Perfusion and cyclic compression of mesenchymal cell-loaded and clinically applicable osteochondral grafts

Enhanced migration of human bone marrow stromal cells in modified collagen hydrogels

PURPOSE

Collagen I hydrogels are widely used as scaffolds for regeneration of articular cartilage defects. We hypothesised that ingrowth might be improved by removing the superficial layer of a compressed hydrogel. The control group consisted of the original unmodified product.

METHODS

The migration of human bone marrow stromal cells (hBMSCs) into the hydrogel was evaluated by confocal microscopy. We quantified the DNA concentration of the hydrogel for each group and time point and evaluated the chondrogenic differentiation of cells.

RESULTS

After one week, the detectable amount of cells at the depth of 26-50 μm was significantly higher in the modified matrix (MM) than in the non-modified matrix (NM) (p = 0.011). The maximum depth of penetration was 75 μm (NM) and 200 μm (MM). After three weeks, the maximum depth of penetration was 175 μm (NM) and 200 μm (MM). Likewise, at a depth of 0-25 μm the amount of detectable cells was significantly higher in the MM group (p = 0.003). After 14 days, the concentration of DNA was significantly higher in the samples of the MM than in the control group (p = 0.000). Staining of histological sections and labelling with collagen II antibodies showed that a chondrogenic differentiation of cells in the scaffold can occur during in vitro cultivation.

CONCLUSIONS

Removing the superficial layer is essential to ensuring proper ingrowth of cells within the compressed hydrogel. Compressed hydrogels contribute better to cartilage regeneration after surface modification.

The interplay between chondrocyte redifferentiation pellet size and oxygen concentration

Chondrocytes dedifferentiate during ex vivo expansion on 2-dimensional surfaces. Aggregation of the expanded cells into 3-dimensional pellets, in the presence of induction factors, facilitates their redifferentiation and restoration of the chondrogenic phenotype. Typically 1×10(5)-5×10(5) chondrocytes are aggregated, resulting in "macro" pellets having diameters ranging from 1-2 mm. These macropellets are commonly used to study redifferentiation, and recently macropellets of autologous chondrocytes have been implanted directly into articular cartilage defects to facilitate their repair. However, diffusion of metabolites over the 1-2 mm pellet length-scales is inefficient, resulting in radial tissue heterogeneity. Herein we demonstrate that the aggregation of 2×10(5) human chondrocytes into micropellets of 166 cells each, rather than into larger single macropellets, enhances chondrogenic redifferentiation. In this study, we describe the development of a cost effective fabrication strategy to manufacture a microwell surface for the large-scale production of micropellets. The thousands of micropellets were manufactured using the microwell platform, which is an array of 360×360 µm microwells cast into polydimethylsiloxane (PDMS), that has been surface modified with an electrostatic multilayer of hyaluronic acid and chitosan to enhance micropellet formation. Such surface modification was essential to prevent chondrocyte spreading on the PDMS. Sulfated glycosaminoglycan (sGAG) production and collagen II gene expression in chondrocyte micropellets increased significantly relative to macropellet controls, and redifferentiation was enhanced in both macro and micropellets with the provision of a hypoxic atmosphere (2% O2). Once micropellet formation had been optimized, we demonstrated that micropellets could be assembled into larger cartilage tissues. Our results indicate that micropellet amalgamation efficiency is inversely related to the time cultured as discreet microtissues. In summary, we describe a micropellet production platform that represents an efficient tool for studying chondrocyte redifferentiation and demonstrate that the micropellets could be assembled into larger tissues, potentially useful in cartilage defect repair.

Effects of perfusion and cyclic compression on in vitro tissue engineered meniscus implants

PURPOSE

The purpose of this study was to investigate the influence of continuous perfusion and mechanical stimulation on bone marrow stromal cells seeded on a collagen meniscus implant.

METHODS

Bone marrow aspirates from 6 donors were amplified in vitro. 10(6) human BMSC were distributed on a collagen meniscus implant. Scaffolds were cultured under static conditions (control) or placed into a bioreactor system where continuous perfusion (10 ml/min) or perfusion and mechanical stimulation (8 h of 10% cyclic compression at 0.5 Hz) were administered daily. After 24 h, 7 and 14 days, cell proliferation, synthesis of procollagen I and III peptide (PIP, PIIIP), histology, and the equilibrium modulus of the constructs were analyzed.

RESULTS

Proliferation demonstrated a significant increase over time in all groups (p < 0.001). PIP synthesis was found to increase from 0.1 ± 0.0 U/ml/g protein after 24 h to 2.0 ± 0.5 (perfusion), 3.8 ± 0.3 (mechanical stimulation), and 1.8 ± 0.2 U/ml/g protein (static control, lower than perfusion and mechanical stimulation, p < 0.05). These differences were also evident after 2 weeks (2.7 ± 0.3, 4.0 ± 0.6, and 1.8 ± 0.2 U/ml/g protein, p < 0.01); PIIIP synthesis was found to increase from 0.1 ± 0.0 U/ml/g protein after 24 h to 2.9 ± 0.7 (perfusion), 3.1 ± 0.9 (mechanical stimulation), and 1.6 ± 0.3 U/ml/g protein (controls) after 1 week and remained significantly elevated under the influence of perfusion and mechanical stimulation (p < 0.01) after 2 weeks. Mechanical stimulation increased the equilibrium modulus more than static culture and perfusion after 2 weeks (24.7 ± 7.6; 12.3 ± 3.7; 15.4 ± 2.6 kPa; p < 0.02).

CONCLUSION

Biomechanical stimulation and perfusion have impact on collagen scaffolds seeded with BMSCs. Cell proliferation can be enhanced using continuous perfusion and differentiation is fostered by mechanical stimulation.

Three-dimensional culture and bioreactors for cellular therapies

A bioreactor is defined as a specifically designed vessel to facilitate the growth of organisms and cells through application of physical and/or electrical stimulus. When cells with therapeutic potential were first discovered, they were initially cultured and expanded in two-dimensional (2-D) culture vessels such as plates or T-flasks. However, it was soon discovered that bioreactors could be used to expand and maintain cultures more easily and efficiently. Since then, bioreactors have come to be accepted as an indispensable tool to advance cell and tissue culture further. A wide array of bioreactors has been developed to date, and in recent years businesses have started supplying bioreactors commercially. Bioreactors in the research arena range from stirred tank bioreactors for suspension culture to those with various mechanical actuators that can apply different fluidic and mechanical stresses to tissues and three-dimensional (3-D) scaffolds. As regenerative medicine gains more traction in the clinic, bioreactors for use with cellular therapies are being developed and marketed. While many of the simpler bioreactors are fit for purpose, others fail to satisfy the complex requirements of tissues in culture. We have examined the use of different types of bioreactors in regenerative medicine and evaluated the application of bioreactors in the realization of emerging cellular therapies.

No effect in combining chondrogenic predifferentiation and mechanical cyclic compression on osteochondral constructs stimulated in a bioreactor

Traumatic and degenerative osteochondral lesions are a common problem in orthopaedic surgery. The concept of tissue engineering represents the possibility of a promising therapeutical approach. The purpose of this study has been to improve the characteristics of osteochondral grafts consisting of a human certified collagen I-bone hybrid matrix seeded with human bone marrow stromal cells and stimulated in a custom-made biomechanoreactor. This study was undertaken as a follow-up to our prior studies. Based on our established system, we added chondrogenic growth factors (IGF-1 and TGF-beta(2)) and evaluated their effect on chondrogenic differentiation. Constructs were stimulated for 14, 21 and 28 days respectively by different protocols, including cyclic mechanical stimulation, hormonal stimulation or a combination of both. More than 70% of the cells were viable throughout the entire experimental period. Histological analysis revealed a homogeneous distribution of cells in a cartilage-like matrix organization. Immunohistological collagen II staining was positive irrespective of stimulation manner and time. Levels of DNA and glycosaminoglycans, having been normalized to DNA, did not change. Analysis of the biomechanical stiffness after 14 days showed increased stiffness in the hormonally and mechanically stimulated group compared to the static group. Stimulation time did not have a significant influence. The media supplements to foster the quality of the tissue tested here did not show any progress in our system. We conclude that cyclic compression enhances matrix stiffness, but stimulation time should be kept short and growth factors should be left out in this system with regard to clinical applicability and financial concerns.