Ni-Catalysed intramolecular reductive aminocarbonylation of 2-haloaryl-tethered nitroarenes for the synthesis of dibenzazepine-based heterocycles

A nickel-catalysed intramolecular reductive aminocarbonylation of 2-haloaryl-tethered nitroarenes is developed for rapid access to a variety of dibenzoazepinones and their derivatives.

The Biocatalytic Degradation of Organic Dyes Using Laccase Immobilized Magnetic Nanoparticles

Free laccase has limitations for its use in industrial applications that require laccase immobilization on proper support, to improve its catalytic activity. Herein, the nanoparticles of magnetic iron oxide (Fe3O4) and copper ferrite (CuFe2O4) were successfully used as support for the immobilization of free laccase, using glutaraldehyde as a cross-linker. The immobilization conditions of laccase on the surface of nanoparticles were optimized to reach the maximum activity of the immobilized enzyme. The synthesized free nanoparticles and the nanoparticle-immobilized laccase were characterized using different techniques, including X-ray diffraction (XRD), Fourier transform infrared spectroscopy (FT-IR), scanning electron microscope (SEM), vibrating sample magnetometer (VSM), and thermogravimetric analysis (TGA). CuFe2O4 nanoparticles, as support, enhanced laccase activity compared to free laccase and Fe3O4 nanoparticle-immobilized laccase that appeared during the study of pH, temperature, and storage stability on free and immobilized laccase. The CuFe2O4 and Fe3O4 nanoparticle-immobilized laccase showed superior activity in a wide pH range, temperature range, and storage period, up to 20 days at 4.0 °C, when compared to free laccase. Additionally, the synthesized nanobiocatalysts were examined and optimized for the biodegradation of the anionic dye Direct Red 23 (DR23). HPLC analysis was used to confirm the dye degradation. The reusability of immobilized laccases for the biodegradation of DR23 dye was investigated for up to six successive cycles, with a decolorization efficiency over 70.0%, which indicated good reusability and excellent stability.

Palladium-catalysed regioselective N-arylation of anthranilamides: a tandem route for dibenzodiazepinone synthesis

A palladium-catalyzed tandem reaction of 2-aminobenzamide and 1,2-dihaloarenes for the synthesis of dibenzodiazepinone via double N-arylations (inter and intra-molecular) has been achieved.

Structural characterization and magnetic properties of undoped and copper-doped cobalt ferrite nanoparticles prepared by the octanoate coprecipitation route at very low dopant concentrations

Nanoparticles of undoped and copper-doped cobalt ferrite Co_1−xCu_xFe₂O₄ at very low dopant concentrations (x = 0; 0.02; 0.04; 0.06; 0.08) were successfully synthesized by pyrolysis of the corresponding hetero metal octanoate precursors obtained via coprecipitation using the octanoate ligand as precipitating agent. The precursors were then characterized by FTIR, ICP-AES and TG-DTA analyses and the results reveal the formation of a copper-cobalt-iron hydroxooctanoate represented by the formula [Co_1−xCu_xFe₂(C₈H₁₅O₂)₆(OH)₂·2H₂O]. The decomposition products obtained upon pyrolysis in air at 400 °C for 3 h were characterized by FTIR, XRD, SEM, TEM, XPS and VSM analyses. FTIR and XRD analyses showed the formation of a single phase mixed spinel ferrite while TEM analysis showed that the particles have a spherical shape with a mean size of 20 nm and form spherical agglomerates with sizes reaching 500 nm in some cases as the SEM images show. The chemical states of the metallic species in the samples were revealed by XPS to be Cu²⁺, Co²⁺ and Fe³⁺. These results combined with XRD confirmed the mixed spinel structure, Co_1−xCu_xFe₂O₄ in which Cu²⁺ ions substitute Co²⁺ ions in tetrahedral sites for x lower than 0.06 and in octahedral sites for x between 0.06 and 0.08. Magnetic parameters such as saturation magnetization (M_s), coercivity (H_c), remanent magnetization (M_r), magnetocrystalline anisotropy constant (K) and reduced magnetization (M_r/M_s), obtained from magnetic hysteresis loops measured at room temperature, are in agreement with this mixed spinel structure and also indicate that these materials are ferromagnetic and could be good candidates for applications in biomedicine and in microwave devices.

Low level copper-doped CoFe₂O₄ has been synthesized and shows an increasing of saturation magnetization up to 6% Cu, subsequently decreasing above 6%.

Synthesis and characterization of magnetic copper–iron-titanate and uptake studies of americium from nuclear waste solutions

Magnetic materials, which find enormous applications due to their benign nature, can have their efficiency and stability enhanced by incorporation of foreign materials and controlling the synthesis conditions.