Poly(vinyl amine) microparticles derived from N-Vinylformamide and their versatile use

Control over Charge Density by Tuning the Polyelectrolyte Type and Monomer Ratio in Saloplastic-Based Ion-Exchange Membranes

Membranes based on polyelectrolyte complexes (PECs) can now be prepared through several sustainable, organic solvent-free approaches. A recently developed approach allows PECs made by stoichiometric mixing of polyelectrolytes to be hot-pressed into dense saloplastics, which then function as ion-exchange membranes. An important advantage of PECs is that tuning their properties can provide significant control over the properties of the fabricated materials, and thus over their separation properties. This work studies the effects of two key parameters─(a) ratio of mixing and (b) choice of polyelectrolytes─on the mechanical, material, and separation properties of their corresponding hot-pressed saloplastic-based ion-exchange membranes. By varying these two main parameters, charge density─the key property of any IEM─was found to be controllable. While studying several systems, including strong/strong, strong/weak, and weak/weak combinations of polyelectrolytes, it was observed that not all systems could be processed into saloplastic membranes. For the processable systems, expected trends were observed where a higher excess of one polyelectrolyte would lead to a more charged system, resulting in higher water uptake and better permselectivities. An anomaly was the polystyrenesulfonate-polyvinylamine system, which showed an opposite trend with a higher polycation ratio, leading to a more negative charge. Overall, we have found that it is possible to successfully fabricate saloplastic-based anion- and cation-exchange membranes with tunable charge densities through careful choice of polyelectrolyte combination and ratio of mixing.

Fluorescent melamine-formaldehyde/polyamine coatings for microcapsules enabling their tracking in composites

This study aimed the development of fluorescent melamine-formaldehyde (MF)/polyamine coatings for labelling of prefabricated microcapsules and their tracking in composites. The composition of the fluorescent MF coatings was studied by FTIR spectroscopy, thermogravimetric analysis, and elemental analysis. The characteristics of the coatings and its deposition on different surfaces were investigated using optical and fluorescence microscopy and fluorescence spectroscopy. MF prepolymers were polymerised with tri- and polyamines yielding in fluorescent coatings without addition of fluorescent dyes. Both, MF/poly(ethylene imine) and MF/poly(vinyl amine) (PVAm) coated glass beads showed maximum fluorescence at an excitation wavelength of λmax = 360 nm with the emission maxima at λmax = 490 nm and λmax = 410 nm, correspondingly. The MF/PVAm polymer was coated on diuron-poly(methyl methacrylate) microcapsules and tracked in highly filled composites (water-based plaster/paint) to show its applicability. MF/polyamine coatings were identified as promising materials for the fluorescent labelling of prefabricated microcapsules.

Preparation and Characterization of Thermoresponsive Poly(N-vinylisobutyramide) Microgels

Microgels are soft, adaptive materials exhibiting various properties not only like hydrogels and microparticles but also like macromolecules, colloids, and surfactants. To widen the range of their biomedical and environmental applications, the exploration of an alternative for poly(N-alkylacrylamide)s without potential safety risks is of great importance. In this article, thermoresponsive poly(N-vinylisobutyramide) (PNVIBA) microgels of uniform size were synthesized with NVIBA as a monomer and N,N'-5-oxanonamethyene-bis-N-vinylacetamide as a cross-linker in the presence of sodium dodecyl sulfate by aqueous free radical precipitation polymerization. The introduction of cationic groups into PNVIBA microgels was also accomplished using N-vinylformamide (NVF) as a comonomer and the subsequent conversion of NVF into vinylamine by hydrolysis.