Influence of ascorbic acid on bonding of peroxide-affected dentin and 4-META/MMA-TBB resin

Use of antioxidants to restore bond strength after tooth bleaching with peroxides

This review compiles the literature on the antioxidants used after tooth bleaching with either low or high-concentrated carbamide and hydrogen peroxide to recover the bond strength. Antioxidants used in bleached teeth are mainly natural and non-enzymatic, except for catalase. Commonly, antioxidants are applied to remove any reactive oxygen species (ROS) residues left from bleaching gels, which adversely affect adhesive procedures, such as restorations or orthodontic brackets bonding. Even though sodium ascorbate, the most thoroughly investigated antioxidant, showed the most efficient bond strength recovery at 10% concentration, its performance depends on the type of solution and the application time. Natural extracts, such as proanthocyanidins and green tea, showed satisfactory results in the reversal of bond strength at 5% and 10% concentrations, respectively. Sodium ascorbyl phosphate, α-tocopherol, and catalase exhibited promising results, but further research is required. The adhesive system type plays an important role in the outcome of enamel bond strength after the antioxidant application. The postponement of either restorations or orthodontic brackets cementation following bleaching procedures seems to be efficiently replaced by antioxidant application prior to bonding procedures. However, the efficacy of using an antioxidant to recover bond strength depends on its type and application time.

Effects of calcium hydroxide reagent on the bond strength of resin cements to root dentin and the retention force of FRC posts

The aim of this study was to determine the effects of calcium hydroxide (Ca(OH)₂) treatment on bond strength of resin cements to root dentin and retention force of fiber-reinforced composite (FRC) posts. Bovine root dentin was endodontically prepared and treated with Ca(OH)₂ for 7 days. Root dentin for bond strength test was adhered to resin-composite with resin cements. For pull-out test, posts consisting of FRC posts and resin-composites were fabricated and cemented to root. Shear bond and pull-out tests were performed using a universal testing machine. No significant differences in bond strength and post retention force were found between Ca(OH)₂ treated and untreated groups. Significant differences were found among the cements. A positive correlation was indicated between bond strength of cements and retention force of FRC posts. In conclusion, Ca(OH)₂ treatment on root dentin did not affect bond strength of resin cements and retention force of FRC posts.

Resin Bonding of Self-Etch Adhesives to Bovine Dentin Bleached from Pulp Chamber

This study evaluated the microtensile bond strength (μTBS) of 1-step self-etch adhesives (1-SEAs) and 2-step self-etch adhesives (2-SEAs) to pulp chamber dentin immediately after bleaching with 2 types of common bleaching techniques. Pulp chamber dentin of bovine teeth was bleached using 30% hydrogen peroxide (H₂O₂) solution with quartz-tungsten-halogen light-curing unit (Group 1) and 3.5% H₂O₂-containing titanium dioxide (TiO₂) (Pyrenees®) activated with 405-nm violet diode laser for 15 min (Group 2). Unbleached specimens were placed in distilled water for 15 min and used as controls. After treatment, dentin was bonded with resin composite using 1-SEA or 2-SEA and stored in water at 37°C for 24 h. Each specimen was sectioned and trimmed to an hourglass-shape and μTBS was measured. Fractured specimens were examined under a scanning electron microscope to determine fracture modes. All specimens in Group 1 failed before proper bonding tests. In Group 2, the μTBS of 2-SEA was significantly greater (with no failed specimens) than 1-SEA (where 21 out of 36 failed). These results indicate that 2-SEA is a better adhesive system than 1-SEA on bleached dentin. Our results also demonstrated that application of H₂O₂ significantly decreases bond strength of resin to dentin; however, in the case of nonvital tooth bleaching, Pyrenees® is a better alternative to the conventional 30% H₂O₂ bleaching.

Effect of fluoridated carbamide peroxide gels on enamel microtensile bond strength

The aim of this study was to examine the resin bond strength on enamel treated with different fluoridated bleaching agents. Forty-eight bovine incisors were divided into four groups to receive bleaching treatments, over a 14-d period, as follows: no treatment; 10% carbamide peroxide (CP) bleaching; 10% CP containing 0.11% fluoride; and 10% CP containing 0.37% fluoride. Immediately, and 7 and 14 d after bleaching, the enamel surfaces were respectively bonded with composite and sectioned to create resin-enamel beams. These beams were subjected to the microtensile bond strength (microTBS) test, then assessed for failure mode under scanning electron microscopy. The results showed that the 0.37% fluoridated group demonstrated a microTBS equivalent to that of the unbleached group at all stages. Non-fluoridated and 0.11% fluoridated groups showed a weaker microTBS after bleaching but regained the bond strength after 14 or 7 d of storage, respectively. In the non-fluoridated group, adhesive failure was the predominant fracture pattern that comprised the enamel prism demineralization change and widely dispersed voids on the resin-enamel interfaces. No evident enamel erosion and fewer microporosities were found in the 0.37% fluoridated group. Accordingly, treatment with 0.37% fluoridated CP maintained the microTBS as effectively as the unbleached enamel. Additional fluoride in the bleaching agents may facilitate subsequent restorative treatment by inhibiting enamel demineralization.