An eco-friendly facile approach for imparting multifunctional protection properties to cellulose/wool blends

Nano-scaled polyacrylonitrile for industrialization of nanofibers with photoluminescence and microbicide performance

Nanofibers are investigated to be superiorly applicable in different purposes such as drug delivery systems, air filters, wound dressing, water filters, and tissue engineering. Herein, polyacrylonitrile (PAN) is thermally treated for autocatalytic cyclization, to give optically active PAN-nanopolymer, which is subsequently applicable for preparation of nanofibers through solution blow spinning. Whereas, solution blow spinning is identified as a process for production of nanofibers characterized with high porosity and large surface area from a minimum amounts of polymer solution. The as-prepared nanofibers were shown with excellent photoluminescence and microbicide performance. According to rheological properties, to obtain spinnable PAN-nanopolymer, PAN (12.5-15% wt/vol, honey like solution, 678-834 mPa s), thermal treatment for 2-4 h must be performed, whereas, time prolongation resulted in PAN-nanopolymer gelling or rubbering. Size distribution of PAN-nanopolymer (12.5% wt/vol) is estimated (68.8 ± 22.2 nm), to reflect its compatibility for the production of carbon nanofibers with size distribution of 300-400 nm. Spectral mapping data for the photoluminescent emission showed that, PAN-nanopolymer were exhibited with two intense peaks at 498 nm and 545 nm, to affirm their superiority for production of fluorescent nanofibers. The microbial reduction % was estimated for carbon nanofibers prepared from PAN-nanopolymer (12.5% wt/vol) to be 61.5%, 71.4% and 81.9%, against S. aureus, E. coli and C. albicans, respectively. So, the prepared florescent carbon nanofibers can be potentially applicable in anti-infective therapy.

In Situ Synthesis of Copper Nanoparticles on Dielectric Barrier Discharge Plasma-Treated Polyester Fabrics at Different Reaction pHs

Polyester (PET) fabrics are widely applied in functional textiles due to their outstanding properties such as high strength, dimensional stability, high melting point, low cost, recyclability, and flexibility. Nevertheless, the lack of polar groups in the PET structure makes its coloration and functionalization difficult. The present work reports the one-step in situ synthesis of copper nanoparticles (CuNPs) onto the PET fabric employing sodium hypophosphate and ascorbic acid as reducing and stabilizing agents, at acidic (pH 2) and alkaline pH (pH 11). This synthesis (i) used safer reagents when compared with traditional chemicals for CuNP production, (ii) was performed at a moderate temperature (85 °C), and (iii) used no protective inert gas. The dielectric barrier discharge (DBD) plasma was used as an environmentally friendly method for the surface functionalization of PET to enhance the adhesion of CuNPs. The size of the CuNPs in an alkaline reaction (76-156 nm for not treated and 93.4-123 nm for DBD plasma-treated samples) was found to be smaller than their size in acidic media (118-310 nm for not treated and 249-500 nm for DBD plasma-treated samples), where the DBD plasma treatment promoted some agglomeration. In acidic medium, metallic copper was obtained, and a reddish color became noticeable in the textile. In alkaline medium, copper(I) oxide (Cu₂O) was detected, and the PET samples exhibited a yellow color. The PET samples with CuNPs presented improved ultraviolet protection factor values. Finally, a minimal concentration of copper salt was studied to obtain the optimized antibacterial effect against Staphylococcus aureus and Escherichia coli. The functionalized samples showed strong antibacterial efficacy using low-concentration solutions in the in situ synthesis (2.0 mM of copper salt) and even after five washing cycles. The DBD plasma treatment improved the antibacterial action of the samples prepared in the alkaline medium.