Modelling the surface free energy parameters of polyurethane coats-part 2. Waterborne coats obtained from cationomer polyurethanes

Polyurethane cationomers containing fluorinated soft segments with hydrophobic properties

The synthesis of ecological waterborne polyurethane cationomers containing fluorinated polyol (0–20 wt.%) was successfully performed. FTIR and NMR analysis results confirmed the structure of the obtained polyurethane cationomers and incorporation of fluorinated component into the polyurethane chains. Average molar mass and phase structure of the obtained PU thin films were determined based on GPC, FTIR, WAXD and SEM-EDX results. The obtained cationomers have linear structures with clearly visible microphase separation of soft and hard segment domains; the presence of fluorinated polyol changes the strength of hydrogen bonds and in consequence degree of phase separation. The activation energy of glass transition was calculated based on multi-frequency DSC data. It has been shown that the presence of soft fluorinated segments in the cationomer structure strongly influences the hydrophobic, thermal and mechanical properties of the obtained films.

Composites prepared from the waterborne polyurethane cationomers-modified graphene. Part I. Synthesis, structure, and physicochemical properties

In the reaction of 4,4′-methylenebis(phenyl isocyanate), polycaprolactone diol, and N-methyldiethanolamine, they were synthesized aqueous dispersions of polyurethane cationomers, from which films were prepared after adding 0–2 wt% graphene. In order to obtain nanocomposites, graphene was previously noncovalent functionalized in tetrahydrofurane in the field of ultrasound. The chemical structure and the morphology of obtained nanocomposites were analyzed by IR spectroscopy, atomic force microscopy (AFM), and differential scanning calorimetry (DSC) microcalorimetry methods. It was found that the presence of graphene results in increased thermal and mechanical strength of received polymer films and contributes to the increase in hydrophobicity of generally hydrophilic coatings prepared from waterborne polyurethane cationomers. Based on received results, possible interactions between graphene and phase structure of polyurethane cationomers were discussed. Relating to the so far described applications of graphene for the modification of polyurethanes, the novelty of this work is the concept of incorporation of graphene particles to polyurethane cationomer chains exclusively through a simple noncovalent functionalization and to investigate the effect of graphene on the properties obtained in this way of thin polyurethane film.