Cyclosporine-impregnated allograft bone sterilized with low-temperature plasma

Freeze-dried and irradiated allograft bone combined with fresh autologous coagula promotes angiogenesis in an ectopic bone allograft implantation model

BACKGROUND

Freeze-dried and irradiated allograft bone (FIAB) is more easily impacted than fresh-frozen allograft bone (FAB), but has weaker incorporation efficiency. We combined FIAB with fresh autologous coagula to enhance donor-host incorporation after impaction during hip revision.

METHODS

Thirty adult male Sprague-Dawley (SD) rats were sacrificed for bone allograft harvesting, and nine male rats were subjected to ectopic bone allograft implantation. For each rat, the container on the left (study) side was filled with freeze-dried allograft bone powder and fresh autologous blood coagula, whereas the right (control) side was filled with freeze-dried allograft bone powder and physiological saline. The extent of angiogenesis (VEGFα) was investigated at postoperative weeks 1, 4, and 8. The deformability of the material was evaluated by performing a confined-impaction mechanical test.

RESULTS

At postoperative weeks 4 and 8, angiogenesis within FIAB on the left side was more pronounced than that on the right side. At postoperative week 1, the left side showed significantly higher VEGFα expression than that on the right side. The delta ratios of compression of the allografts were found to be influenced by bone height and impaction frequency, but not by stiffness or elastic modulus (EM).

CONCLUSION

Supplementation with fresh autologous coagula promoted angiogenesis within the FIABs. Moreover, FIABs were equivalent to FABs in terms of deformability.

Effect of VEGF-A165 addition on the integration of a cortical allograft in a tibial segmental defect in rabbits

PURPOSE

Long-bone segmental defects caused by infection, fracture, or tumour are a challenge for orthopaedic surgeons. Structural allografts are sometimes used in their treatment but their poor biological characteristics are a liability. The objective of this study was to determine whether the addition of recombinant vascular endothelial growth factor-A (VEGF) to a structural allograft improved its integration into a rabbit tibial segmental defect in a non-union model.

METHODS

Tibial segmental defects were filled with heat sterilized allogenic tubular tibiae sections and then stabilized with a screw plate. In the VEGF treatment group (n = 6 tibiae), 2 μg of VEGF added to a 50 μl matrigel solution was inserted into the allograft cavity. In the control group (n = 6 tibiae), only matrigel was added. After 12 weeks, macroscopic and microscopic analysis, radiographs, and computerized micro-tomography (micro-CT) were performed. If allograft consolidation was present, a torsional resistance analysis was performed.

RESULTS

Addition of VEGF to the allograft decreased the rate of osteosynthesis failure compared with the control group (1/6 vs. 5/6, p = 0.08), increased trabecular continuity evaluated by micro-CT in the bone-allograft interphases (8/12 vs. 2/12, p = 0.036) and histological trabecular continuity (7/12 vs. 0/12, p = 0.0046). Full consolidation was observed in three tibiae of the VEGF group and one in the control group (differences not significant); however, torsional resistance showed no significant differences (n.s.).

CONCLUSION

Addition of VEGF to a structural allograph inserted into a rabbit tibial segmental defect increased allograft integration rate. Further research in this direction might help clinicians in dealing with large bone defects.

Sterilizing tissue-materials using pulsed power plasma

This paper investigates the potential of pulsed power to sterilize hard and soft tissues and its impact on their physico-mechanical properties. It hypothesizes that pulsed plasma can sterilize both vascular and avascular tissues and the transitive layers in between without deleterious effects on their functional characteristics. Cartilage/bone laminate was chosen as a model to demonstrate the concept, treated at low temperature, at atmospheric pressure, in short durations and in buffered environment using a purposed-built pulsed power unit. Input voltage and time of exposure were assigned as controlling parameters in a full factorial design of experiment to determine physical and mechanical alteration pre- and post-treatment. The results demonstrated that, discharges of 11 kV sterilized samples in 45 s, reducing intrinsic elastic modules from 1.4 ± 0.9 to 0.9 ± 0.6 MPa. There was a decrease of 14.1 % in stiffness and 27.8 % in elastic-strain energy for the top quartile. Mechanical impairment was directly proportional to input voltage (P value < 0.05). Bacterial inactivation was proportional to treatment time for input voltages above 32 V (P < 0.001; R Sq = 0.98). Thermal analysis revealed that helix-coil transition decelerated with exposure time and collagen fibrils were destabilized as denaturation enthalpy reduced by 200 μV. We concluded by presenting a safe operating threshold for pulsed power plasma as a feasible protocol for effective sterilization of connective tissues with varying level of loss in mechanical robustness which we argue to be acceptable in certain medical and tissue engineering application.