.05); otherwise, no significant differences were observed among the coronal, middle, and apical thirds.

Conclusions

Within the limitations of this study, a large amount of EndoSeal MTA remained after retreatment, especially in C-shaped root canals.

The Penetration Ability of Calcium Silicate Root Canal Sealers into Dentinal Tubules Compared to Conventional Resin-Based Sealer: A Confocal Laser Scanning Microscopy Study

The purpose of this study was to compare the penetration ability of calcium silicate root canal sealers and conventional resin-based sealer using confocal laser scanning microscopy (CLSM). A total of 60 recently extracted single-rooted human premolars were used in this study. The root canals were prepared to a size 40/0.06 taper with ProFile rotary instruments and irrigated with NaOCl and EDTA. After drying all canals, the specimens were randomly divided into three experimental groups (n = 20): Group 1, gutta-percha (GP)/AH Plus with continuous wave compaction; group 2, GP/BioRoot RCS with a single-cone technique; and group 3, GP/Endoseal MTA with a single-cone technique. All experimental samples were sectioned perpendicular to their long axis using a low-speed diamond wheel at the apical, middle, and coronal third levels. The penetration abilities of all samples were evaluated using CLSM. A Kruskal⁻Wallis analysis and a series of Mann⁻Whitney U post hoc tests were performed. A higher intensity level was found in the coronal area and a lower intensity level in the apical area in all the experimental groups. The AH Plus group showed higher sum fluorescence intensity in the apical and coronal thirds compared with the BioRoot RCS and Endoseal MTA groups, whereas the BioRoot RCS group showed a higher intensity level in the middle third, similar to the AH Plus group. The maximum sealer penetration depth was low in the apical area and high in the coronal area in the AH Plus and Endoseal MTA groups. In the BioRoot RCS group, maximum sealer penetration was observed in the middle third. In conclusion, there were significant differences in sealer penetration pattern and distance according to the root level and sealer type.

Comparing the Ability of Different Materials and Techniques in Filling Artificial Internal Resorption Cavities

Objective

This ex vivo study aims to investigate the root filling quality of warm vertical technique, single-cone technique with GuttaFlow2, Endoseal MTA and EndoSequence BC sealer as a sealer in artificial internal resorption cavity.

Methods

For this study, 40 human single-root teeth were selected. After root preparation, the roots were horizontally sectioned 7 mm from the apex. The hemisphere cavities were created on both sides, and then they were re-approximated. According to filling methods and materials, the samples were randomly as-signed to four experimental groups: I: warm vertical compaction technique (WVC), II: single-cone technique with GuttaFlow2 (GF), III: single-cone technique with Endoseal MTA sealer (EM), IV: single-cone technique with EndoSequence BC sealer (ES). Filled roots were radiographed in buccolingual and mesiodistal views to check the obturation, and stored in humid environment at the room temperature for 7 days. Each tooth was sectioned 7 mm from the root apex at the level of the previous cut, and it was then photographed un-der stereomicroscope. The photographs and radiographs of all samples were imported to an image-analysis software to calculate the percentage of sealer, gutta-percha, and voids. The results were statistically analyzed using one-way ANOVA and Kruskal-Wallis Dunn's tests.

Results

In buccolingual view of radiographs, the WVC and EM groups showed significantly lower percent-age of voids (P value<0.05) compared to that in the GF group. In mesiodistal view, the WVC and EM groups showed significantly lower percentage of voids (P value<0.05) compared to that in the GF and ES groups. In stereomicroscope evaluation, the WVC and EM groups showed significantly lower percentage of voids (P value<0.05) compared to that in the GF and ES groups. The differences observed between the WVC and EM groups (P value>0.05) or between the GF and ES groups (P value>0.05) were not significant.

Conclusion

WVC technique and single-cone technique with EM sealer are the optimum methods to fill ar-tificial resorption cavities.

Novel Calcium Zirconate Silicate Cement Biomineralize and Seal Root Canals

This study evaluated the sealing ability of gutta-percha (GP) with a calcium silicate-based sealer and a novel calcium zirconate containing calcium silicate cement (ZC). The root canals of the extracted premolars were prepared, which were then randomly allocated to three experimental groups (12 root canals per group) for obturation by continuous wave of condensation with the GP and AH 26 sealer (CW); obturation using a single GP with a calcium silicate-based EndoSequence BC sealer (SC); or obturation with ZC. The roots were inserted into sterile Eppendorf tubes, which were inoculated coronally with Porphyromonas gingivalis. The amount of endotoxin leakage into the apical reservoirs were measured using the Limulus Amebocyte Lysate (LAL) assay over 21 days, with comparisons made using one-way ANOVA and Scheffe’s tests (α = 0.05). After 21 days, 75% of the canals that had been obturated by SC, 50% of those obturated by CW and 42% of those obturated by ZC showed endotoxin leakage. The amount of leakage was higher in the SC canals than in the CW (p = 0.031) or ZC (p = 0.03) canals, although there was no significant difference in the amount of leakage for CW and ZC (p > 0.05). X-ray diffraction revealed the presence of tricalcium silicate (Ca₃SiO₅) and calcium zirconate (CaZrO₃) in the synthesized ZC. Scanning electron microscopy revealed mineralized precipitates on the dentin of canals obturated by ZC. The novel calcium zirconate silicate cement appears to promote biomineralization and seal root canals at least as effectively as the conventional sealer.

Interfacial Characteristics and Cytocompatibility of Hydraulic Sealer Cements

INTRODUCTION

The stability and long-term success of root canal obturation depends on the choice of sealer because the sealer bonds to the dentin and stabilizes the solid cone. Furthermore, the sealer needs to be nontoxic because sealer toxicity will certainly lead to treatment failure. The aim of this study was to assess the sealer-dentin interface of 3 hydraulic root canal sealers and to evaluate their cytocompatibility compared with AH Plus (Dentsply DeTrey GmbH, Konstanz, Germany).

METHODS

Four dental root canal sealers were assessed. AH Plus, MTA Fillapex (Angelus, Londrina, Brazil), BioRoot RCS (Septodont, Saint-Maur-des-Fossés, France), and Endoseal (Maruchi, Wonju-si, Gangwon-do, South Korea) were characterized using scanning electron microscopy and energy-dispersive spectroscopy. The sealer-tooth interface was assessed by confocal microscopy and scanning electron microscopy, and biocompatibility was measured by assessing the cell metabolic function using direct contact assays and alkaline phosphatase activity.

RESULTS

The tricalcium silicate-based sealers presented a different microstructure and elemental composition despite their similar chemistry and classification. BioRoot RCS was free of aluminum, and all sealers presented different radiopacifying elements. The sealer penetration in the dentinal tubules and interfacial characteristics were different. The migration of silicon was evident from sealer to tooth for all sealers containing tricalcium silicate. MTA Fillapex and BioRoot RCS exhibited the best cytocompatibility in both the direct contact test and alkaline phosphatase activity.

CONCLUSIONS

The use of hydraulic calcium silicate-based sealers has introduced a different material type to endodontics. These materials are different than other sealers mostly because of their hydraulic nature and their interaction with the environment. Although the sealers tested had a similar chemistry, their cytocompatibility and bonding mechanisms were diverse.

Different Setting Conditions Affect Surface Characteristics and Microhardness of Calcium Silicate-Based Sealers

OBJECTIVE

To investigate the effect of different setting conditions on surface microhardness and setting properties of calcium silicate-based sealers.

METHODS

Three sealers, EndoSequence Bioceramic (BC; Brasseler USA, Savannah, GA, USA), Endoseal MTA (ES; Maruchi, Wonju, Korea), and Well-Root ST (WR; Vericom, Chuncheon, Korea), were compared. Specimens were exposed to either butyric acid (pH 5.4) or phosphate-buffered saline (PBS [pH 7.4]) for 48 h and stored at 100% humidity for 12 days. The control specimens were stored at 100% humidity for 14 days. Surface microhardness was measured, topographic changes were observed, and phase analysis was performed using X-ray diffraction. Microhardness according to storage conditions was compared using one-way analysis of variance and Tukey's multiple comparison tests (P < .05).

RESULTS

The BC and ES sealers exhibited decreased microhardness when stored in acid or PBS compared with control (P < .05). In the WR group, acid exposure lowered microhardness of the specimens compared with control (P < .05). Scanning electron microscopy revealed different topographies in specimens from all tested sealers exposed to acid or PBS.

CONCLUSION

The surface microhardness of calcium silicate-based sealers was reduced by exposure to either acid or PBS. Acid solutions, however, had a more detrimental effect than PBS.

Intratubular Biomineralization in a Root Canal Filled with Calcium-Enriched Material over 8 Years

This case report describes intratubular biomineralization in root canal, filled with calcium-enriched material after 8 years of clinical maintenance. The schematic findings of dentinal tubules were investigated with scanning electron microscopy (SEM) and energy dispersive spectroscopy (EDS). The root canal obturation material was closely adapted to root dentin surface, suggesting the possibility of chemical bonding between the two interfaces. SEM and EDS observation of dentinal tubules showed intratubular biomineralized crystal structures with Ca/P ratio in a range of 1.30-2.12, suggesting bioactive capacity of calcium-enriched material.

Composition and physicochemical properties of calcium silicate based sealers: A review article

Background

Recently a new generation of endodontic sealers has been developed based on calcium silicate as MTA Fillapex, Endoseal MTA, Total Fill BC Sealer, EndoSequence BC Sealer, iRoot SP, Endo CPM sealer, MTA-Angelus and ProRoot Endo Sealer. A review of literature was conducted to discuss the composition, physicochemical properties, and clinical perspectives of calcium silicate based sealers.

Material and Methods

A literature search was conducted in PubMed and web of knowledge databases with appropriate MeSh terms and keywords. A total of 71 studies were reviewed for data extraction.

Results and Conclusions

Calcium silicate based sealers showed suitable physical properties to be used as an endodontic sealer. However, its high solubility remains an important issue. They show good performance regarding calcium ion release, film thickness, and fowability. More researches are required about features of calcium silicate based sealers before recommending them for clinical applications.

Key words:Calcium silicate, root canal filling materials, composition, physical properties.

Comparative evaluation of Fracture Resistance of Endodontically Treated Teeth Obturated with Pozzolan-based MTA Sealer and Epoxy Resin-based Sealer: An in vitro Study

Aim

To evaluate and compare the effect of epoxy resin-based sealer and a pozzolan-based mineral trioxide aggregate (MTA) sealer on the fracture resistance of endodontically treated teeth.

Materials and methods

Thirty single-rooted mandibular premolars were decoronated to a standardized root length of 15 mm. ProTaper rotary files up to a master apical file size of F3 were used for cleaning and shaping the root canals followed by 2.5% sodium hypochlorite irrigation. The teeth were randomly divided into three groups (n = 10 each), and the obturation was completed using gutta-percha with Endoseal MTA (group I) and AH Plus (group II) as root canal sealers. Group III served as control (instrumented and unfilled). Each specimen was then subjected to fracture testing by using a universal testing machine at a crosshead speed of 1.0 mm/minute until fracture. The force required to fracture each specimen was recorded and the data were subjected to statistical analysis using one-way analysis of variance (ANOVA), followed by pairwise comparison using post hoc Games-Howell test (p < 0.05).

Results

The fracture resistance of groups I and II were significantly higher than those of group III. No significant difference in the fracture resistance was observed between group I (Endoseal MTA) and group II (AH Plus) groups.

Conclusion

It can be concluded that the new root canal sealer, Endoseal MTA, is able to reinforce the tooth against fracture as good as AH Plus.

Clinical significance

Endoseal MTA is a sealer for the reinforcement of endodontically treated teeth.

How to cite this article

Upadhyay ST, Purayil TP, Ginjupalli K. Comparative evaluation of Fracture Resistance of EndodonticallyTreated Teeth Obturated with Pozzolan-based MTA Sealer and Epoxy Resin-based Sealer: An in vitro Study. World J Dent 2017;8(1):37-40.