Molecularly imprinted titania microbeads for extraction of the metabolite 1-hydroxypyrene from urine prior to its determination by HPLC

Porous cage-like hollow magnetic carbon-doped CoO nanocomposite as an advanced sorbent for magnetic solid-phase extraction of nine polycyclic aromatic hydrocarbons

In this study, porous cage-like hollow magnetic carbon-doped CoO nanocomposite (CoO@C) was successfully synthesized using a metal-organic frameworks (MOFs) as precursor by one-step calcination method in this work. The obtained nanoporous composite showed excellent magnetic response by taking advantage of the magnetism of CoO even without the Fe₃O₄, making it an advanced sorbent for magnetic solid-phase extraction (MSPE). The Co-MOF and CoO@C were characterized by XRD, TGA, SEM, TEM, vibrating sample magnetometry, and FT-IR spectroscopy. Based on this, a method using CoO@C for MSPE coupled with HPLC was established for the analysis of nine polycyclic aromatic hydrocarbons (PAHs) from various real water samples. The amount of sorbent, extraction times, extraction temperature, desorption times, oscillation rate, and elution volume were optimized. Under the optimal conditions, the method had good relative standard deviations (RSDs) of 1.1%-6.5% and a satisfying linearity range of 0.5-1000 μg L^-1. The low LOD and LOQ for nine PAHs were found to be 0.06-1.30 μg L^-1 and 0.19-4.30 μg L^-1, respectively. The experimental results indicated that the prepared nanocomposite showed excellent adsorption capacity compared to other commercial sorbents and has potential applications for the removal of hazardous pollutants from environmental samples.

Design of a pseudo stir bar sorptive extraction using graphenized pencil lead as the base of the molecularly imprinted polymer for extraction of nabumetone

Molecularly imprinted polymer (MIP) was synthesized through the coprecipitation method on the graphene oxide anchored pencil lead as a substrate for the first time and applied as an efficient sorbent for pseudo stir bar sorptive extraction of nabumetone. The extracted analyte was determined by a novel spectrophotometric method based on the aggregation of silicate sol-gel stabilized silver nanoparticles in the presence of the analyte. The synthesized polymer was characterized using Fourier transform infrared spectroscopy and field emission scanning electron microscopy. Optimization of important parameters affecting the extraction efficiency was done using central composite design whereas the spectrophotometric method was optimized via one at a time variable. Under the optimal conditions, the calibration curve exhibited linearity in the concentration range of 1.5-20.0 μg L^-1. A limit of detection of 0.20 μg L^-1, an enhancement factor of 393 and relative standard deviations (at 10 μg L^-1, n = 6) of 4.6% and 8.1% for intra- and inter-day analysis were obtained. The developed procedure was successfully utilized for the quantification of traces of nabumetone in tap water and biological samples with the complex matrix including human urine and serum.

A molecularly imprinted polymer undergoing a color change depending on the concentration of bisphenol A

A molecularly imprinted system is introduced here whose color gradually changes as the analyte becomes rebound. The MIP was prepared from an acryloyl-modified β-cyclodextrin (β-CD), acrylamide (AAm), and N,N'-methylenebisacrylamide (MBAA), and imprinted with bisphenol A (BPA). The sensing capability of the MIP was first tested by potentiometry. A spin-coated gold plate coated with the MIP was used as a working electrode; the electrode can differentiate BPA from phenol or p-cresol, which were used as analogs of BPA. Next, a color-responsive system was fabricated by forming a hydrogel membrane containing the modified β-CD, AAm, and MBAA. A vesicle solution was prepared from N-(2-aminoethyl)pentacosa-10,12-diynamide by sonication and incorporated into the hydrogel. The blue polydiacetylene was formed by UV photopolymerization. In the presence of BPA, this system undergoes a color change from blue to red that is proportional to the degree of BPA rebinding. The color change is due to the contraction of the gel membrane that rebinding causes. The method works to 0.5 mM BPA concentration range. The detection limits for BPA are 0.1 mM on visual assessment and 50 μM on spectrophotometric readout. Graphical AbstractA molecular imprinting system is described whose color changes from blue to red as it binds bisphenol A. The degree of rebinding can be measured by detecting the color change of polydiacetylene vesicle. CD: cyclodextrin, BPA: bisphenol A.