An intumescent flame-retardant layer with β-cyclodextrin as charring agent and its flame retardancy in jute/polypropylene composites

Water Hyacinth Fiber as a Bio-Based Carbon Source for Intumescent Flame-Retardant Poly (Butylene Succinate) Composites

In this study, flame-retardant poly (butylene succinate) (PBS) composites were developed utilizing a bio-based intumescent flame retardant (IFR) system. Water hyacinth fiber (WHF) was used as a bio-based carbon source, while ammonium polyphosphate (APP) served as both an acid source and a blowing agent. Effects of WHF:APP weight ratio and total IFR content on the thermal stability and flammability of WHF/APP/PBS composites were investigated. The results demonstrated that the 15WHF/30APP/PBS composite with a WHF to APP ratio of 1:2 and a total IFR content of 45 wt% had a maximum limiting oxygen index (LOI) value of 28.8% and acquired good flame retardancy, with a UL-94 V-0 rating without polymer-melt dripping. Additionally, its peak heat release rate (pHRR) and total heat release (THR) were, respectively, 53% and 42% lower than those of the neat PBS. Char residue analysis revealed that the optimal WHF:APP ratio and total IFR content promoted the formation of a high graphitized intumescent char with a continuous and dense structure. In comparison to the neat PBS, the tensile modulus of the 15WHF/30APP/PBS composite increased by 163%. Findings suggested the possibility of employing WHF, a natural fiber, as an alternative carbon source for intumescent flame-retardant PBS composites.

Synergistic Effects of DOPO-Based Derivative and Organo-Montmorillonite on Flame Retardancy, Thermal Stability and Mechanical Properties of Polypropylene

Polypropylene (PP), as a general thermoplastic polymer, is broadly used in different fields. However, the high flammability, melt dripping and poor mechanical properties of PP are a constraint to the expansion of its applications. In this paper, PP composites containing a combination of a phenethyl-bridged DOPO derivative (PN-DOPO) and organic montmorillonite (OMMT) were prepared via melt blending. The synergistic effects of PN-DOPO and OMMT on the flame retardancy, thermal stability and mechanical properties of PP composites were investigated systematically. The results showed that 20 wt% addition of PN-DOPO with OMMT improved the flame retardancy of PP composites. In particular, the introduction of 17 wt% PN-DOPO and 3 wt% OMMT increased the LOI values of the PP matrix from 17.2% to 23.6%, and the sample reached the V-0 level and reduced the heat release rate and total heat release. TGA indicated that OMMT could improve the thermal stability of the PP/PN-DOPO blends and promote the char residues of PP systems. Rheological behaviour showed a higher storage modulus, loss modulus and complex viscosity of PP/PN-DOPO/OMMT composites, suggesting a more effective network structure. In addition, the tensile strength, flexural properties and impact strength of the PP/PN-DOPO/OMMT composites actually increased for a good dispersion effect. Combined with the char layer analysis, the introduction of OMMT promoted more continuous and compact structural layers containing an aluminium-silicon barrier and phosphorus-containing carbonaceous char in the condensed phase. OMMT can improve the flame retardancy, thermal stability and mechanical properties of PP, and, thus, PN-DOPO/OMMT blends can serve as an efficient synergistic system for flame-retarded PP composites.

Facile Preparation of Chitosan-Based Composite Film with Good Mechanical Strength and Flame Retardancy

To improve on the poor strength and flame retardancy of a chitosan (CS)-based functional film, cellulose nanofiber (CNF) was taken as the reinforced material and both ammonium polyphosphate (APP) and branched polyethyleneimine (BPEI) as the flame-retardant additives in the CS matrix to prepare the CS/CNF/APP/BPEI composite film by simple drying. The resulting composite film showed good mechanical strength, with a tensile strength reaching 71.84 Mpa due to the high flexibility of CNF and the combination of CS, CNF and BPEI through strong hydrogen bonding interactions. The flame retardant-performance of the composite film greatly enhanced the limit oxygen index (LOI), up to 32.7% from 27.6% for the pure film, and the PHRR intensity decreased to 28.87 W/g from 39.38% in the micro-scale combustion calorimetry (MCC) test due to the ability of BPEI to stimulate the decomposition of APP, releasing non-flammable gases such as CO₂, N₂, NH₃, etc., and forming a protective phosphating layer to block the entry of O₂. Based on the good flame retardancy, mechanical strength and transparency, the CS/CNF/APP/BPEI composite film has a great potential for future applications.

Synergistic Flame-Retardant Effect of Aluminum Diethyl Phosphinate in PP/IFR System and the Flame-Retardant Mechanism

Synergistic flame-retardant effect of aluminum diethyl phosphinate (AlPi) in intumescent flame retardant polypropylene (PP/IFR) system and the flame-retardant mechanism were investigated. The flame retardancy of PP/IFR/AlPi (the mass ratio of IFR to AlPi is 2 : 1) was the best, which was proved by the results of the limiting oxygen index (LOI) test, UL-94 test, and cone calorimeter test ( CCT) test. Here, the LOI value of the sample was as high as 34% and passed the V–0 rating in UL–94 test. The peak heat release rate (PHRR) decreased by 92.57%, the total heat release (THR) reduced by 90.52%. Thermogravimetric (TGA) data showed that the introduction of AlPi improved thermal stability and changed the thermal degradation behavior of PP/IFR composites. Interestingly, scanning electron microscopy (SEM), energy-dispersive X-ray spectroscopy (EDXS) and laser Raman spectroscopy (LRS) proved that PP/IFR/AlPi had formed more residual carbon, but the flame retardancy was worse than PP/IFR/AlPi. This is because when the mass ratio of IFR to AlPi is 2 : 1, the synergy between IFR and AlPi was significant, gas-phase flame retardant and condensed-phase flame retardant reached a balance and obtained the best flame retardant effect.