Preparation of ZnCo 2 O 4 Nanosheets Coated on evenly arranged and fully separated Nanowires with high capacitive and photocatalytic properties by a One‐Step Low‐Temperature Water bath method

Fabrication of ZnCo2O4-Zn(OH)2 Microspheres on Carbon Cloth for Photocatalytic Decomposition of Tetracycline

Zinc cobalt oxide-zinc hydroxide (ZnCo2O4-Zn(OH)2) microspheres were successfully fabricated on carbon cloth via a sample hydrothermal method. The surface morphology of these microspheres and their efficacy in degrading methyl violet were further modulated by varying the thermal annealing temperatures. Adjusting the thermal annealing temperatures was crucial for controlling the porosity of the ZnCo₂O₄-Zn(OH)₂ microspheres, enhancing their photocatalytic performance. Various analytical techniques were utilized to evaluate the physical and chemical properties of the ZnCo2O4-Zn(OH)2 microspheres, including field-emission scanning electron microscopy, energy-dispersive spectroscopy, X-ray diffraction, field-emission transmission electron microscopy, X-ray photoelectron spectroscopy, and UV-vis spectroscopy. Compared to untreated ZnCo2O4-Zn(OH)2 microspheres, those subjected to thermal annealing exhibited increased specific surface area and light absorption capacity, rendering them highly effective photocatalysts under UVC light exposure. Subsequent studies have confirmed the superior performance of ZnCo2O4-Zn(OH)2 microspheres as a reusable photocatalyst for degrading methyl violet and tetracycline. Furthermore, trapping experiments during the photodegradation process using ZnCo₂O₄-Zn(OH)₂ microspheres identified hydroxyl radicals (·OH) and superoxide radicals (·O₂⁻) as the primary reactive species.

Coupling of Nd doping and oxygen-rich vacancy in CoMoO4@NiMoO4 nanoflowers toward advanced supercapacitors and photocatalytic degradation

In this paper, we successfully prepared rare earth element-doped 0.8% Nd-CoMoO4@NiMoO4 nanoflowers with a large specific surface area using the sol-gel method for the first time. In the experiment, we added a structure-directing agent to successfully assemble the nanosheets into a three-dimensional ordered micro-flower shape. By using the strategy of forming a flower-shaped morphology with a structure-directing agent and doping Nd elements to generate oxygen vacancies, the problems of the collapse of the active material structure and slow reaction kinetics were solved. Through relevant electrochemical performance tests, it was found that when the rare earth element Nd was doped at a concentration of 0.8%, the material exhibited exceptional specific capacitance (2387 F g-1 at 1 A g-1) and cycling stability (99.3% after 10 000 cycles at 5 A g-1). These performance characteristics far surpassed those of the other synthesized products. We assembled 0.8% Nd-CoMoO4@NiMoO4 with hydrophilic CNTs into an asymmetric device, 0.8% Nd-CoMoO4@NiMoO4//CNTs. This device exhibited high specific capacitance (262 F g-1 at 1 A g-1) and cycling stability (99.2% after 3000 cycles), with a good energy storage effect. In addition, 0.8% Nd-CoMoO4@NiMoO4 has a low band gap, which broadens the absorption range of the product and improves the utilization rate of visible light. The photocatalyst showed good degradation efficiency (all exceeding 96%) and cycling stability (96%) for all four dyes. This paper provides a new strategy and method for preparing doped polymetallic mixtures, which has potential application value.