Simultaneous Detection of Catechol and Hydroquinone Using Acetylene Black and Gold Nanoparticle Composite Modified Electrodes

Nitrogen doped 1 T/2H mixed phase MoS2/CuS heterostructure nanosheets for enhanced peroxidase activity

Heteroatom doping and phase engineering are effective ways to promote the catalytic activity of nanoenzymes. Nitrogen-doped 1 T/2H mixed phase MoS2/CuS heterostructure nanosheets N-1 T/2H-MoS2/CuS are prepared by a simple hydrothermal approach using polyoxometalate (POM)-based metal-organic frameworks (MOFs) (NENU-5) as a precursor and urea as nitrogen doping reagent. The XPS spectroscopy (XPS) and Raman spectrum of N-1 T/2H-MoS2/CuS prove the successful N-doping. NENU-5 was used as the template to prepare 1 T/2H-MoS2/CuS with high content of 1 T phase by optimizing the reaction time. The use of urea as nitrogen dopant added to 1 T/2H-MoS2/CuS, resulted in N-1 T/2H-MoS2/CuS with an increase in the content of the 1 T phase from 80 % to 84 % and higher number of defects. N-1 T/2H-MoS2/CuS shows higher peroxidase activity than 1 T/2H-MoS2/CuS and a catalytic efficiency (Kcat/Km) for H2O2 twice as high as that of 1 T/2H-MoS2/CuS. The enhanced catalytic activity has probably been attributed to several reasons: (i) the insertion of urea during the hydrothermal process in the S-Mo-S layer of MoS2, causing an increase in the interlayer spacing and in 1 T phase content, (ii) the replacement of S atoms in MoS2 by N atoms from the urea decomposition, resulting in more defects and more active sites. As far as we know, N-1 T/2H-MoS2/CuS nanosheets have the lowest detection limit (0.16 µm) for the colorimetric detection of hydroquinone among molybdenum disulfide-based catalysts. This study affords a new approach for the fabrication of high-performance nanoenzyme catalysts.

An Amperometric Biomedical Sensor for the Determination of Homocysteine Using Gold Nanoparticles and Acetylene Black-Dihexadecyl Phosphate-Modified Glassy Carbon Electrode

A novel nanocomposite film composed of gold nanoparticles and acetylene black-dihexadecyl phosphate was fabricated and modified on the surface of a glassy carbon electrode through a simple and controllable dropping and electropolymerization method. The nanocomposite film electrode showed a good electrocatalytic response to the oxidation of homocysteine and can work as an amperometric biomedical sensor for homocysteine. With the aid of scanning electron microscopy, energy dispersive X-ray technology and electrochemical impedance spectroscopy, the sensing interface was characterized, and the sensing mechanism was discussed. Under optimal conditions, the oxidation peak current of homocysteine was linearly increased with its concentration in the range of 3.0 µmol/L~1.0 mmol/L, and a sensitivity of 18 nA/(μmol/L) was obtained. Furthermore, the detection limit was determined as 0.6 µmol/L, and the response time was detected as 3 s. Applying the nanocomposite film electrode for monitoring the homocysteine in human blood serum, the results were satisfactory.

One A3B Porphyrin Structure-Three Successful Applications

Porphyrins are versatile structures capable of acting in multiple ways. A mixed substituted A3B porphyrin, 5-(3-hydroxy-phenyl)-10,15,20-tris-(3-methoxy-phenyl)-porphyrin and its Pt(II) complex, were synthesised and fully characterised by 1H- and 13C-NMR, TLC, UV-Vis, FT-IR, fluorescence, AFM, TEM and SEM with EDX microscopy, both in organic solvents and in acidic mediums. The pure compounds were used, firstly, as sensitive materials for sensitive and selective optical and fluorescence detection of hydroquinone with the best results in the range 0.039-6.71 µM and a detection limit of 0.013 µM and, secondly, as corrosion inhibitors for carbon-steel (OL) in an acid medium giving a best performance of 88% in the case of coverings with Pt-porphyrin. Finally, the electrocatalytic activity for the hydrogen and oxygen evolution reactions (HER and OER) of the free-base and Pt-metalated A3B porphyrins was evaluated in strong alkaline and acidic electrolyte solutions. The best results were obtained for the electrode modified with the metalated porphyrin, drop-casted on a graphite substrate from an N,N-dimethylformamide solution. In the strong acidic medium, the electrode displayed an HER overpotential of 108 mV, at i = -10 mA/cm2 and a Tafel slope value of 205 mV/dec.