Compositional, structural, and phase changes in in vitro laser-irradiated human tooth enamel

Raman Analyses of Laser Irradiation-Induced Microstructural Variations in Synthetic Hydroxyapatite and Human Teeth

The microstructural and molecular-scale variations induced by laser irradiation treatment on human teeth enamel in comparison with synthetic hydroxyapatite (HAp) were examined through Raman microprobe spectroscopy as a function of irradiation power. The results demonstrated that laser irradiation could modify stoichiometry, microstructure, and the population of crystallographic defects, as well as the hardness of the materials. These modifications showed strong dependences on both laser power and initial nonstoichiometric structure (defective content of HPO₄), because of the occurrence of distinct reactions and structural reconstruction. The reported observations can redirect future trends in tooth whitening by laser treatment and the production of HAp coatings because of the important role of stoichiometric defects.

Effect of sodium fluoride plus tricalcium phosphate with and without CO2 laser on remineralization of white spot lesions

Objectives

The aim of this in vitro study was to evaluate the effect of NaF plus TCP with and without CO₂ laser irradiation on management of demineralized enamel using microhardness test and digital microscopy.

Methods

Eighty intact extracted human premolar teeth were randomly divided into 4 groups (20/each). Each group was subjected to a demineralizing solution to create white spot lesion. Group 1 was treated with 3M Vanish™. Group 2 was irradiated with CO₂ laser. Group 3 was subjected to CO₂ laser followed by 3M Vanish™. Group 4 was treated by 3M Vanish™ then CO₂ laser. The teeth were immersed in artificial saliva. Surface microhardness was measured for each tooth before demineralization at base line (M1 as a control), after demineralization (M2) and after management (M3). Comparison of microhardness values between groups was performed using one way ANOVA test with significant level (0.05) followed by multiple comparisons post-hoc Tukey test between groups. Enamel surface was photographed by digital microscope.

Results

All intervention methods used in the current study significantly increased microhardness values of demineralized enamel (P < 0.001). Little improvement of enamel appearance was observed in all groups meanwhile using CO₂ laser on demineralized enamel directly led to signs of white and black dots affecting the appearance of enamel surface.

Significance

The most effective intervention regarding microhardness was group 2 followed by group 3, group 4 and group 1. Coating the enamel surface with 3M Vanish™ before CO₂ laser irradiation acted as a protective layer from the undesirable effects of laser on the teeth with increasing enamel microhardness values more than using Vanish alone. So the promising intervention method regarding both microhardness and appearance was group 4.

Caries inhibition of simulated active caries lesions with CO2 laser irradiation and fluoride

It has been well established that CO₂ laser irradiation can be used to transform the mineral phase of dental enamel to make it more resistant to acid dissolution. The purpose of this study was to investigate if carbon dioxide laser irradiation and topical fluoride can be used to treat incipient caries lesions to inhibit further progression, i.e. treat active lesion surfaces as opposed to sound surfaces prior to subjecting them to an acid challenge. Simulated active caries lesions were produced on twenty eight bovine enamel samples using a pH cycling model and those surfaces were irradiated by a 9.4 μm CO₂ laser and treated with topical fluoride. Changes in the surface morphology, acid resistance, and permeability were measured using digital microscopy, optical coherence tomography (OCT), and SWIR reflectance surface dehydration rate measurements at 1950 nm after exposure to a further acid challenge. There was a significant reduction (P < 0.05) of further lesion progression for lesion windows treated with CO₂ laser irradiation followed by the application of an acidulated phosphate fluoride gel compared to the untreated lesion windows on each sample. Treatment by laser irradiation alone was not effective. The degree of lesion inhibition was not as high as has been previously observed for laser irradiated sound enamel surfaces exposed to an acid challenge.

In vitro CO2 9.3-μm short-pulsed laser caries prevention-effects of a newly developed laser irradiation pattern

Caries prevention with different lasers has been investigated in laboratory studies and clinical pilot trials. Objective of this in vitro study was to assess whether 9.3-μm microsecond short-pulsed CO₂ laser irradiation enhances enamel caries resistance without melting, with and without additional fluoride application. Seven groups of enamel, totaling 105 human enamel samples, were irradiated with 2 different carbon dioxide lasers with 2 different energy application systems (original versus spread beam; 9.3 μm wavelength, pulse repetition rate 43 Hz vs 100 Hz, fluence ranges from 1.4 to 3.9 J/cm², pulse duration 3 μs to 18 μs). The laboratory pH-cycling was performed with or without additional fluoride, followed by cross-sectional microhardness testing. To assess caries inhibition, the mean relative mineral loss delta Z (∆Z) was determined. To evaluate for melting, scanning electron microscopy (SEM) examinations were performed. For the non-laser control groups with additional fluoride use, the relative mineral loss (ΔZ, vol% × μm) ranged between 512 ± 292 and 809 ± 297 (mean ± SD). ΔZ for the laser-irradiated samples with fluoride use ranged between 186 ± 214 and 374 ± 191, averaging a 58% ± 6% mineral loss reduction (ANOVA, P < 0.01 to P < 0.0001). For the non-laser-treated controls without additional fluoride, the mineral loss increased (ΔZ 914 ± 422 to 1224 ± 736). In contrast, the ΔZ for the laser-treated groups without additional fluoride ranged between 463 ± 190 and 594 ± 272 (P < 0.01 to P < 0.001) indicative of 50% ± 2% average reduction in mineral loss. Enhanced caries resistance was achieved by all applied fluences. Using the spread beam resulted in enhanced resistance without enamel melting as seen by SEM. CO₂ 9.3-μm short-pulsed laser irradiation with both laser beam configurations resulted in highly significant reduction in enamel mineral loss. Modifying the beam to a more homogenous profile will allow enamel caries resistance even without apparent enamel melting.

Effect of the carbon dioxide 10,600-nm laser and topical fluoride gel application on enamel microstructure and microhardness after acid challenge: an in vitro study

The aim of this in-vitro study was to evaluate positive effects of the carbon dioxide laser (CO₂, 10,600 nm) with acidulated phosphate fluoride (APF) gel on enamel acid resistance. Twenty extracted human third molars (40 surfaces) were randomly assigned into four groups: group C, untreated control; group L, CO₂ laser alone group; group F, APF 1.23% fluoride gel; and group FL, APF 1.23% gel and laser. Samples from group L were irradiated with a CO₂ laser for 30s. The parameter settings used were average power, 0.73 W; time on, 100 μs; time off, 40 ms; tip-to-tissue distance, 20 mm; tip diameter 700 μm; and energy density with movements, 5 J/cm². Samples from group F were treated with the APF gel for 4 min, and the gel was washed off with distilled water. The enamel samples from group FL were treated with APF gel for 4 min and then irradiated with the CO₂ laser for 30s without removing the gel. Each enamel sample was placed in 50 ml soft drink (pH = 2.75) for 10 min then rinsed with deionized water and stored in artificial saliva at 37 °C for 1 h. Samples were assessed for Vickers hardness number (VHN) before and after treatments and subjected to SEM analysis. Data were analyzed using a one-way analysis of variance (ANOVA) and Tukey's test (α < 0.05). After the acid challenge, the untreated C group was demineralized to a great extent and the enamel surface was with the lowest mean score of microhardness. The observed VHN in the control (C group) had a mean value of 176.13, the scores in the CO₂ laser group (L group) were with mean value of 238.40, the F group with a mean value of 218.45, and the fluoride-treated and laser-irradiated FL group-with a mean of 268.28 VHN. Paired t test performed to compare groups C, L, F, and FL has shown that group FL has greater resistance to decrease in microhardness of dental enamel (P ≤ 0.05) on exposure to acidic protocol. After the acid challenge, the fluoride-treated and laser-irradiated samples (group FL) showed the least diminution in enamel surface microhardness. The sub-ablative carbon dioxide laser irradiation in combination with fluoride treatment is more effective in protecting enamel surface and resisting demineralization than CO₂ laser irradiation or fluoride alone.

Influence of a pulsed CO2 laser operating at 9.4 μm on the surface morphology, reflectivity, and acid resistance of dental enamel below the threshold for melting

Below the threshold for laser ablation, the mineral phase of enamel is converted into a purer phase hydroxyapatite with increased acid resistance. Studies suggest the possibility of achieving the conversion without visible surface alteration. In this study, changes in the surface morphology, reflectivity, and acid resistance were monitored with varying irradiation intensity. Bovine enamel specimens were irradiated using a CO 2 laser operating at 9.4 ?? ? m with a Gaussian spatial beam profile—1.6 to 3.1 mm in diameter. After laser treatment, samples were subjected to demineralization to simulate the acidic intraoral conditions of dental decay. The resulting demineralization and erosion were assessed using polarization-sensitive optical coherence tomography, three-dimensional digital microscopy, and polarized light microscopy. Distinct changes in the surface morphology and the degree of inhibition were found within the laser-treated area in accordance with the laser intensity profile. Subtle visual changes were noted below the melting point for enamel that appear to correspond to thresholds for denaturation of the organic phase and thermal decomposition of the mineral phase. There was significant protection from laser irradiation in areas in which the reflectivity was not increased significantly, suggesting that aesthetically sensitive areas of the tooth can be treated for caries prevention.

Femtosecond laser ablation of enamel

The surface topographical, compositional, and structural modifications induced in human enamel by femtosecond laser ablation is studied. The laser treatments were performed using a Yb:KYW chirped-pulse-regenerative amplification laser system (560 fs and 1030 nm) and fluences up to 14  J/cm2. The ablation surfaces were studied by scanning electron microscopy, grazing incidence x-ray diffraction, and micro-Raman spectroscopy. Regardless of the fluence, the ablation surfaces were covered by a layer of resolidified material, indicating that ablation is accompanied by melting of hydroxyapatite. This layer presented pores and exploded gas bubbles, created by the release of gaseous decomposition products of hydroxyapatite (CO2 and H2O) within the liquid phase. In the specimen treated with 1-kHz repetition frequency and 14  J/cm2, thickness of the resolidified material is in the range of 300 to 900 nm. The micro-Raman analysis revealed that the resolidified material contains amorphous calcium phosphate, while grazing incidence x-ray diffraction analysis allowed detecting traces of a calcium phosphate other than hydroxyapatite, probably β-tricalcium phosphate Ca3(PO4)2, at the surface of this specimen. The present results show that the ablation of enamel involves melting of enamel’s hydroxyapatite, but the thickness of the altered layer is very small and thermal damage of the remaining material is negligible.

Caries inhibition with a CO2 9.3 μm laser: An in vitro study

BACKGROUND AND OBJECTIVES

The caries preventive effects of different laser wavelengths have been studied in the laboratory as well as in pilot clinical trials. The objective of this in vitro study was to evaluate whether irradiation with a new 9.3 μm microsecond short-pulsed CO2 -laser could enhance enamel caries resistance with and without additional fluoride applications.

STUDY DESIGN/MATERIALS AND METHODS

One hundred and one human tooth enamel samples were divided into seven groups. Each group was treated with different laser parameters (CO2 -laser, wavelength 9.3 μm, 43 Hz pulse-repetition rate, pulse duration between 3 µs at 1.5 mJ/pulse to 7 µs at 2.9 mJ/pulse). A laboratory pH-cycling model followed by cross-sectional microhardness testing determined the mean relative mineral loss delta Z (ΔZ) for each group to assess caries inhibition in tooth enamel by the CO2 9.3 µm short-pulsed laser irradiation. The pH-cycling was performed with or without additional fluoride.

RESULTS

The non-laser control groups with additional fluoride had a relative mineral loss (ΔZ, vol% × µm) that ranged between 646 ± 215 and 773 ± 223 (mean ± SD). The laser irradiated and fluoride treated samples had a mean ΔZ ranging between 209 ± 133 and 403 ± 245 for an average 55% ± 9% reduction in mineral loss (ANOVA test, P < 0.0001). Increased mean mineral loss (ΔZ between 1166 ± 571 and 1339 ± 347) was found for the non-laser treated controls without additional fluoride. In contrast, the laser treated groups without additional fluoride showed a ΔZ between 470 ± 240 and 669 ± 209 (ANOVA test, P < 0.0001) representing an average 53% ± 11% reduction in mineral loss. Scanning electron microscopical assessment revealed that 3 µs pulses did not markedly change the enamel surface, while 7 µs pulses caused some enamel ablation.

CONCLUSION

The CO2 9.3 µm short-pulsed laser energy renders enamel caries resistant with and without additional fluoride use. The observed enhanced acid resistance occurred with the laser irradiation parameters used without obvious melting of the enamel surface as well as after irradiation with energies causing cutting of the enamel. Lasers Surg. Med. 48:546-554, 2016. Published 2016. This article is a U.S. Government work and is in the public domain in the USA.

Morphological and ultrastructural comparative analysis of bone tissue after Er:YAG laser and surgical drill osteotomy

OBJECTIVE

The purpose of this study was to analyze morphological, chemical, and crystallographic changes of bone tissue after osteotomy performed with an erbium:yttrium-aluminium-garnet (Er:YAG) laser and a low speed pilot drill.

MATERIALS AND METHODS

Bone blocks were prepared from porcine ribs, and on each block, two tunnel preparations were performed using the Er:YAG laser (pulse energy: 1000 mJ, pulse duration: 300 μs, pulse repetition rate: 20 Hz) or the low-speed surgical pilot drill. The morphological changes of the cortical and the spongious surface of the tunnel preparations were analyzed under the field emission scanning electron microscopy (FE-SEM) at low and high resolution. The distribution and the level of chemical elements in the treated surfaces were evaluated by qualitative and semiquantitative energy dispersive x-ray analysis (SEM-EDX). Diffraction x-ray analysis was used to detect any differences and thermally induced modifications of hydroxyapatite crystals.

RESULTS

FE-SEM revealed sharp edges of the Er:YAG preparations, with empty intertrabecular spaces and no signs of carbonization. In the drill group, the surface of the preparations was smooth, completely covered with smear layer and microcracks, and with hairy-like irregularities on the edges. SEM-EDX analysis did not reveal any differences in the number of specific chemical elements between the laser and the drill group. There were no thermally induced modifications of hydroxyapatite crystal structure in the bone tissue in either group.

CONCLUSIONS

The Er:YAG laser ablation did not cause any chemical or crystallographic changes of the bone tissue. Compared with the drill, Er:YAG laser created well-defined edges of the preparations, and cortical bone had no smear layer.

Evaluation of enamel surface modification using PS-OCT after laser treatment to increase resistance to demineralization

At laser intensities below ablation, carbonated hydroxyapatite in enamel is converted into a purer phase hydroxyapatite with increased acid resistance. Previous studies suggested the possibility of achieving the conversion without surface modification. This study attempts to evaluate the thresholds for the modification without additional changes in physical and optical properties of the enamel. Bovine specimens were irradiated using an RF-excited CO₂ laser operating at 9.4-µm with a pulse duration of 26-µs, pulse repetition rates of 100-1000 Hz, with a Gaussian spatial beam profile - 1.4 mm in diameter. After laser treatment, the samples were subjected to acid demineralization for 48 hours to simulate acidic intraoral conditions of a caries attack. The resulting demineralization and erosion were assessed using polarization sensitive OCT (PS-OCT) and 3D digital microscopy. The images from digital microscopy demonstrated a clear delineation between laser protected zones without visual changes and zones with higher levels of demineralization and erosion. Distinct changes in the surface morphology were found within the laser treated area in accordance with the Gaussian spatial beam profile. There was significant protection from the laser in areas that were not visually altered.

A method for monitoring enamel erosion using laser irradiated surfaces and optical coherence tomography

INTRODUCTION

Since optical coherence tomography (OCT) is well suited for measuring small dimensional changes on tooth surfaces, OCT has great potential for monitoring tooth erosion. Previous studies have shown that enamel areas ablated by a carbon dioxide laser manifested lower rates of erosion compared to the non-ablated areas. The purpose of this study was to develop a model to monitor erosion in vitro that could potentially be used in vivo.

METHODS

Thirteen bovine enamel blocks were used in this in vitro study. Each 10 mm × 2 mm block was partitioned into five regions, the central region was unprotected, the adjacent windows were irradiated by a CO2 laser operating at 9.3 µm with a fluence of 2.4 J/cm(2) , and the outermost windows were coated with acid resistant varnish. The samples were exposed to a pH cycling regimen that caused both erosion and subsurface demineralization for 2, 4 and 6 days. The surfaces were scanned using a time-domain polarization sensitive optical coherence tomography (PS-OCT) system and the degree of surface loss (erosion) and the integrated reflectivity with lesion depth was calculated for each window.

RESULTS

There was a large and significant reduction in the depth of surface loss (erosion) and the severity of demineralization in the areas irradiated by the laser.

CONCLUSION

Irradiation of the enamel surface with a pulsed carbon dioxide laser at sub-ablative intensities results in significant inhibition of erosion and demineralization under the acid challenge employed in this study. In addition, these results suggest that it may be feasible to modify regions of the enamel surface using the laser to serve as reference marks to monitor the rate of erosion in vivo.

Influence of CO2 (10.6 μm) and Nd:YAG laser irradiation on the prevention of enamel caries around orthodontic brackets

One possible undesirable consequence of orthodontic therapy is the development of incipient caries lesions of enamel around brackets. The aim of this study was to compare the effects of CO2 (λ = 10.6 μm) and Nd:YAG (λ = 1,064 nm) lasers associated or not with topical fluoride application on the prevention of caries lesions around brackets. Brackets were bonded to the enamel of 65 premolars. The experimental groups (n = 13) were: G1--application of 1.23% acidulated fluoride phosphate gel (AFP, control); G2--Nd:YAG laser irradiation (0.6 W, 84.9 J/cm(2), 10 Hz, 110 μs, contact mode); G3--Nd:YAG laser irradiation associated with AFP; G4--CO2 laser irradiation (0.5 W, 28.6 J/cm(2), 50 Hz, 5 μs, and 10 mm focal distance); and G5--CO2 laser irradiation associated with AFP. Quantitative light-induced fluorescence was used to assess enamel demineralization. The data were statistically compared (α = 5%). The highest demineralization occurred in the Nd:YAG laser group (G2, 26.15% ± 1.94). The demineralization of all other groups was similar to that of the control group. In conclusion, CO2 laser alone was able to control enamel demineralization around brackets at the same level as that obtained with topical fluoride application.

The effect of fractional CO2 laser irradiation on remineralization of enamel white spot lesions

This study investigated the combined effect of fractional CO(2) laser irradiation and fluoride on treatment of enamel caries. Sixty intact premolars were randomly assigned into four groups and then stored in a demineralizing solution to induce white spot lesions. Tooth color was determined at baseline (T1) and after demineralization (T2). Afterwards, the teeth in group 1 remained untreated (control), while group 2 was exposed to an acidulated phosphate fluoride (APF) gel for 4 min. In groups 3 and 4, a fractional CO(2) laser was applied (10 mJ, 200 Hz, 10 s) either before (group 3) or through (group 4) the APF gel. The teeth were then immersed in artificial saliva for 90 days while subjected to daily fluoride mouthrinse and weekly brushing. Color examinations were repeated after topical fluoride application (T3) and 90 days later (T4). Finally, the teeth were sectioned, and microhardness was measured at the enamel surface and at 30 and 60 μ from the surface. In both lased groups, the color change between T1 and T4 stages (∆E(T1-T4)) was significantly lower than those of the other groups (p < 0.05). Laser irradiation followed by fluoride application (group 3) caused a significant increase in surface microhardness compared to APF alone and control groups (p < 0.05). Microhardness at depths of 30 and 60 μ was also significantly greater in group 3 compared to those of all other groups (p < 0.05). Application of a fractional CO(2) laser before fluoride therapy is suggested for recovering the color and rehardening of demineralized enamel.

Histological and SEM analysis of root cementum following irradiation with Er:YAG and CO2 lasers

Recently, the Er:YAG and CO(2) lasers have been applied in periodontal therapy. However, the characteristics of laser-irradiated root cementum have not been fully analyzed. The aim of this study was to precisely analyze the alterations of root cementum treated with the Er:YAG and the CO(2) lasers, using non-decalcified thin histological sections. Eleven cementum plates were prepared from extracted human teeth. Pulsed Er:YAG laser contact irradiation was performed in a line at 40 mJ/pulse (14.2 J/cm(2)/pulse) and 25 Hz (1.0 W) under water spray. Continuous CO(2) laser irradiation was performed in non-contact mode at 1.0 W, and ultrasonic instrumentation was performed as a control. The treated samples were subjected to stereomicroscopy, scanning electron microscopy (SEM), light microscopy and SEM energy dispersive X-ray spectroscopy (SEM-EDS). The Er:YAG laser-treated cementum showed minimal alteration with a whitish, slightly ablated surface, whereas CO(2) laser treatment resulted in distinct carbonization. SEM analysis revealed characteristic micro-irregularities of the Er:YAG-lased surface and the melted, resolidified appearance surrounded by major and microcracks of the CO(2)-lased surface. Histological analysis revealed minimal thermal alteration and structural degradation of the Er:YAG laser-irradiated cementum with an affected layer of approximately 20-μm thickness, which partially consisted of two distinct affected layers. The CO(2)-lased cementum revealed multiple affected layers showing different structures/staining with approximately 140 μm thickness. Er:YAG laser irradiation used with water cooling resulted in minimal cementum ablation and thermal changes with a characteristic microstructure of the superficial layer. In contrast, CO(2) laser irradiation produced severely affected distinct multiple layers accompanied by melting and carbonization.

Nondestructive assessment of dentin demineralization using polarization-sensitive optical coherence tomography after exposure to fluoride and laser irradiation

Previous studies have demonstrated that polarization-sensitive optical coherence tomography (PS-OCT) can be used to image natural and artificial caries in dentin. The purpose of this study was to measure nondestructively the severity of artificial caries lesions in dentin and determine the efficacy of intervention with anticaries agents including fluoride and lasers. Although several studies have assessed the utility of PS-OCT to image caries lesions in enamel and to quantify the lesion severity, only a few studies have focused on lesions in dentin. In this study, images of artificial dentin lesions on extracted human teeth were acquired with PS-OCT. Before exposure to an artificial demineralizing solution, three incisions were made on the sample surfaces using either Er:YAG, Nd:YAG (lambda = 355 nm), or TEA CO(2) lasers and selected areas were treated with topical fluoride to create six unique treatment areas for each of the three laser conditions investigated. The integrated reflectivity and depth of demineralization were calculated for each of the six areas on each sample using the PS-OCT images. Polarized light microscopy (PLM) and transverse microradiography (TMR) were used to measure lesion severity on histological thin sections for comparison. PS-OCT successfully measured the inhibition of demineralization by topical fluoride. Laser irradiation was not particularly effective in increasing or decreasing the rate of dentin demineralization. PLM and TMR corroborated those results. This study demonstrates that PS-OCT can be used to measure demineralization on dentin surfaces and determine the degree of inhibition of demineralization by anticaries agents.

A physical approach to modify the hydraulic reactivity of alpha-tricalcium phosphate powder

A microsized alpha-tricalcium phosphate (alpha-TCP) powder was calcined at various temperatures (350 degrees C<T<800 degrees C) for various durations (1-24h) and the resulting physico-chemical and reactivity changes were measured. Without calcination, the alpha-TCP powder started reacting within minutes after contacting a 0.2M Na(2)HPO(4) solution as measured by isothermal calorimetry. The overall reaction was finished within a few days. After calcination at 350 degrees C< or =T < or =550 degrees C for 24h, no significant changes in the crystalline composition, crystallite size, particle size or specific surface area were noticed. However, the powder reactivity was progressively changed. More specifically, the hydraulic reaction of the powders calcined at 500 and 550 degrees C only started after 2-3h whereas the overall hydraulic reaction was only slightly postponed, suggesting that physical or chemical changes had occurred at the particle surface. As mainly physical changes were detected at the particle surface during calcination at 500 degrees C, it was speculated that the appearance of this reaction delay (=induction time) was due to the disappearance of surface defects during the calcination step, i.e. to the need to create surface defects to induce dissolution and hence reaction.

The effects of lasers and fluoride on the acid resistance of decalcified human enamel

OBJECTIVE

In order to preserve the maximum amount of healthy enamel and increase the acid resistance of decalcified enamel, a CO(2) laser, an Nd:YAG laser, and acidulated phosphate fluoride (APF) were used to treat incipient carious lesions, then their effects were compared.

MATERIALS AND METHODS

One hundred and sixty samples of human caries-free premolars were immersed in pH-cycling solution (pH = 5) for 2 d for decalcified lesion formation. Then the tooth samples were randomly divided into eight groups and the lesions were treated using the different modalities: a control group, an APF only group, an APF = Nd:YAG laser group, and APF = CO(2) laser group, an Nd:YAG laser = APF group, a CO(2) laser = APF group, a CO(2) laser only group, and an Nd:YAG laser only group. The energy density setting for the two types of lasers was 83.33 J/cm(2). After treatment the tooth samples were immersed in pH-cycling solution again for 2 d for acid challenge. As for the acid-resistance evaluation, the calcium concentration dissolved from the enamel surface was analyzed by an electrolyte analyzer. Scanning electron microscopy (SEM) was used to assess morphologic changes and polarized light microscopy (PLM) was used to evaluate optical changes in the lesions.

RESULTS

The control group showed a statistically significantly (p < 0.05) higher calcium concentration compared with all the other groups. The APF group also had a statistically significantly higher calcium concentration (p < 0.05) than did the laser groups. However, there was no statistically significant difference in any of the laser groups whether combined with fluoride or not (p > 0.05). Upon SEM analysis, melted surfaces and crater-like holes 1-20 microm in diameter were found in the CO(2) laser and Nd:YAG laser groups. On PLM, positive birefringence and reversal of birefringence after acid challenge of the lased enamel were seen.

CONCLUSIONS

Using lasers and fluoride on decalcified enamel appears to increase the enamel's acid resistance, and the effects of the lasers were better than those of fluoride treatment.

Evaluation of mineral content of enamel prepared by erbium, chromium:yttrium-scandium-gallium-garnet laser

The aim of this study was to evaluate the mineral content of enamel etched at two different power settings with an erbium, chromium:yttrium-scandium-gallium-garnet (Er,Cr:YSGG) laser. Buccal, lingual and mesial or distal surfaces of five premolar teeth were cut, and three enamel slabs were obtained from each tooth. Fifteen enamel specimens were divided into three groups (1 W, 2 W and control) of five specimens each and subjected to Er,Cr:YSGG laser. The mean percentage weights of the five elements [calcium (Ca), potassium (K), magnesium (Mg), sodium (Na) and phosphorus (P)] in each slab were measured by inductively coupled plasma-atomic emission spectrometry (ICP-AES). One way analysis of variance (ANOVA) was used to analyze differences among the groups (1 W, 2 W and control). There were no significant differences among the groups (1 W, 2 W and control) for Ca, K, Mg, Na, or P, or for the Ca/P ratio (P > 0.05). Scanning electron microscopy (SEM) photographs indicated that the surface irregularities increased with increased power setting. Laser treatment did not affect the mean percentage weights of Ca, K, Mg, Na, and P, or the Ca/P ratio, in any group.

Non-destructive assessment of inhibition of demineralization in dental enamel irradiated by a lambda=9.3-microm CO2 laser at ablative irradiation intensities with PS-OCT

BACKGROUND AND OBJECTIVE

Polarization sensitive optical coherence tomography (PS-OCT) has great promise for the non-destructive assessment of the efficacy of anti-caries agents such as fluoride and thermal laser treatments on enamel surfaces. The purpose of this study was to demonstrate that PS-OCT can be used to measure demineralization in craters/incisions prepared in enamel by a CO(2) laser operating at the high irradiation intensities required for cavity preparations.

MATERIALS AND METHODS

Incisions in bovine enamel surfaces were produced by a CO(2) laser used with a water spray. The laser was operated at lambda=9.3 microm with a pulse duration of 15 micros and an incident fluence of 20 J/cm(2). The laser treatments were also combined with topical fluoride treatments. A PS-OCT system operating at 1,310 nm was used to acquire polarization resolved images of six areas including sound and laser-ablated+topical fluoride treated zones on each sample. After imaging the teeth, they were sectioned and the thin sections were examined with polarized light microscopy (PLM) and transverse microradiography (TMR). The integrated reflectivity and lesion depth derived from the PS-OCT scans, the integrated mineral loss and depth measured using TMR and the lesion depth measured with PLM were acquired for each area on the fifteen samples for comparison.

RESULTS

The integrated reflectivity and depth in the areas treated by the laser and fluoride were significantly lower (P<0.05) than for the untreated enamel. Similar results were observed for TMR and PLM.

CONCLUSIONS

These results suggest that PS-OCT has great potential for the non-destructive "in vivo" assessment of the inhibition of demineralization by lasers at ablative irradiation intensities with and without topical fluoride application.

A comparison of fatigue crack growth in human enamel and hydroxyapatite

Cracks and craze lines are often observed in the enamel of human teeth, but they rarely cause tooth fracture. The present study evaluates fatigue crack growth in human enamel, and compares that to the fatigue response of sintered hydroxyapatite (HAp) with similar crystallinity, chemistry and density. Miniature inset compact tension (CT) specimens were prepared that embodied a small piece of enamel (N=8) or HAp (N=6). The specimens were subjected to mode I cyclic loads and the steady state crack growth responses were modeled using the Paris Law. Results showed that the fatigue crack growth exponent (m) for enamel (m=7.7+/-1.0) was similar to that for HAp (m=7.9+/-1.4), whereas the crack growth coefficient (C) for enamel (C=8.7 E-04 (mm/cycle)x(MPa m(0.5))(-m)) was significantly lower (p<0.0001) than that for HAp (C=2.0 E+00 (mm/cycle)x(MPa m(0.5))(-m)). Micrographs of the fracture surfaces showed that crack growth in the enamel occurred primarily along the prism boundaries. In regions of decussation, the microstructure promoted microcracking, crack bridging, crack deflection and crack bifurcation. Working in concert, these mechanisms increased the crack growth resistance and resulted in a sensitivity to crack growth (m) similar to bone and lower than that of human dentin. These mechanisms of toughening were not observed in the crack growth response of the sintered HAp. While enamel is the most highly mineralized tissue of the human body, the microstructural arrangement of the prisms promotes exceptional resistance to crack growth.

Nondestructive assessment of the inhibition of enamel demineralization by CO2 laser treatment using polarization sensitive optical coherence tomography

Studies have shown that lasers can be used to modify the chemical composition of tooth enamel to render it less soluble. The purpose of this study was to determine if polarization-sensitive optical coherence tomography (PS-OCT) can be used to nondestructively assess the inhibition of demineralization after CO2 laser irradiation. Human and bovine enamel specimens were irradiated by a microsecond pulsed CO2 laser operating at a wavelength of 9.3 microm. Some specimen areas were also treated with topical fluoride to create six treatment groups on each sample, including protected surface (no demineralization), protected +laser, laser, fluoride, laser+fluoride, and unprotected surface. Samples were placed in an artificial demineralization solution to create lesions approximately 100-200 microm in depth and were subsequently scanned with a PS-OCT system to assess lesion severity before sectioning for analysis by polarized light microscopy and transverse microradiography for comparison. PS-OCT was able to measure a significant reduction in the integrated reflectivity due to inhibition by the laser on both human and bovine enamel even though the laser modification of the enamel surface did cause an increase in reflectivity and decrease in optical penetration. This study shows that the PS-OCT is well suited for the clinical assessment of caries inhibition after laser treatments.

Precision ablation of dental enamel using a subpicosecond pulsed laser

In this study we report the use of ultra-short-pulsed near-infrared lasers for precision laser ablation of freshly extracted human teeth. The laser wavelength was approximately 800nm, with pulsewidths of 95 and 150fs, and pulse repetition rates of 1kHz. The laser beam was focused to an approximate diameter of 50microm and was scanned over the tooth surface. The rise in the intrapulpal temperature was monitored by embedded thermocouples, and was shown to remain below 5 degrees C when the tooth was air-cooled during laser treatment. The surface preparation of the ablated teeth, observed by optical and electron microscopy, showed no apparent cracking or heat effects, and the hardness and Raman spectra of the laser-treated enamel were not distinguishable from those of native enamel. This study indicates the potential for ultra-short-pulsed lasers to effect precision ablation of dental enamel.

Dissolution studies of bovine dental enamel surfaces modified by high-speed scanning ablation with a lambda = 9.3-microm TEA CO(2) laser

BACKGROUND AND OBJECTIVES

Previous studies have demonstrated that lasers can be used to modify the chemical composition of dental enamel to render the mineral phase more resistant to acid dissolution with minimal peripheral thermal damage. Transverse excited atmospheric (TEA) CO(2) lasers tuned to the strong mineral absorption of hydroxyapatite (HAP) near lambda = 9 microm are well-suited for the efficient ablation of dental hard tissues if the laser-pulse is stretched to greater than 5-10 microseconds to avoid plasma shielding phenomena. Moreover, TEA CO(2) lasers can be operated at very high repetition rates and are inherently less expensive and more versatile than Er:YAG and Er:YSGG solid-state lasers. In this study a lambda = 9.3-microm TEA CO(2) with a pulse duration of 8 microseconds and a repetition rate of 300 Hz was used to uniformly treat bovine enamel surfaces at ablative irradiation intensities. We hypothesized that a uniform surface layer of modified enamel of improved crystallinity and CaP phase composition would be formed with an enhanced resistance to acid-dissolution in the ablated areas at higher scanning rates used with the water spray. Such a modified layer of enamel formed at the base and walls of a cavity preparation under the irradiation conditions employed in this study have the potential to inhibit secondary caries under sealants and restorations.

STUDY DESIGN/MATERIALS AND METHODS

The surfaces of bovine enamel blocks (3 x 3 mm(2)) were rapidly scanned across the laser beam at rates of 2, 3, and 6 mm/second with and without a water-spray at an incident fluence of 30 J/cm(2). The resistance to acid dissolution was evaluated using controlled surface dissolution experiments on laser-irradiated and control samples.

RESULTS

The groups irradiated at a fluence of 30 J/cm(2) with a repetition rate of 300 Hz and a high scan rate of 6 mm/second with and without water-cooling significantly reduced the overall surface dissolution rates (P < 0.001). At low scan rates (2-3 mm/second) excessive heat deposition resulted in the formation of an outer layer of asperities containing non-apatitic CaP phases that were more susceptible to acid-dissolution. At a scanning rate of 6 mm/second even without the water spray a layer of purer phase HAP was formed without thermal damage, indicating that a high scanning rate can be used to avoid excessive thermal damage during ablation. The best results (80% inhibition) were attained for the higher scanning speed 6-mm/second combined with a water spray.

CONCLUSION

This study demonstrates that an enamel surface with enhanced resistance to acid dissolution is produced after ablation with lambda = 9.3-microm TEA CO(2) laser pulses delivered at high-repetition rates if sufficiently high scanning rates are used with or without a water-spray.

Microstructural changes of enamel, dentin-enamel junction, and dentin induced by irradiating outer enamel surfaces with CO2 laser

The microstructural changes of enamel, dentin-enamel junction (DEJ), and dentin after CO(2) laser irradiation were studied. Buccal enamel surfaces of human third molars about 2 mm from the DEJ were irradiated, and the laser tip was moved 5 mm in a mesiodistal direction with 5 s of irradiation time. The output powers were 2 to 10 W in a continuous mode, and the average doses were approximately from 250 to 1,250 J/cm(2). All specimens were examined by a scanning electron microscope, and heat-transfer simulation was also applied to calculate temperature distribution. Surface ablation of enamel and separation of enamel and dentin along the DEJ were observed when the laser power output exceeded 3 W. Heat-transfer simulation indicated that dentin was prone to store more thermal energy than enamel. In conclusion, operation parameters of the CO(2) laser should be carefully selected to avoid thermal damage to the DEJ.

Acid resistance of erbium-doped yttrium aluminum garnet laser-treated and phosphoric acid-etched enamels

OBJECTIVE

To compare the effects of erbium-doped yttrium aluminum garnet (Er:YAG) laser ablation and of phosphoric acid etching on the in vitro acid resistance of bovine enamel.

MATERIALS AND METHODS

Teeth were polished to make the surface flat. The polished enamel was either etched with 37% phosphoric acid for 30 seconds or ablated with a single 33 J/cm2 pulse from an Er:YAG laser. The control specimens were free from acid etching and laser ablation. Changes in crystal structure, dissolved mineral (calcium [Ca] and phosphorus [P]) contents, and calcium distribution in the enamel subsurface after a pH-cycling process were evaluated.

RESULTS

After laser treatment, poor crystal structures improved without forming any new phases, such as tricalcium phosphates. Among the tested enamels, dissolved mineral contents were significantly different (P < .05). Er:YAG laser-treated enamels had the lowest mineral dissolution (Ca, 13.78 ppm; P, 6.33 ppm), whereas phosphoric acid-etched enamels had the highest (Ca, 15.90 ppm; P, 7.33 ppm). The reduction rate and reduced depth of calcium content along the subsurface were lowest in Er:YAG laser-treated enamels.

CONCLUSION

The Er:YAG laser-treated enamels are more acid resistant to acid attack than phosphoric acid-etched enamels.

CO2 laser-induced zonation in dental enamel: A Raman and IR microspectroscopic study

The gradient of structural alteration and molecular exchange across CO(2) laser-irradiated areas in dental enamel was analyzed by Raman and attenuated total reflectance infrared microspectroscopy. The type and the degree of structural changes in morphologically distinguishable zones within the laser spot vary depending on the laser-irradiation parameters--power (1 and 3 W), treatment time (5 and 10 s), and operational mode (super pulse and continuous wave). Using higher power, irrespective of the operation mode, the enamel tissue ablates and a crater is formed. The prevalent phase at the bottom of the crater is dehydrated O(2) (2-)-bearing apatite, that is, the fundamental framework topology is preserved. Additional nonapatite calcium phosphate phases are located mainly at the slope of the laser crater. No structural transformation of mineral component was detected aside the crater rim, only a CO(3)-CO(2) exchange, which decays with the radial distance. A lower-power laser irradiation slightly roughens the enamel surface and the structural modification of enamel apatite is considerably weaker for continuous wave than for super pulse mode. Prolonged low-power laser treatment results in recrystallization, and thus structural recovering of apatite might be of clinical relevance for enamel surface treatments.

Thermal ablation of FEL irradiation using gypsum as an indicator

Thermal effects produced in a laser-irradiated sample were studied by micro-X-ray diffraction and micro-Fourier transform infrared spectroscopy (FTIR). Gypsum, transformed into bassanite at 124 degrees C and into anhydrite at 147 degrees C, was used as a thermal indicator. Pit formation by a wavelength-tunable free electron laser (FEL) irradiation on the gypsum pellet maximized at a wavelength of 3.0 microm, 2 mJ/shot, and pits were not detected in those irradiated at 2.6 or 3.8 microm compared with the maximum at 3.0 microm and diminished at 2.0 or 4.0 microm in the human tooth case. Micro-X-ray diffraction and micro-FTIR did not reveal any appreciable bassanite or anhydrite in the irradiated regions. From the laser ablation viewpoint, these results allow the FEL ablation to be considered as plasma or evaporative ones. This study indicated that the micro-pulse of laser was effective to prevent thermal damages of laser irradiation.

Physico-chemical changes of human enamel irradiated with ArF excimer laser

BACKGROUND AND OBJECTIVES

Irradiation of tooth enamel by lasers can alter its structure and chemical composition. The purpose of this work was to determine the compositional changes and to elucidate the mechanisms of laser-enamel interaction using ArF excimer laser.

STUDY DESIGN/MATERIALS AND METHODS

Human enamel irradiated with ArF excimer laser (wavelength, 193 nm) at different fluences, was examined using X-ray diffraction, infrared (IR) spectroscopy and microprobe analysis.

RESULTS

Ablation without significant compositional changes in irradiated enamel was evident when low fluences (approximately 200-380 mJ/cm2) were used. However, fluences between 640 and 2,300 mJ/cm2 resulted in an increased Ca/P ratio, decreased amount of carbonate and protein, and the formation of tricalcium phosphate and tetracalcium phosphate, suggesting the involvement of a photothermal mechanism.

CONCLUSIONS

The results show that ArF excimer laser can alter the chemical composition and morphology of the highly mineralized (96%) dental enamel, depending on the fluence used.

Change of Enamel after Er:YAG and CO2Laser Irradiation and Fluoride Treatment

OBJECTIVE

Our aim was to compare acquired acid resistance in dental enamel after Er:YAG and CO(2) laser irradiation in vitro with additional fluoride treatment.

BACKGROUND DATA

The application of lasers in dental hard tissue can impact dental constituents and fluoride with complex interactions.

METHODS

Bovine enamels were divided into four groups according to their surface condition: unlased, Er:YAG laser-ablated, fluoridetreated after Er:YAG laser ablation, and CO(2) laser-irradiated after Er:YAG laser and fluoride treatment. Calcium distribution in enamel after pH-cycling process and crystallographical change after laser treatment were evaluated.

RESULTS

The crystallinity of enamel was much improved after Er:YAG laser ablation. The CO(2) laser irradiation in the fluoride-treated laser enamel formed alpha-TCP and fluorapatite. The change of calcium distribution in enamel was least in the CO(2) laser-irradiated specimens; the fluoride-treated specimen after Er:YAG laser ablation was next. Additional fluoride treatment both after Er:YAG and before CO(2) laser irradiation improved the acid resistance of enamel.

CONCLUSION

Both external treatment of fluoride and irradiation of CO(2) laser after Er:YAG laser ablation greatly reduced calcium loss in enamel during the pH cycling process.

Increased fluoride uptake and acid resistance by CO2 laser-irradiation through topically applied fluoride on human enamel in vitro

OBJECTIVES

The aim of the current in vitro study was to evaluate the effect of CO(2)-laser treatment immediately after applying amine fluoride solution on enamel. It was hypothesized that such a treatment would increase enamel fluoride uptake, and reduce dissolution rate and thermal surface alterations.

METHODS

Fluoride uptake was determined in 40 human enamel sections randomly assigned to four groups (n=10), which were either left untreated (1), exposed to a 1% amine fluoride solution for 15s without irradiation (2), irradiated for 15s with a continuous-wave carbon dioxide laser (3), or laser-treated for 15s through the amine fluoride solution applied immediately beforehand (4). Fluoride uptake was determined with an ion selective electrode after acid dissolution of the specimens (surface and subsurface layers). For the determination of acid resistance, another 40 enamel sections were treated according to the above protocol. Acid resistance was determined in surface and subsurface layers by measuring eluted calcium upon 3% lactic acid exposure with atomic absorption spectrometry. Enamel surface alterations after laser irradiation were monitored using scanning electron microscopy.

RESULTS

Laser irradiation through the fluoride solution led to significantly higher fluoride contents in the surface enamel layer compared to fluoride treatment alone or laser treatment alone (p=0.002). Laser treatment with or without fluoride resulted in an increased acid resistance of enamel specimens. Fewer surface alterations were observed upon SEM examination of specimens irradiated through the amine fluoride solution compared to counterparts treated with laser only.

CONCLUSIONS

CO(2) laser light application through an amine fluoride solution may be useful and effective in the prevention of caries.

Crystalline structure of dental enamel after Ho:YLF laser irradiation

Irradiation of teeth with lasers using specific wavelengths and energy densities produces surface melting. This effect has been already applied to different procedures such as caries prevention and hypersensitivity reduction. The aim of this study is to characterize the crystalline structure of bovine enamel after holmium laser irradiation. A holmium laser (Ho:YLF) with emission wavelength of 2065 nm was used. Enamel tissues were irradiated in ablative regime and their structures before and after irradiation were analyzed using the powder X-ray diffraction technique. The X-ray diffraction patterns of non-irradiated enamel correspond to carbonated hydroxyapatite and those produced by irradiated samples indicate the existence of a mixture of two crystalline phases: hydroxyapatite and tetracalcium phosphate. The structural characteristics of holmium irradiated enamel were compared with those of the same tissue irradiated with other lasers.

Carbon dioxide laser in dental caries prevention

OBJECTIVES

To describe CO2 laser characteristics and to review the literature regarding its effects on caries inhibition in enamel and dentin. Another aim of this review is to discuss the effects of CO2 laser in combination with fluoride.

DATA AND SOURCES

The literature was searched for review and original research papers relating CO2 laser characteristics, CO2 laser effects on enamel and dentin, use of CO2 laser in dental caries prevention and the effects of CO2 laser in combination with fluoride. The articles have been selected using Medline and manual tracing of references cited in key papers otherwise not elicited.

STUDY SELECTION

Dental studies pertinent to key aspects of review, and those that focus on CO2 laser.

CONCLUSIONS

Irradiation of dental enamel by specific wavelengths and fluencies of CO2 laser alters the hydroxyapatite crystals reducing the acid reactivity of the mineral; CO2 laser irradiation in combination with fluoride treatment is more effective in inhibiting caries-like lesions than CO2 laser irradiation or fluoride alone; When laser and fluoride are combined, it is possible to reduce laser energy density and fluoride levels; If this laser technology becomes available at a reasonable cost and the results can be applied in clinical practice, there will be a promising future for this laser in caries prevention.

Prevention of Dental Caries in Partially Erupted Permanent Teeth with a CO2Laser

OBJECTIVE

The purpose of this study was to determine the effect of CO2 laser irradiation in the prevention of pit and fissure caries in immature molars with covering opercula.

BACKGROUND DATA

In pediatric dentistry, it is not unusual to find partially erupted immature permanent teeth, especially with opercula. Conventional dental caries prevention is not effective in these cases because of the immaturity of tooth substance and the presence of the opercula, which accumulate a substantial amount of plaque.

MATERIALS AND METHODS

The CO2 laser was used on 22 immature erupting molars with opercula. In each case, we first cut the operculum with a CO2 laser in a 2- or 3-watt continuous mode. Then, the occlusal surface was irradiated spot by spot along the pits and fissures of the molar using a CO2 laser in a 2-watt pulsed mode with 0.2 sec of irradiation time (average power, 0.3 watt; pulse width, 10 msec; repetition time, 15 Hz; energy density, 15 J/cm2). Each of the studied teeth was clinically examined for dental caries for 3 years.

RESULTS

It took less than 2 min to cut the operculum, and there was no bleeding. The irradiation imparted acid resistance to the teeth without any discomfort to the patients. The patients did not complain of any pain after the procedure. Only two of the studied teeth developed dental caries during the observation period.

CONCLUSION

We conclude that a CO2 laser might be an effective mode of treatment in the prevention of pit and fissure caries in partially erupted permanent molars covered with opercula.

Ultrastructural analysis of bone tissue irradiated by Er:YAG Laser

BACKGROUND AND OBJECTIVES

The use of erbium:yttrium aluminum garnet (Er:YAG) laser has been suggested for bone ablation, however, little is known about the nature of the tissue after irradiation. This study was aimed to analyze the ultrastructure of bone tissue treated with Er:YAG laser, as compared to those treated with CO(2) laser and bur drilling.

STUDY DESIGN/MATERIALS AND METHODS

Parietal bones of Wistar rats were treated and analyzed by light microscopy, transmission electron microscopy (TEM), electron diffraction analysis and energy dispersive X-ray spectroscopy (SEM-EDX).

RESULTS

This study demonstrated that Er:YAG laser irradiation resulted in a very thin changed layer of approximately 30 microm thickness, which consisted of two distinct sub-layers: a superficial, greatly altered layer and a deep, less affected layer.

CONCLUSIONS

The major changes found on bone surface after Er:YAG laser irradiation consisted of micro-cracking, disorganization, and slight recrystallization of the original apatites and reduction of surrounding organic matrix.

Sintering mechanism of the CaF2 on hydroxyapatite by a 10.6-l microm CO2 laser

BACKGROUND AND OBJECTIVES

Laser has been reported as a heat source for melting and re-crystallization. Occurring at about 1100 degrees C, the melting of surface dental enamel along with re-crystallization might have an assistant role in the therapy of hypersensitive tooth, apical sealing of endodontic surgery in dentistry, preventive dentistry for pit and fissure sealing, and fluoridation. For laser to be accepted in clinical applications, it is desired that, studies must show the incorporation of CaF(2) into hydroxyapatite could reduce the sintering temperature for the sake of safety.

STUDY DESIGN/MATERIALS AND METHODS

In this study, the Sharplan 20XJ CO(2) laser with 10.6- microm wavelength was set under the following parameters: power, 5 W; repetitive mode, 0.1 second; beam, focused. Fluorite was added to hydroxyapatite as a synthetic compound to lower the sintering temperature. Human dental enamel without caries was used for in vitro sintering test. Scanning electron microscopy (SEM), X-ray diffractometer (XRD), Fourier transforming infrared spectroscopy (FTIR), and differential thermal analysis/thermogravimetric analysis (DAT/TGA) were used for the investigation of sintering mechanism of CaF(2).

RESULTS

Fusion between hexagonal shape crystals and cubic shape crystals (CaF(2)) were observed under SEM study. Hexagonal shape crystals indicated the formation of fluorapatite under XRD analysis. Under FTIR study, we examined reductions of water (3445 cm(-1)) and hydroxyl bands (3567 and 627 cm(-1)) in irradiated compounds. From the DTA pattern of synthetic compound, it showed the endothermic reaction reaching its peak point around 1180 +/- 20 degrees C. It was attributed to the phase transformation and/or initial melting.

CONCLUSIONS

In this study, we proposed the interrelationship of the eutectics between initiator (CaF(2)) and the reaction product (calcium hydroxide) that reduced the sintering temperature. It appeared that the co-eutectics interacted to reduce the sintering temperature of hydroxyapatite below 800 degrees C and that the key eutectic was calcium hydroxide. The clinical feasibility of the melting and re-crystallization of hydroxyapatite under 10.6-microm CO(2) laser would be therefore enhanced.

Mechanism of water augmentation during IR laser ablation of dental enamel

BACKGROUND AND OBJECTIVES

The mechanism of water augmentation during IR laser ablation of dental hard tissues is controversial and poorly understood. The influence of an optically thick applied water layer on the laser ablation of enamel was investigated at wavelengths in which water is a primary absorber and the magnitude of absorption varies markedly.

STUDY DESIGN/MATERIALS AND METHODS

Q-switched and free running Er: YSGG (2.79 microm) and Er:YAG (2.94 microm), free running Ho:YAG and 9.6 microm TEA CO(2) laser systems were used to produce linear incisions in dental enamel with and without water. Synchrotron-radiation IR spectromicroscopy with the Advanced Light Source at Lawrence Berkeley National Laboratory was used to determine the chemical changes across the laser ablation profiles with a spatial resolution of 10-microm.

RESULTS

The addition of water increased the rate of ablation and produced a more desirable surface morphology during enamel ablation with all the erbium systems. Moreover, ablation was markedly more efficient for Q-switched (0.15 microsecond) versus free-running (150 microsecond) erbium laser pulses with the added water layer. Although the addition of a thick water layer reduced the rate of ablation during CO(2) laser ablation, the addition of the water removed undesirable deposits of non-apatite mineral phases from the crater surface. IR spectromicroscopy indicates that the chemical composition of the crater walls deviates markedly from that of hydroxyapatite after Er:YAG and CO(2) laser irradiation without added water. New mineral phases were resolved that have not been previously observed using conventional IR spectroscopy. There was extensive peripheral damage after irradiation with the Ho:YAG laser with and without added water without effective ablation of enamel.

CONCLUSIONS

We postulate that condensed mineral phases from the plume are deposited along the crater walls after repetitive laser pulses and such non-apatitic phases interfere with subsequent laser pulses during IR laser irradiation reducing the rate and efficiency of ablation. The ablative recoil associated with the displacement and vaporization of the applied water layer removes such loosely adherent phases maintaining efficient ablation during multiple pulse irradiation.

Effect of CO2 laser on pulpal temperature and surface morphology: an in vitro study

OBJECTIVES

The objective of this study was to evaluate the potential effects on underlying dental hard tissues of a high pulse rate carbon dioxide (CO2) laser that was designed for soft tissue surgery.

METHODS

Eighteen extracted human teeth were sectioned longitudinally, cleaned, and varnished, leaving nine exposed windows on each: six on the coronal surface (enamel) and three on the root surface (cementum, dentin). The CO2 irradiation conditions used were: wave length 10.6 microm; 1.2-2.6J/cm(2) fluence per pulse; repetition rate 120-1000Hz; 100-200ms pulse duration; and cumulative fluences ranging from 14 to 2200J/cm(2). Each window was irradiated with a 0.3mm beam diameter at one of nine power settings for 0.1, 0.5, or 1.0s. The pulp chamber temperature was measured with a microthermocouple. The irradiated teeth were evaluated by Polarized Light Microscopy (PLM) and Scanning Electron Microscopy (SEM).

RESULTS

The pulp chamber temperature rise ranged from 0.5 to 19 degrees C depending on the location of the window and distance to pulp chamber. SEM revealed crystal fusion in both enamel and dentin at all cumulative fluences. At cumulative fluences of 40J/cm(2), 200 pulses/second and higher, measurable tissue loss was observed with PLM both in dentin and enamel.

CONCLUSIONS

These results indicate there are threshold conditions above which pulsed CO2 laser light used for soft tissue surgery may cause detrimental changes to underlying oral hard tissue and to the pulp.

Free-electron laser etching of dental enamel

OBJECTIVE

The purpose of this study was to evaluate the Mark-III free-electron laser as a means of etching enamel surfaces, with potential application to resin bonding.

METHODS

The FEL was tuned to wavelengths ranging from 3.0 to 9.2 microm. Specific wavelengths that are resonantly absorbed by phosphates, proteins, and water were used. First, bovine enamel was polished and exposed to static FEL exposures. Lased enamel was examined using scanning electron microscopy (SEM). Additional bovine enamel specimens were exposed to FEL at similar wavelengths, but with rastering to create treated rectangular areas on each specimen. Surface roughness was evaluated using profilometry and atomic force microscopy (AFM). Composite was bonded to the lased enamel, and shear bond strengths were determined using an Instron universal testing machine. As a control, the surface roughness of, and shear bond strengths to, acid-etched enamel were determined.

RESULTS

Static FEL exposures caused changes in the enamel ranging from an etched appearance to pits, cracks, and frank cratering. The surface roughness of lased enamel was much greater than that of acid-etched enamel, and was qualitatively different as well. Shear bond strengths of resin to acid-etched enamel were significantly higher than bond strengths to lased enamel.

CONCLUSIONS

Under the conditions used in this study, the FEL did not offer a practical and effective method of etching enamel for resin bonding. However, the ability of the FEL to deliver many specific wavelengths makes it an interesting tool for further research of laser effects on tooth structure.

Phase, compositional, and morphological changes of human dentin after Nd:YAG laser treatment

Although techniques for repairing root fracture have been proposed, the prognosis is generally poor. If the fusion of a root fracture by laser is possible, it will offer an alternative to extraction. Our group has attempted to use lasers to fuse a low melting-point bioactive glass to fractured dentin. This report is focused on the phase, compositional, and morphological changes observed by means of X-ray diffractometer, Fourier transforming infrared spectroscopy, and scanning electron microscopy-energy dispersive X-ray spectroscopy in human dentin after exposure to Nd:YAG laser. The irradiation energies were from 150 mJ/ pulse-10 pps-4 s to 150 mJ/pulse-30 pps-4 s. After exposure to Nd:YAG laser, dentin showed four peaks on the X-ray diffractometer that corresponding to a-tricalcium phosphate (TCP) and beta-TCP at 20 = 30.78 degrees/34.21 degrees and 32.47 degrees/33.05 degrees, respectively. The peaks of a-TCP and beta-TCP gradually increased in intensity with the elevation of irradiation energy. In Fourier transforming infrared analysis, two absorption bands at 2200 cm(-1) and 2015 cm(-1) could be traced on dentin treated by Nd:YAG laser with the irradiation energies beyond 150 mJ/pulse-10 pps-4 s. The energy dispersive X-ray results showed that the calcium/phosphorus ratios of the irradiated area proportionally increased with the elevation of irradiation energy. The laser energies of 150 mJ/ pulse-30 pps-4 s and 150 mJ/pulse-20 pps-4 s could result in the a-TCP formation and collagen breakdown. However, the formation of glass-like melted substances without a-TCP at the irradiated site was induced by the energy output of 150 mJ/ pulse-10 pps-4 s. Scanning electron micrographs also revealed that the laser energy of 150 mJ/ pulse-10 pps-4 s was sufficient to prompt melting and recrystallization of dentin crystals without cracking. Therefore, we suggest that the irradiation energy of Nd:YAG laser used to fuse a low melting-point bioactive glass to dentin is 150 mJ/ pulse-10 pps-4 s.

In vitro study of the Nd:YAG laser effect on human dental enamel: optical and scanning electron microscope analysis

OBJECTIVE

The Nd:YAG laser irradiation of dental enamel was evaluated in enamel demineralization experiments in a Streptococcus mutans culture media.

SUMMARY BACKGROUND DATA

Previous studies had shown that a continuous wave Nd:YAG laser at an energy of approximately 67 mJ may induce an increased acid resistance in human dental enamel when exposed to severe demineralization conditions.

METHODS

Enamel windows of 3 x 4 cm in the buccal surface were irradiated with a continuous wave Nd:YAG laser at a wavelength of 1,064 microns using energy densities of from 83.75 to 187.50 J/cm2. Enamel windows of 3 x 4 cm on the lingual surface served as control (without the laser irradiation). The enamel windows were then exposed to a Streptococcus mutans culture media at a temperature of 37 degrees C for 15 and 21 days. The laser effects and demineralization were examined both by optical microscopy and scanning electron microscopy (SEM).

RESULTS

A comparison between the lased and the unlased windows of enamel showed fusion and recrystalization of the enamel and increased acid-resistance in all groups irradiated with the Nd:YAG laser. On the other hand, the 3 x 4 delimited enamel surfaces from the control group (not irradiated with the Nd:YAG laser) showed 100% demineralization.

CONCLUSIONS

These findings are consistent with the finding that laser irradiation of dental results in significant reduction of the effective solubility of enamel mineral.

Investigational study of the use of Er:YAG laser versus dental drill for caries removal and cavity preparation--phase I

OBJECTIVE

We determined that the Er:YAG pulsed 2.94 micron radiation was successful in the removal of caries, cavity preparation, and etching prior to acid etching.

SUMMARY BACKGROUND DATA

The laser group was compared to a control group in which the high-speed drill was employed. Parameters measured included histological evaluation of the pulp, scanning electron microscopy of the surface morphology of the tooth, dye penetration studies, bond strength measurements, and rating of the laser's ability to remove caries and form the preparation.

METHODS

We collectively evaluated 60 patients with 106 teeth in both the laser and control groups over a 1-year period. Teeth were treated in vivo and then extracted immediately, at 2 days, 1 month, and up to 1-year to assess pulpal healing, surface morphology, and the quality of the preparation, restoration, and pain.

RESULTS

The dental laser was shown to be equal or better than the drill in the tested procedures of caries removal, cavity preparation, and etching prior to acid etching. The scanning electron microscopy revealed no microfracturing, open dentinal tubules, and effective etching with the laser having a mean of 2.7 with an optimum rating of 3. The histological testing confirmed that the pulp was not compromised using the laser with scores of theta for hemorrhage, 0.47 for hyperemia, and 0.12 for inflammation on a scale of 0 to 3 where 0 is no effect.

CONCLUSIONS

The FDA has recently cleared the Er:YAG to remove all classes of caries, form the cavity preparation, and modify the enamel and dentin prior to acid etching. In this Phase I study conducted as part of the clinical trials, there were no complications and no tooth was compromised. Patients were consistently treated without anesthesia with the same or better results than the drill as confirmed by scanning electron microscopy and histological studies.

Crystallographic analysis of demineralized human enamel treated by laser-irradiation or remineralization

Crystallographic information on dental hard tissue is helpful in evaluating whether incipient caries that has received preventative treatments is resistant to subsequent attack. The aim here was to analyse crystallographically by means of high-resolution electron microscopy (HREM) demineralized human enamel that had been laser-irradiated or remineralized. Electron-microscopic observation identified a distinct layer at a depth of 100 nm in the demineralized and laser-irradiated enamel. The crystallinity in the shallower area was inferior to that in the deeper area. Comparison of the HREM findings from the deeper area with the data provided by the Joint Committee on Powdered Diffraction Standards revealed that the mineral in the demineralized and laser-irradiated enamel was either alpha- or beta-tricalcium phosphate, while that in the remineralized enamel was thought to be tetracalcium diphosphate monoxide.

Morphological study of the effects of CO2 laser emitted at 9.3 microm on human dentin

OBJECTIVE

The purpose of this study was to investigate the effects of dentin ablation using a carbon dioxide (CO2) laser emitted at 9.3 microm by scanning electron microscopy (SEM) and confocal laser scanning microscopy (CLSM).

BACKGROUND DATA

There have been no reports on effects of CO2 laser irradiation emitted at 9.3 microm on dentin by SEM and CLSM.

METHODS

Thirty extracted human teeth showing no clinical signs of caries were used. All teeth were horizontally sectioned to approximately 200 microm thickness and sections were irradiated using a 9.3 microm CO2 laser at different parameters as follows: 26 mJ [energy density (ED) 53.0 J/cm2] and 30 mJ (ED 61.1 J/cm2). After laser irradiation, samples were treated with sodium hypochlorite, stained using rhodamine-123, and observed with CLSM followed by SEM procedures.

RESULTS

No craters or cracks were observed, but many small molten and rehardened particles were documented on the sample surface using SEM. Some small cracks were seen in the subsurface layer, and some patent dentinal tubules were detected using CLSM.

CONCLUSION

These results suggest that laser irradiation at these parameters affected the sample surface only (less than 20 microm) and would be less harmful to thermal damage of dental pulp for dentin ablation.

Permanent and transient changes in the reflectance of CO2 laser-irradiated dental hard tissues at lambda = 9.3, 9.6, 10.3, and 10.6 microns and at fluences of 1-20 J/cm2

BACKGROUND AND OBJECTIVE

Effective use of lasers for preventive dental treatments requires accurate knowledge of the amount and distribution of laser energy deposited during irradiation. At CO2 wavelengths, the reflection losses are considerable and reduce the laser energy absorbed by the tissue surface.

STUDY DESIGN/MATERIALS AND METHODS

The specular and diffuse reflectance of enamel and dentin were measured at the 10.6-, 10.3-, 9.6-, and 9.3-microns wavelengths of the CO2 laser. Changes in reflectance during and after laser irradiation were investigated.

RESULTS

The low-fluence reflectance (< 1 J/cm2) of calcified dental tissues at CO2 wavelengths varies between 9% and 50%. Permanent and transient changes in the reflectance are induced at higher irradiation intensities.

CONCLUSION

These changes resulted in increased energy coupling during irradiation.