Rheological, thermal and mechanical properties of biodegradable poly(lactic acid)/poly(butylene adipate-co-terephthalate)/poly(propylene carbonate) polyurethane trinary blown films

Improving the compatibility and toughness of sustainable polylactide/poly(butylene adipate-co-terephthalate) blends by incorporation of peroxide and diacrylate

Polylactide/poly(butylene adipate-co-terephthalate) (PLA/PBAT) blends were compatibilized using dicumyl peroxide (DCP) and poly(ethylene glycol) 600 diacrylate (PEG600DA) through a one-step melt-blending process. The compatibility and performance of these blends were subsequently characterized. The results showed that grafts formed "in situ" effectively improved the compatibility and interfacial adhesion between PLA and PBAT phases. Melt viscosity and elasticity of both the PLA/PBAT/DCP and PLA/PBAT/DCP/PEG600DA blends evinced significant increases. Compared to PLA alone, both cold and melt crystallization abilities of the PLA/PBAT/DCP/PEG600DA blends were enhanced, with crystallinities increasing by 5 % - 10 %. Furthermore, the thermal stability, as well as hydrophobicity and oleophobicity of the compatibilized blends improved. In comparison with PLA, the elongation at break and notched impact strength for the PLA/PBAT/DCP/PEG600DA (60/40/0.1/4) blend achieved increases of 290 % and 44.23 kJ/m2, corresponding to improvements of 279 % and 1457 %, respectively. The toughening effect was substantially influenced by the ductile matrix (either a co-continuous phase or a flexible PBAT matrix) in addition to the strong interfacial adhesion and fine phase domain. These eco-friendly blends exhibit considerable potential for packaging articles and 3D printing products owing to their excellent mechanical properties and enhanced melt rheology.

Improvement of properties of polylactic acid/polypropylene carbonate blends using epoxy soybean oil as an efficient compatibilizer

Epoxidized soybean oil (ESO) was used as a compatibilizer and blended with polylactic acid (PLA) and polypropylene carbonate (PPC) resin to prepare a series of PLA/PPC/ESO blends with varying compositions. The influence of the variation in the amount of ESO added to the blend system on the thermal properties, optical properties, rheological properties, mechanical properties, and microscopic morphology of the blends was studied. The research indicates that ESO can react with PLA and PPC to form a chemical bond interface, which improves the compatibility of PLA and PPC to a certain extent. With the increase in the amount of ESO added to the blend (1- 5 phr), the complete decomposition temperature, storage modulus, loss modulus, complex viscosity, notched impact strength, and elongation at break of the blend all show a trend of continuous increase. At the same time, the melt flow rate, light transmittance, and tensile strength of the blend do not show significant fluctuations. When the amount of ESO in the system is 5 phr, compared with the PLA/PPC blend, the notched impact strength and elongation at break of the PLA/PPC/ESO blend increase from 4270.3 J/m2, 43.89 % to 8560.4 J/m2, 211.28 %, respectively, and its tensile strength and transmittance still remain around 63 MPa, 92 %. This improves the toughness of the blend while maintaining its rigidity, demonstrating excellent mechanical and optical properties. At this time, the microscopic morphology of the fracture surface of the impact sample also shows obvious characteristics of tough fracture. However, when the amount of ESO added to the blend is excessive (6 phr), the compatibility of the blending system decreases, which will degrade the performance of the blending material and ultimately destroy the phase morphology of the blend and reduce its mechanical properties.

Effect of Different Comonomers Added to Graft Copolymers on the Properties of PLA/PPC/PLA-g-GMA Blends

The melt-free radical grafting of glycidyl methacrylate (GMA) onto poly (lactic acid) (PLA) with styrene (St), α-methylstyrene (AMS), and epoxy resin (EP) as comonomers in a twin-screw extruder was used to prepare PLA-g-GMA graft copolymers. The prepared graft copolymers were then used as compatibilizers to prepare PLA/PPC/PLA-g-GMA blends by melt blending with PLA and polypropylene carbonate (PPC), respectively. The effects of different comonomers in the PLA-g-GMA graft copolymers on the thermal, rheological, optical, and mechanical properties and microstructure of the blends were studied. It was found that the grafting degree of PLA-g-GMA graft copolymers was increased to varying degrees after the introduction of comonomers in the PLA-g-GMA grafting reaction system. When St was used as the comonomer, the grafting degree of the PLA-g-GMA graft copolymer increased most significantly, from 0.8 to 1.6 phr. St as a comonomer also most improved the compatibility between PLA and PPC, and the haze of the blends was reduced while maintaining high transmittance. In addition, the PLA-g-GMA graft copolymer with the introduction of St as a comonomer significantly improved the impact toughness of the blends, while the thermal stability and tensile strength of the blends remained largely unchanged.