Design of experiments for thermo-mechanical behavior of polypropylene/high-density polyethylene/nanokaolinite clay composites

Effects of wood fiber impulse-cyclone drying process on the UV-accelerated aging properties of wood-plastic composites

The impulse-cyclone drying and the silane coupling agent (A187) modification are applied to treat wood fibers under the following conditions: 180°C, 180°C+A187, 200°C+A187, 220°C+A187 and 240°C+ A187. Then, HDPE/wood fiber composites are fabricated with a two-stage plastic extruder, and the effects of impulse-cyclone drying technique on the UV-accelerated aging properties of composites are investigated. Fourier-transform infrared spectroscopy (FTIR) reveals that the silane coupling agent chemically reacts with the hydroxyl groups on the wood fiber surfaces, the anti-UV aging properties of composites is enhanced. Mechanical test shows that during the 0-3000 h of UV aging process, the mechanical properties of samples tend to increase initially and then decrease within a period of time. After 3000 h of UV aging, the specimen 4 exhibits the least loss of mechanical properties, with flexural modulus, flexural modulus and impact strength of 65.40 Mpa, 2082.08 Mpa and 12.85 Mpa, respectively. The effects of impulse-cyclone drying technique on the UV-accelerated aging properties of composites are investigated through Spectrophotometry and Surface microstructure observation. indicates that the ΔL* and ΔE* values increase greatly at the stage of 0-1000 h aging, which though tend to stabilize after 1000 h. The degree of discoloration changes little for specimen 4,and the number of surface cracks is relatively small, which exhibits the optimal aging resistance. In conclusion, the addition of wood fibers treated by impulse-cyclone drying (220°C) and A187 modification is effective in enhancing the anti-UV aging properties of HDPE/wood fiber composites. Nevertheless, such enhancing effect turns to decline when the temperature of impulse-cyclone drying treatment is excessively high.

Effect of Modified Red Pottery Clay on the Moisture Absorption Behavior and Weatherability of Polyethylene-Based Wood-Plastic Composites

Red pottery clay (RPC) was modified using a silane coupling agent, and the modified RPC (mRPC) was then used to enhance the performance of high-density polyethylene-based wood-plastic composites. The effect of the mRPC content on the performances of the composites was investigated through Fourier transform infrared spectrometry, differential mechanical analysis (DMA) and ultraviolet (UV)-accelerated aging tests. After adding the mRPC, a moisture adsorption hysteresis was observed. The DMA results indicated that the mRPC effectively enhanced the rigidity and elasticity of the composites. The mRPC affected the thermal gravimetric, leading to a reduction of the thermal degradation rate and a right-shift of the thermal degradation peak; the initial thermal degradation temperature was increased. After 3000 h of UV-accelerated aging, the flexural strength and impact strength both declined. For aging time between 0 and 1000 h, the increase in amplitude of ΔL* (luminescence) and ΔE* (color) reached a maximum; the surface fading did not became obvious. ΔL* and ΔE* increased more significantly between 1000 and 2000 h. These characterization results indicate that the chromophores of the mRPC became briefly active. However, when the aging times were higher than 2000 h, the photo-degradation reaction was effectively prevented by adding the mRPC. The best overall enhancement was observed for an mRPC mass percentage of 5%, with a storage modulus of 3264 MPa and an increase in loss modulus by 16.8%, the best anti-aging performance and the lowest degree of color fading.