Investigation on Microbial Biodeterioration of the Stone Monuments in Yildiz Technical University-Yildiz Campus-Istanbul-Turkey

On the Response to Aging of OPEFB/Acrylic Composites: A Fungal Degradation Perspective

Biological agents and their metabolic activity produce significant changes over the microstructure and properties of composites reinforced with natural fibers. In the present investigation, oil palm empty fruit bunch (OPEFB) fiber-reinforced acrylic thermoplastic composites were elaborated at three processing temperatures and subjected to water immersion, Prohesion cycle, and continuous salt-fog aging testing. After exposition, microbiological identification was accomplished in terms of fungal colonization. The characterization was complemented by weight loss, mechanical, infrared, and thermogravimetric analysis, as well as scanning electron microscopy. As a result of aging, fungal colonization was observed exclusively after continuous salt fog treatment, particularly by different species of Aspergillus spp. genus. Furthermore, salt spray promoted filamentous fungi growth producing hydrolyzing enzymes capable of degrading the cell walls of OPEFB fibers. In parallel, these fibers swelled due to humidity, which accelerated fungal growth, increased stress, and caused micro-cracks on the surface of composites. This produced the fragility of the composites, increasing Young's modulus, and decreasing both elongation at break and toughness. The infrared spectra showed changes in the intensity and appearance of bands associated with functional groups. Thermogravimetric results confirmed fungal action as the main cause of the deterioration.

Microbial Diversity on the Surface of Historical Monuments in Lingyan Temple, Jinan, China

Lingyan Temple is an important part of the World Heritage Mixed Property on Mount Taishan, in which numerous cultural heritage monuments, including exquisite painted arhat statues and inscriptions, display the ancient Chinese Buddhist culture. However, these monuments are suffering aesthetic and structural damage due to rich biofilms. In this study, the microbial communities colonized on historical monuments in different microenvironments were characterized through a combination of culture-dependent techniques and high-throughput sequencing. Microbial diversity was significantly different among the historical sites with different microenvironments. For example, Actinobacteria and Ascomycota were the core phyla in the indoor samples, while they were less abundant in the outdoor samples, and phototrophic microorganisms including Cyanobacteria and green algae were only dominant in the samples near springs. The results suggested that environmental factors such as water and airborne microorganisms may be the main causes influencing microbial distribution. Most of the identified dominant species were common on the historical monuments and could contribute to biodeterioration. This analysis of microbiota will provide further information on the biodeterioration processes and preservation strategies of cultural heritage monuments in Lingyan Temple.