Synthesis of reduced graphene oxide for high-performance supercapacitor

VIS-active TiO2 films decorated by expanded graphite: impact of the exfoliation time on the photocatalytic behaviour

TiO2/C nanocomposite films were applied on water treatment. Expanded graphite nanosheets (EG) were obtained by UVC-assisted liquid-phase exfoliation technique, without the addition of acids, surfactants, or aggressive oxidizing agents, which characterizes the process as an eco-friendly method. The carbon nanosheets were synthesized directly from graphite bulk at different times and deposited on TiO2 films surface by airbrush spray coating method, forming a TiO2/C heterojunction. The increase in the exfoliation time promoted a more efficient photocatalytic dye removal under visible light. Morphological modifications, changes in the electronic structure, and wide range of light absorption were observed from the TiO2/C heterojunction formation. The results showed that hybrid TiO2/C supported photocatalyst is a promise alternative for practical photocatalytic applications under sunlight.

Reduced graphene oxide/ionic liquid composites with tunable interlayer spacing for improved charge/discharge kinetics in supercapacitors

The large specific surface area and high conductivity of reduced graphene oxide (RGO) make it a promising material for supercapacitors. However, aggregation of graphene sheets into graphitic domains upon drying hampers supercapacitor performance by drastically impeding ion transport inside electrodes. Here, we present a facile approach to optimize charge storage performance in RGO-based supercapacitors by systematically tuning their micropore structure. To this end, we combine RGOs with room temperature ionic liquids during electrode processing to impede stacking of sheets into graphitic structures with small interlayer distance. In this process, RGO sheets function as the active electrode material while ionic liquid serves both as a charge carrier and a spacer to control interlayer spacing inside electrodes and form ion transport channels. We show that composite RGO/ionic liquid electrodes with larger interlayer spacing and more ordered structure exhibit improved capacitance and charging kinetics.

Noble Metals Functionalized on Graphene Oxide Obtained by Different Methods-New Catalytic Materials

In recent years, research has focused on developing materials exhibiting outstanding mechanical, electrical, thermal, catalytic, magnetic and optical properties such as graphene/polymer, graphene/metal nanoparticles and graphene/ceramic nanocomposites. Two-dimensional sp² hybridized graphene has become a material of choice in research due to the excellent properties it displays electrically, thermally, optically and mechanically. Noble nanomaterials also present special physical and chemical properties and, therefore, they provide model building blocks in modifying nanoscale structures for various applications, ranging from nanomedicine to catalysis and optics. The introduction of noble metal nanoparticles (NPs) (Au, Ag and Pd) into chemically derived graphene is important in opening new avenues for both materials in different fields where they can provide hybrid materials with exceptional performance due to the synergistical result of the specific properties of each of the materials. This review presents the different synthetic procedures for preparing Pt, Ag, Pd and Au NP/graphene oxide (GO) and reduced graphene oxide (rGO) composites.

Efficient iron-cobalt oxide bifunctional electrode catalysts in rechargeable high current density zinc-air batteries

Iron-cobalt (FeCo) oxides dispersed on reduced graphene oxide (rGO) were synthesized from nitrate precursors at loading levels from 10 wt% to 60 wt%. These catalysts were tested in lab-scale zinc-air batteries (ZABs) at a high current density of 100 mA cm^-2 of the cathode area for the first time, cycling between 60 min of discharging and 60 min of charging. The optimum loading level for the best ZAB cycling performance was found to be 40 wt%, at which CoFe₂O₄ and CoO nanocrystals were detected. A discharge capacity of at least 90% was maintained for about 60 cycles with FeCo 40 wt%, demonstrating superior stability over amorphous FeCo oxides with FeCo 10 wt% despite similar performance at electrochemical tests. At a high current density of 100 mA cm^-2, OER catalytic activity was found to be the limiting factor in ZAB's cyclability. The discrepancies between the ORR/OER catalytic activities by electrochemical and battery cycling test results highlight the role and importance of rGO in improving electrical conductivity and activation of metal oxide electrocatalysts under high current density conditions. The difference of battery cycling test results from traditional electrochemical test results suggests that electrochemical tests conducted at low current densities may be inadequate in predicting practical battery cycling performance.