Immobilized nickel boride nanoparticles on magnetic functionalized multi-walled carbon nanotubes: a new nanocomposite for the efficient one-pot synthesis of 1,4-benzodiazepines

In this study, a new magnetic nanocomposite consisting of Ni2B nanoparticles anchored on magnetic functionalized multi-walled carbon nanotubes (Fe3O4/f-MWCNT/Ni2B) was synthesized and characterized using various techniques such as FT-IR, XRD, FESEM, SEM-based EDX, SEM-based elemental mapping, HRTEM, DLS, SAED, XPS, BET, TGA, and VSM. The as-prepared magnetic nanocomposite was successfully employed for the preparation of bioactive 1,4-benzodiazepines from the three-component reaction of o-phenylenediamine (1), dimedone (2), and different aldehydes (3), in polyethylene glycol 400 (PEG-400) as a solvent at 60 °C. The obtained results demonstrated that the current one-pot three-component protocol offers many advantages, such as good-to-excellent yields within acceptable reaction times, favorable TONs and TOFs, eco-friendliness of the procedure, easy preparation of the nanocomposite, mild reaction conditions, a broad range of products, excellent catalytic activity, green solvent, and reusability of the nanocomposite.

Synthetic aspects of 1,4- and 1,5-benzodiazepines using o-phenylenediamine: a study of past quinquennial

Benzodiazepines, seven-membered heterocyclic compounds having two nitrogen atoms at different positions, are ruling scaffolds in the area of pharmaceutical industry. They act as cardinal moieties in organic synthesis as well as in medicinal chemistry. Among the different benzodiazepines, 1,4- and 1,5-benzodiazepines play a far-reaching role in the field of biological activities such as anticonvulsion, anti-anxiety, sedation, and hypnotics. In the past few decades, researchers have conducted a lot of work on these moieties and developed broad, valuable, and significant approaches for their synthesis. In this review article, we recapitulate the systematic synthetic strategies of 1,4- and 1,5-benzodiazepines using o-phenylenediamine as a precursor over the past five years (2018-2022). This article will be helpful for scientists and researchers to examine and explore novel and efficient methods for the synthesis of these biologically active moieties.

Regulated synthesis of Zr-metal-organic frameworks with variable hole size and its influence on the performance of novel MOF-based heterogeneous amino acid-thiourea catalysts

We present an efficient and easy synthesis method for incorporating organocatalytic moieties into Zr-metal organic frameworks (Zr-MOFs). The catalytic activity and selectivity of the new chiral catalysts were improved by adjusting the aperture of the MOF cavities. The hole size of the Zr-MOF was modulated by adding acid and replacing bridge ligands during synthesis. The difunctional chiral units of amino acid-thiourea are anchored onto the Zr-MOF by a mild synthesis method from an isothiocyanate intermediate which could effectively avoid the racemization of chiral moieties in the synthesis process. By means of specific surface area measurement (BET), scanning electron microscopy (SEM) and powder X-ray Diffraction (PXRD), it was confirmed that Zr-MOFs with different pore sizes were synthesized without breaking the basic octahedral structure of the MOF. Finally, good yields (up to 83%) and ee values (up to 73%) were achieved with the new heterogeneous catalysts in 48 hours for the aldol reaction of 4-nitrobenzaldehyde with acetone. By contrast, using the catalyst support without modulating the synthesis, the yield (30%) and the ee-value (26%) were both low. Experiments have confirmed the important influence on the reaction selectivity of providing a suitable reaction environment by controlling the aperture of MOF cavities.