Mechanochemical synthesis of chloroapatite and its characterization by powder X-ray diffractometory and attenuated total reflection-infrared spectroscopy

Mechanochemical synthesis of cerium chlorapatite from a mixture of cerium chloride heptahydrate, dicalcium phosphate dihydrate, and calcium hydroxide for biomedical application

BACKGROUND

Cerium ions promote osteoclastogenesis and activate bone metabolism, while cerium oxide nanoparticles exhibit potent anti-inflammatory properties, making them promising for biomedical applications.

OBJECTIVE

The purpose of this study was to develop and evaluate a synthesis method for sustained-release cerium-ion bioceramics containing apatite. Substituted apatite was found to be an effective biomaterial.

METHODS

Cerium-containing chlorapatite was synthesized using a mechanochemical method employing dicalcium phosphate, cerium chloride heptahydrate, and calcium hydroxide as raw materials. The synthesized samples were characterized using X-ray diffraction (XRD), Fourier transform infrared (FTIR) spectroscopy, scanning electron microscopy, energy-dispersive X-ray spectroscopy, and Raman spectroscopy.

RESULTS

Cerium chlorapatite was successfully synthesized in the 10.1% and 20.1% samples. However, at Ce concentrations higher than 30.2%, the samples consisted of three or more phases, indicating the instability of a single phase.

CONCLUSION

The method used in this study was found to be more efficient and cost-effective than the precipitation method for producing substituted apatite and calcium phosphate-based biomaterials. This research contributes to the development of sustained-release cerium-ion bioceramics with potential applications in the field of biomedicine.

Chlorapatite Derived From Fish Scales

The present work demonstrates the production of chlorapatite (ClAp) through thermal decomposition of chemically treated fish scales, originating from an Amazon fish species (Arapaima gigas). The scales were treated with hydrochloric acid (HCl) solution for deproteinization. Afterwards, the solution was neutralized by sodium hydroxide (NaOH) treatment to obtain an apatite-rich slurry. The heat treatment was carried out at different temperatures including 600 °C, 800 °C, and 1000 °C. The powders obtained were characterized through X-ray diffraction (XRD), Fourier transform infrared spectroscopy (FTIR), energy-dispersive X-ray spectroscopy (EDS), and scanning electron microscopy (SEM). The XRD analysis and FTIR spectra confirmed the incorporation of chlorine into the apatite structure. The FTIR results showed absorption bands relative to the OH^-, PO₄^3- functional groups which are a characteristic of chlorapatite; moreover, the intensity of the OH-Cl elongation could be observed. Chlorapatite Ca₅(PO₄)₃Cl, NaCl, and NaCaPO₄ phases were identified, achieving up to 87.4 wt% for ClAp. From the SEM observations, the ClAp obtained consisted of slightly larger grains and more crystalline with increasing temperature with observed grains ranging in sizes between 1 and 5 μm and 84.27% crystallinity for the ClAp1000 sample. The ClAp and NaCaPO₄ can be used in electronics as a phosphor material due to the fact of its luminescence and biomedical applications.