Formation and destruction of physical crosslinks by mild treatments in chemically crosslinked poly(vinyl alcohol) gels

Irreversible Swelling Behavior and Reversible Hysteresis in Chemically Crosslinked Poly(vinyl alcohol) Gels

We report the swelling properties of chemically crosslinked poly(vinyl alcohol) (PVA) gels with high degrees of polymerization and hydrolysis. Physical crosslinking by microcrystallites was introduced in this chemical PVA gel by a simple dehydration process. The equilibrium swelling ratio was measured in several mixed solvents, which comprised two-components: a good solvent (water or dimethyl sulfoxide (DMSO)), and a poor organic solvent for PVA. In the case of aqueous/organic solvent mixtures subjected to a multiple-sample test, the swelling ratio decreased continuously when the concentration of the organic solvent increased, reaching a collapsed state in the respective pure organic solvents. In the case of DMSO, starting from a swollen state, the swelling ratio rapidly decreased by between 15 and 50 mol % when the concentration of the organic compound increased in a single-sample test. To understand the hysteresis phenomenon, the swelling ratio was measured in a DMSO/acetone mixed solvent, starting from a collapsed state in acetone. The reversibility of swelling in response to successive concentration cycles between DMSO and acetone was examined. As a result, an irreversible swelling behavior was observed in the first cycle, and the swelling ratio in acetone after the first cycle became larger than the initial ratio. Subsequently, the swelling ratio changed reversibly, with a large hysteresis near a specific molar ratio of DMSO/acetone of 60/40. The microstructures were confirmed by Fourier transform infrared spectroscopy during the cycles. The irreversible swelling behavior and hysteresis are discussed in terms of the destruction and re-formation of additional physical crosslinking in the chemical PVA gels.

Reproduction method for dried biomodels composed of poly (vinyl alcohol) hydrogels

Models mimicking the realistic geometries and mechanical properties of human tissue are requiring ever-better materials. Biomodels made of poly (vinyl alcohol) are particularly in demand, as they can be used to realistically reproduce the characteristics of blood vessels. The reproducibility of biomodels can be altered due to dehydration that is observed after long periods of usage. In order to improve their usability, one should consider the method used to reproduce them; however, few studies have reported a method reproduce biomodels. This study proposes a novel reproduction method for biomodels that allows them to quickly and easily reproduce their geometric and mechanical properties. Specimens of the dried biomodels were reformed through immersion in temperature-controlled water. Our results show that water at 35 °C can be effective to reproduce both the geometric and mechanical properties of the specimens. X-ray diffraction (XRD) measurements revealed that water immersion can reform the crystal structure of the pre-dried specimens, and images obtained using micro-computed tomography acquisition show that the geometry of the specimens can be reformed by water immersion without introducing any defects. These results indicate that the proposed method can lead to high reproducibility of both the original geometric and mechanical properties of the dried biomodels.