Two Intermediates in Ammonothermal InN Crystal Growth: [In(NH 3 ) 5 Cl]Cl 2 and InF 2 (NH 2 )

Ammonothermal Crystal Growth of Functional Nitrides for Semiconductor Devices: Status and Potential

The state-of-the-art ammonothermal method for the growth of nitrides is reviewed here, with an emphasis on binary and ternary nitrides beyond GaN. A wide range of relevant aspects are covered, from fundamental autoclave technology, to reactivity and solubility of elements, to synthesized crystalline nitride materials and their properties. Initially, the potential of emerging and novel nitrides is discussed, motivating their synthesis in single crystal form. This is followed by a summary of our current understanding of the reactivity/solubility of species and the state-of-the-art single crystal synthesis for GaN, AlN, AlGaN, BN, InN, and, more generally, ternary and higher order nitrides. Investigation of the synthesized materials is presented, with a focus on point defects (impurities, native defects including hydrogenated vacancies) based on GaN and potential pathways for their mitigation or circumvention for achieving a wide range of controllable functional and structural material properties. Lastly, recent developments in autoclave technology are reviewed, based on GaN, with a focus on advances in development of in situ technologies, including in situ temperature measurements, optical absorption via UV/Vis spectroscopy, imaging of the solution and crystals via optical (visible, X-ray), along with use of X-ray computed tomography and diffraction. While time intensive to develop, these technologies are now capable of offering unprecedented insight into the autoclave and, hence, facilitating the rapid exploration of novel nitride synthesis using the ammonothermal method.

Novel Fluoridoaluminates from Ammonothermal Synthesis: Two Modifications of K2AlF5 and the Elpasolite Rb2KAlF6

Two new modifications of the pentafluoridoaluminate K2AlF5 were obtained from ammonothermal synthesis at 753 K, 224 MPa and 773 K, 220 MPa, respectively. Both crystallize in the orthorhombic space group type Pbcn, with close metric relations and feature kinked chains of cis-vertex-connected AlF6 octahedra resulting in the Niggli formula ∞1{[AlF2/2eF4/1t]2−}. The differences lie in the number of octahedra necessary for repetition within the chains, which for K2AlF5-2 is realized after four and for K2AlF5-3 after eight octahedra. As a result, the orthorhombic unit cell for K2AlF5-3 is doubled in chain prolongation direction [001] as compared to K2AlF5-2 (1971.18(4) pm versus 988.45(3) pm, respectively), while the unit cell parameters within the other two directions are virtually identical. Moreover, the new elpasolite Rb2KAlF6 is reported, crystallizing in the cubic space group Fm3¯m with a = 868.9(1) pm and obtained under ammonothermal conditions at 723 K and 152 MPa.