Mechanical and thermal properties of cationic ring-opening o-cresol formaldehyde epoxy/polyurethane acrylate composites enhanced by reducing graphene oxide

Exceptional performance of Fe@carbon-rich nanoparticles prepared via hydrothermal carbonization of oil mill wastes for H2S removal

Carbon-encapsulated iron oxide nanoparticles (CE-nFe) have been obtained from an industrial waste (oil mill wastewater-OMW, as a carbonaceous source), and using iron sulfate as metallic precursor. In an initial step, the hydrochar obtained has been thermally activated under an inert atmosphere at three different temperatures (600 °C, 800 °C and 1000 °C). The thermal treatment promotes the development of core-shell nanoparticles, with an inner core of α-Fe/Fe3O4, surrounded by a well-defined graphite shell. Temperatures above 800 °C are needed to promote the graphitization of the carbonaceous species, a process promoted by iron nanoparticles through the dissolution, diffusion and growth of the carbon nanostructures on the outer shell. Breakthrough column tests show that CE-nFe exhibit an exceptional performance for H2S removal with a breakthrough capacity larger than 0.5-0.6 g H2S/gcatalyst after 3 days experiment. Experimental results anticipate the crucial role of humidity and oxygen in the adsorption/catalytic performance. Compared to some commercial samples, these results constitute a three-fold increase in the catalytic performance under similar experimental conditions.

Graphene Oxide and Oxidized Carbon Black as Catalyst for Crosslinking of Phenolic Resins

Influence of different graphite-based nanofillers on crosslinking reaction of resorcinol, as induced by hexa(methoxymethyl)melamine, is studied. Curing reactions leading from low molecular mass compounds to crosslinked insoluble networks are studied by indirect methods based on Differential Scanning Calorimetry. Reported results show a catalytic activity of graphene oxide (eGO) on this reaction, comparable to that one already described in the literature for curing of benzoxazine. For instance, for an eGO content of 2 wt %, the exothermic crosslinking DSC peak (upon heating at 10 °C/min) shifted 6 °C. More relevantly, oxidized carbon black (oCB) is much more effective as catalyst of the considered curing reaction. In fact, for an oCB content of 2 wt %, the crosslinking DSC peak can be shifted more than 30 °C and a nearly complete crosslinking is already achieved by thermal treatment at 120 °C. The possible origin of the higher catalytic activity of oCB with respect to eGO is discussed.