Soluble Pt Nanoparticles Stabilized by a Tris-imidazolium Tetrafluoroborate as Efficient and Recyclable Catalyst for the Stereoselective Hydrosilylation of Alkynes

Tunable Aryl Alkyl Ionic Liquid Supported Synthesis of Platinum Nanoparticles and Their Catalytic Activity in the Hydrogen Evolution Reaction and in Hydrosilylation

Tunable aryl alkyl ionic liquids (TAAILs) are ionic liquids (ILs) with a 1-aryl-3-alkylimidazolium cation having differently substituted aryl groups. Herein, nine TAAILs with the bis(trifluoromethylsulfonyl)imide anion are utilized in combination with and without ethylene glycol (EG) as reaction media for the rapid microwave synthesis of platinum nanoparticles (Pt-NPs). TAAILs allow the synthesis of small NPs and are efficient solvents for microwave absorption. Transmission electron microscopy (TEM) shows that small primary NPs with sizes of 2 nm to 5 nm are obtained in TAAILs and EG/TAAIL mixtures. The Pt-NPs feature excellent activity as electrocatalysts in the hydrogen evolution reaction (HER) under acidic conditions, with an overpotential at a current density of 10 mA cm^-2 as low as 32 mV vs the reversible hydrogen electrode (RHE), which is significantly lower than the standard Pt/C 20% with 42 mV. Pt-NPs obtained in TAAILs also achieved quantitative conversion in the hydrosilylation reaction of phenylacetylene with triethylsilane after just 5 min at 200 °C.

Sweet, Sugar-Coated Hierarchical Platinum Nanostructures for Easy Support, Heterogenization and Separation

Metal nanoparticles are increasingly gaining interest in the field of heterogeneous catalysis. Here, we present a novel strategy for synthesizing sugar-coated platinum nanostructures (SC-Pt-NS) from the carbohydrates sucrose and D(-)-fructose. In the synthesis from a mixture of H2PtCl6·6H2O, the carbohydrate in an ionic liquid (IL) yielded primary particles of a homogeneous average size of ~10 nm, which were aggregated to hierarchical Pt nanostructures of ~40–65 nm and surrounded or supported by the carbohydrate. These sugar-coated platinum nanostructures present a facile way to support and heterogenize nanoparticles, avoid leaching and enable easier separation and handling. The catalytic activity of the SC-Pt-NS was shown in the hydrosilylation test reaction of phenylacetylene with triethylsilane, where very high turnover frequency (TOF) values of up to 87,200 h−1 could be achieved, while the platinum metal leaching into the product was very low.

Evidence for the “cocktail” nature of platinum-catalyzed alkyne and alkene hydrosilylation reactions

Evidence of the involvement of a “cocktail”-type catalytic system in the alkyne and alkene hydrosilylation reaction in the presence of platinum on a carbon support is reported.

Rhodium Nanoparticles Stabilized by PEG-Tagged Imidazolium Salts as Recyclable Catalysts for the Hydrosilylation of Internal Alkynes and the Reduction of Nitroarenes

PEGylated imidazolium (bromide and tetrafluoroborate) and tris-imidazolium (bromide) salts containing triazole linkers have been used as stabilizers for the preparation of water-soluble rhodium(0) nanoparticles by reduction of rhodium trichloride with sodium borohydride in water at room temperature. The nanomaterials have been characterized (Transmission Electron Microscopy, Electron Diffraction, X-ray Photoelectron Spectroscopy, Inductively Coupled Plasma-Optical Emission Spectroscopy). They proved to be efficient and recyclable catalysts for the stereoselective hydrosilylation of internal alkynes, in the presence or absence of solvent, and in the reduction of nitroarenes to anilines with ammonia-borane as hydrogen donor in aqueous medium (1:4 tetrahydrofuran/water).

Gold nanoparticles stabilized by PEG-tagged imidazolium salts as recyclable catalysts for the synthesis of propargylamines and the cycloisomerization of γ-alkynoic acids

Water-soluble gold nanoparticles prepared in the presence of PEG-tagged tris-imidazolium bromide, containing Au(0) and Au(i) species, are reusable catalysts.