Influence of non-rubber components on film formation behavior of natural rubber latex

Rapid formation of carbon nanotubes-natural rubber films cured with glutaraldehyde for reducing percolation threshold concentration

Carbon nanotubes (CNTs) filled natural rubber (NR) composites with various CNT contents at 0, 1, 2, 3, 4 and 5 phr were prepared by latex mixing method using glutaraldehyde as curing agent. This work aims to improve the electrical and mechanical properties of CNT filled NR vulcanizates. The CNT dispersion of NR composites was clarified using dispersion grader, optical microscopy and scanning electron microscopy. The electrical properties of NR composites in the existing of CNT networks were studied by following the well-known percolation theory. It was observed that the NR composites exhibited low percolation threshold at 0.98 phr of CNT. Moreover, a three-dimensional network formation of CNT in the NR composites was observed and it is indicated by the t-value of 1.67. The mechanical properties of NR composites in terms of modulus, tensile strength and hardness properties were increased upon the addition of CNT to the optimum mechanical properties at 1 phr of CNT. Therefore, the present work is found the novelty of the study that the conductive rubber latex film can be produced using GA as low-temperature curing agent which enhanced good electrical properties. Moreover, this work is found to be beneficial in case of conductive rubber latex film that requires high modulus at low strain. The additional advantage of this system is the curing process occurs at low-temperature using GA and it can be easily processed.

The Interplay of Protein Hydrolysis and Ammonia in the Stability of Hevea Rubber Latex during Storage

Natural rubber (NR) latex derived from Hevea brasiliensis is a complex colloid comprising mainly rubber hydrocarbons (latex particles) and a multitude of minor non-rubber constituents such as non-rubber particles, proteins, lipids, carbohydrates, and soluble organic and inorganic substances. NR latex is susceptible to enzymatic attack after it leaves the trees. It is usually preserved with ammonia and, to a lesser extent, with other preservatives to enhance its colloidal stability during storage. Despite numerous studies in the literature on the influence of rubber proteins on NR latex stability, issues regarding the effect of protein hydrolysis in the presence of ammonia on latex stability during storage are still far from resolved. The present work aims to elucidate the interplay between protein hydrolysis and ammoniation in NR latex stability. Both high- and low-ammonia (with a secondary preservative) NR latexes were used to monitor the changes in their protein compositions during storage. High-ammonia (FNR-A) latex preserved with 0.6% (v/v) ammonia, a low 0.1% ammonia/TMTD/ZnO (FNR-TZ) latex, and a deproteinized NR (PDNR) latex were labeled with fluorescence agents and observed using confocal laser scanning microscopy to determine their protein composition. Protein hydrolysis was confirmed via sodium dodecyl sulfate-polyacrylamide gel electrophoresis (SDS-PAGE). The results revealed that protein hydrolysis increased with the storage duration. The change in protein composition accompanying hydrolysis also allows the spatial distribution of allergenic proteins to be estimated in the latex. Concurrently, the latex stability increased with the storage duration, as measured by the latex's mechanical stability time (MST) and the zeta potential of the latex particles. As monitored by AFM, the surface roughness of the NR latex film increased markedly during extended storage compared with that of the DPNR latex, which remained smooth. These results underscore the pivotal role of ammonia in bolstering NR latex stability brought on by protein hydrolysis, which greatly impacts latex film's formation behavior. NR latex stability underpins the quality of latex-dipped goods during manufacturing, particularly those for medical gloves.

Impact of N,N ′ -Methylene-bis-Morpholine on the Preservation of Natural Rubber Latex

Natural rubber latex (NRL) preserved by high ammonia (HA) presents substantial pollution issues despite its good all-around properties. Cleaning preservation of NRL is critical in the modern rubber industry. In this study, NRL was preserved using N,N $\prime$ -methylene-bis-morpholine (MBM), and the impact of MBM on the preservation and characteristics of NRL was investigated. The results showed that when the MBM dose was greater than 0.15 wt%, the volatile fatty acid value (VFA No.) and viscosity value of fresh NRL were lower, and it could be stored for longer than 5 days without losing stability. Furthermore, MBM demonstrated a favorable preservation effect on concentrated NRL (CNRL). To be effective, MBM must be administered at a dosage greater than 0.3 wt%. The mechanical stability test (MST) and VFA No. of the low-ammonia (LA)-CNRL prepared by MBM combined with ammonia were somewhat lower, whereas the viscosity value was greater. The research showed that the dose of lauric acid soap needs to be increased to improve the stability of ultra-LA-CNRL made by MBM–ammonia composite preservation. After pre-vulcanization treatment, the stability of LA-CNRL preserved by MBM–ammonia composite was drastically reduced. As the stabilizer dose was increased, the CNRL viscosity value decreased, whereas the MST and heat stability improved. The LA-CNRL vulcanized film has excellent mechanical properties similar to HA-CNRL. Furthermore, the infrared spectrum of the LA-CNRL raw rubber film was similar to that of the HA-CNRL film. The thermal degradation curve and characteristic temperature were also similar to that of the HA film. The study indicates that MBM has an outstanding preservation effect on fresh NRL and LA-CNRL, and the findings constitute a significant step forward in the development of the CNRL sector.

The role of natural rubber endogenous proteins in promoting the formation of vulcanization networks

Non-rubber components are critical in the formation of the natural rubber (NR) vulcanization network, which leads to outstanding mechanical properties of NR. This study reports the effect of NR endogenous proteins (C-serum protein/lutoid protein [CSP/LP]) on the formation of vulcanization networks at the molecular level. Results indicate that CSP/LP has a positive effect on vulcanization. Fourier-transform infrared spectroscopy and X-ray photoelectron spectroscopy analyses demonstrate that the decrease in vulcanization time of CSP/LP is ascribed to coordination interaction between Zn2+ and amide bond. The interaction increases the availability of ZnO in the matrix, thereby promoting the formation of the vulcanized network. CSP/LP also participates in the construction of the vulcanization network as a new crosslinking point, thus increasing crosslinking density and improving the mechanical properties of the NR. This study provides new research ideas for studying the relationship among component–structure–property of NR materials and developing high-strength and high-toughness elastomer materials.