Electrocatalytic Oxidation of Ethanol on the Surface of Graphene Based Nanocomposites: An Introduction and Review to it in Recent Studies

Pd Nanoparticle-Decorated Novel Ternary Bi2O2CO3-Bi2MoO6-CuO Heterojunction for Enhanced Photo-electrocatalytic Ethanol Oxidation

Recently, photo-electrooxidation of fuel using a noble metal-semiconductor junction has been one of the most promising approaches in fuel cell systems. Herein, we report the development of a Pd-supported Bi2MoO6-Bi2O2CO3-CuO novel ternary heterojunction for ethanol oxidation in alkali in the presence and absence of visible light. Various spectroscopic and microscopic characterization techniques confirm strong coupling between palladium nanoparticles and Bi2MoO6-Bi2O2CO3-CuO ternary heterojunction supports. The photo-electrocatalytic efficacy of the synthesized catalysts was inspected by cyclic voltammetry (CV), chronoamperometry (CA), and electrochemical impedance spectroscopy (EIS). The CV study reveals that the forward peak current density (in mA mg-1 of Pd) of the synthesized quaternary heterojunction was about 1482.5, which is 2.4, 4, and 4.6 times higher than that of Pd/CuO (608.3), Pd/Bi2MoO6-Bi2O2CO3 (368.3), and similarly synthesized Pd catalyst (321.5) under visible light radiation. The best heterojunction catalyst shows 2.21-fold higher peak current density in visible light compared to that in dark. CA study reveals that after operation for 6000 s, the current density of the quaternary electrode is 1.5 and 3.4 times greater than that of Pd/CuO and Pd/C catalysts, respectively. The greater photocurrent response, lower photoluminescence (PL) emission intensity, and smaller semicircle arc in the Nyquist plot of the quaternary catalyst demonstrate the efficient segregation and higher charge transfer conductance of photogenerated charges to facilitate the photo-electrooxidation process of ethanol. The stability test shows that the quaternary catalyst loses only 9.8 and 7.7% of its maximum current density after 500 cycles of CV operation in the dark and light, respectively, indicating that light energy is more beneficial in establishing high stability. The dramatic enhancement of the photo-electrocatalytic activity of the quaternary electrode is owing to the lower band gap, high ECSA, enhanced charge separation of photogenerated carriers (e--h+), and all cocatalytic support of Bi2MoO6, Bi2O2CO3, and CuO in Pd/ Bi2MoO6-Bi2O2CO3-CuO under visible light radiation. The morphology and structure of the used quaternary catalyst are tested using FESEM and PXRD. Finally, ex situ FTIR spectroscopy and HPLC techniques help understand the ethanol electrooxidation reaction mechanism.

Bimetallic AgPt Nanoalloys as an Electrocatalyst for Ethanol Oxidation Reaction: Synthesis, Structural Analysis, and Electro-Catalytic Activity

In the present work, the chemical synthesis of AgPt nanoalloys is reported by the polyol method using polyvinylpyrrolidone (PVP) as a surfactant and a heterogeneous nucleation approach. Nanoparticles with different atomic compositions of the Ag and Pt elements (1:1 and 1:3) were synthesized by adjusting the molar ratios of the precursors. The physicochemical and microstructural characterization was initially performed using the UV-Vis technique to determine the presence of nanoparticles in suspension. Then, the morphology, size, and atomic structure were determined using XRD, SEM, and HAADF-STEM techniques, confirming the formation of a well-defined crystalline structure and homogeneous nanoalloy with an average particle size of less than 10 nm. Finally, the cyclic voltammetry technique evaluated the electrochemical activity of bimetallic AgPt nanoparticles supported on Vulcan XC-72 carbon for the ethanol oxidation reaction in an alkaline medium. Chronoamperometry and accelerated electrochemical degradation tests were performed to determine their stability and long-term durability. The synthesized AgPt (1:3)/C electrocatalyst presented significative catalytic activity and superior durability due to the introduction of Ag that weakens the chemisorption of the carbonaceous species. Thus, it could be an attractive candidate for cost-effective ethanol oxidation compared to commercial Pt/C.

Influence of Solvents on the Electroactivity of PtAl/rGO Catalyst Inks and Anode in Direct Ethanol Fuel Cell

This paper presents research on the effects of common solvents such as n-butyl acetate, isopropanol, and ethanol on the properties and electroactivity of catalyst ink based on PtAl/rGO. The inks prepared by mixing PtAl/rGO catalyst, Nafion solution (5 wt%), and solvent were coated on carbon cloth by the spin coating method. The results obtained showed that ethanol was the most suitable solvent for the preparation of catalyst ink with a volume ratio between catalyst slurry and solvent of 1 : 1 (CI-EtOH (1/1) ink). The surface of the CI-EtOH (1/1) coated electrode was smooth, flat, and even and had no cracks due to the increase of Nafion mobility, resulting in significant improvement in the interaction between Pt particles and ionomer. Moreover, the electrochemical activity of the CI-EtOH (1/1) ink in ethanol electrooxidation reaction, in both acidic and alkaline media, has the highest value, with the forward current density, IF, reaching 1793 mA mgPt−1 and 4751 mA mgPt−1, respectively. In the application in direct ethanol fuel cell (DEFC), the CI-EtOH ink-coated anode also exhibited the highest power density in both PEM-DEFC (with a proton exchange membrane) and AEM-DEFC (with an anion exchange membrane) at 19.10 mW cm−2 and 27.07 mW cm−2, respectively.

Formation of silica-supported platinum nanoparticles as a function of preparation conditions and boron impregnation

Preparation of supported metal nanoparticles for catalytic applications often relies on an assumption that the initially prepared wet-impregnated support material is covered with approximately a monolayer of adsorbed species that are shaped into the target nanoparticulate material with a desired size distribution by utilizing appropriate post-treatments that often include calcination and reduction schemes. Here, the formation and evolution of surface nanoparticles were investigated for wet-chemistry deposition of platinum from trimethyl(methylcyclopentadienyl)platinum (IV) precursor onto flat silica supports to interrogate the factors influencing the initial stages of nanoparticle formation. The deposition was performed on silicon-based substrates, including hydroxylated silica (SiO₂) and boron-impregnated hydroxylated silica (B/SiO₂) surfaces. The deposition resulted in the immediate formation of Pt-containing nanoparticles, as confirmed by atomic force microscopy and x-ray photoelectron spectroscopy. The prepared substrates were later reduced at 550 °C under H₂ gas environment. This reduction procedure resulted in the formation of metallic Pt particles. The reactivity of the precursor and dispersion of Pt nanoparticles on the OH-terminated silica surface were compared to those on the B-impregnated surface. The size distribution of the resulting nanoparticles as a function of surface preparation was evaluated, and density functional theory calculations were used to explain the differences between the two types of surfaces investigated.