Modification and characterization of urethane acrylate oligomers used for UV-curable coatings

Optimization of UV-Curable Polyurethane Acrylate Coatings with Hexagonal Boron Nitride (hBN) for Improved Mechanical and Adhesive Properties

Polymer coatings are widely used in industries for protection, decoration, and specific applications, typically including volatile organic compounds (VOCs) to achieve low viscosity. The growing environmental concerns and the anticipated limits on fossil feedstock have driven the coating industry towards eco-friendly alternatives, with UV-curing technology emerging as a promising solution due to its energy efficiency, low-temperature operation, reduced VOC emissions, and high curing speed. Polyurethane acrylates (PUAs) are critical in UV-curable formulations, offering excellent flexibility, impact strength, optical, and adhesion properties. However, UV-cured PUA coatings face limitations in thermal stability and tensile strength, which can be addressed by incorporating fillers. This study investigates the effects of multi-functionalized hexagonal boron nitride (hBN) nanoparticles on the mechanical, thermal, optical, and adhesion properties of UV-cured PUA films and coatings for pre-coated metals. The results demonstrated that incorporating hBN nanoparticles enhanced the mechanical and thermal properties of the nanocomposite films, with optimal performance observed at 0.5% hBN loading. Despite the improved properties, the FTIR spectra indicated that the low concentration of hBN did not produce significant changes, potentially due to the overshadowing signals from the difunctional polyurethane acrylate.

Preparation and Characterization of 3D-Printed Biobased Composites Containing Micro- or Nanocrystalline Cellulose

Stereolithography (SLA), one of the seven different 3D printing technologies, uses photosensitive resins to create high-resolution parts. Although SLA offers many advantages for medical applications, the lack of biocompatible and biobased resins limits its utilization. Thus, the development of new materials is essential. This work aims at designing, developing, and fully characterizing a bio-resin system (made of poly(ethylene glycol) diacrylate (PEGDA) and acrylated epoxidized soybean oil (AESO)), filled with micro- or nanocellulose crystals (MCC and CNC), suitable for 3D printing. The unfilled resin system containing 80 wt.% AESO was identified as the best resin mixture, having a biobased content of 68.8%, while ensuring viscosity values suitable for the 3D printing process (>1.5 Pa s). The printed samples showed a 93% swelling decrease in water, as well as increased tensile strength (4.4 ± 0.2 MPa) and elongation at break (25% ± 2.3%). Furthermore, the incorporation of MCC and CNC remarkably increased the tensile strength and Young’s modulus of the cured network, thus indicating a strong reinforcing effect exerted by the fillers. Lastly, the presence of the fillers did not affect the UV-light penetration, and the printed parts showed a high quality, thus proving their potential for precise applications.