Synthesis and characterization of two quaternary uranium tellurides, RbTiU₃Te₉ and CsTiU₃Te₉

Black crystals of RbTiU₃Te₉ and CsTiU₃Te₉ have been synthesized at 1223 and 1173 K, respectively, by high-temperature solid-state routes. These compounds crystallize in a new structure type in space group C(2h)²-P2₁/m of the monoclinic system. The structure, which is similar to that of CsTiUTe₅, consists of UTe₂ layers connected into a three-dimensional framework by TiTe₆ octahedra. The expanded UTe₂ layers leave channels that are filled by Rb or Cs atoms. Single-crystal resistivity measurements on CsTiU₃Te₉ are consistent with semiconducting behavior; the calculated activation energy is 0.30(1) eV. X-ray photoelectron spectroscopic measurements on CsTiU₃Te₉ indicate that the compound contains U⁴⁺. From single-crystal magnetic measurements, CsTiU₃Te₉ is consistent with antiferromagnetic coupling between magnetic U atoms. The very low value of the effective magnetic moment of 0.56(2) μ(B) is believed to arise from a coexistence of magnetic and nonmagnetic U atoms.

Structures and bonding in K0.91U1.79S6 and KU2Se6

The compounds K0.91U1.79S6 and KU2Se6, members of the AAn2Q6 actinide family (A = alkali metal or Tl; An = Th or U; Q = S, Se, or Te), have been synthesized from US2, K2S, and S at 1273 K and U, K2Se, and Se at 1173 K, respectively. KU2Se6 shows Curie-Weiss behavior above 30 K and no magnetic ordering down to 5 K. The value of mu(eff) is 2.95(1) mu(B)/U. Its electronic spectrum shows the peaks characteristic of 5f-5f transitions. It is a semiconductor with an activation energy of 0.27 eV for electrical conduction. Both K0.91U1.79S6 and KU2Se6 crystallize in space group Immm of the orthorhombic system and are of the KTh2Se6 structure type. Both contain infinite one-dimensional linear Q-Q chains characteristic of the AAn2Q6 family. Typical of the known AAn2Q6 compounds, in KU2Se6, there are two alternating Se-Se distances of 2.703(2) and 2.855(2) A, both much longer than an Se-Se single bond. In contrast, in K0.91U1.79S6, the first sulfide of this family to be characterized structurally, there are alternating normal S2(2-) pairs 2.097(5) A in length. In K0.91U1.79S6, the formal oxidation state of U is 4+.