Surface characterization of passive film and elemental release analysis of a Ni–Cr alloy during bleaching, part I: effects of different bleaching agents

Effects of disinfection with a vinegar-hydrogen peroxide mixture on the surface composition and topography of a cobalt-chromium alloy

STATEMENT OF PROBLEM

Choosing the best disinfection agent for removable partial dentures may be challenging since most commercially available disinfection solutions alter the properties of the metal framework.

PURPOSE

The purpose of this in vitro study was to analyze the changes in the surface topography and elemental composition of a cobalt-chromium (Co-Cr) alloy when immersed in a vinegar-hydrogen peroxide mixture.

MATERIAL AND METHODS

Disk-shaped specimens (N=50) were fabricated with Co-Cr alloy and randomly distributed into 5 groups (N=10) according to the immersion solutions: distilled water (control) (W); 0.5% sodium hypochlorite (H); 3% hydrogen peroxide and water in a 1:1 ratio (HP); vinegar and water in a 1:1 ratio (V); and vinegar and 3% hydrogen peroxide mixture in a 1:1 ratio (VHP). The immersions simulated 90 uses of 10 minutes each. The surface topography and the elemental composition were analyzed with scanning electron microscopy and energy-dispersive spectroscopy, before (T0) and after (T1) the immersions. The 2-way ANOVA for repeated measures was used for statistical comparisons (α=.05).

RESULTS

The tested mixture (VHP) did not change the metal surface topography or increase the oxygen proportion, indicating that no corrosion occurred. Similarly, groups W, HP, and V had no topographic changes and nonsignificant statistical differences at T1 for elemental composition (P>.05). However, the specimens immersed in sodium hypochlorite (H) showed staining, surface irregularity, composition change, with an appearance of 22.56% more oxygen, 41% less chromium, and 28.77% less cobalt at T1 (P<.05).

CONCLUSIONS

The immersion of Co-Cr alloy in a vinegar-hydrogen peroxide mixture did not change the surface structure of the metal.

Effect of a vinegar-hydrogen peroxide mixture on the surface properties of a cobalt-chromium alloy: A possible disinfectant for removable partial dentures

STATEMENT OF PROBLEM

A vinegar-hydrogen peroxide mixture has been reported to be effective in eliminating Candida albicans and Staphylococcus aureus from acrylic resin, and its action has been reported to be comparable with that of sodium hypochlorite or peracetic acid. However, the effects of this mixture on cobalt-chromium alloys remain unknown.

PURPOSE

The purpose of this in vitro study was to evaluate the surface roughness, Knoop microhardness, surface free energy, and wettability of a cobalt-chromium alloy when exposed to a vinegar-hydrogen peroxide mixture.

MATERIAL AND METHODS

Fifty specimens of cobalt-chromium alloy were fabricated and immersed for 900 minutes, simulating 3 months of a daily 10-minute immersion in the following chemical agents (n=10): distilled water (W); 0.5% sodium hypochlorite (H); 3% hydrogen peroxide and water dilution in 1:1 ratio (HP); white-wine vinegar and water dilution in 1:1 ratio (V); and vinegar and hydrogen peroxide mixture in 1:1 ratio (VHP). Surface roughness, Knoop microhardness, surface free energy, and wettability were measured with single blinding before and after immersions. Data were statistically analyzed by using 2-way repeated measures ANOVA (α=.05).

RESULTS

The vinegar-hydrogen peroxide mixture did not affect the surface roughness or Knoop microhardness. However, 0.5% sodium hypochlorite significantly increased the roughness and decreased microhardness. Surface free energy and wettability increased after immersions, regardless of the types of solution.

CONCLUSIONS

Immersion in a vinegar-hydrogen peroxide mixture did not affect the surface characteristics of a cobalt-chromium alloy.

The Effect of Porcelain Firing on Electrochemical Behavior of a Dental Alloy in Hydrogen Peroxide

PURPOSE

The aim of this study was to evaluate changes in electrochemical corrosion properties of porcelain firing simulated nickel-chromium dental casting alloy exposed to a 10% hydrogen peroxide bleaching agent.

MATERIALS AND METHODS

The electrochemical corrosion behavior of a Ni-Cr alloy was evaluated by cyclic polarization test in the aerated electrolyte (pH = 6.5). Test groups were produced in as-cast (group 1, control group) and simulated porcelain firing (group 2: heat-treated/mean value; group 3: heat-treated/cycle) conditions. Scanning electron microscopy (SEM) was also used to examine the alloy surfaces before and after the corrosion test.

RESULTS

The ranking of the groups with respect to Ecorr and Icorr was as follows: 1, 2, 3 and 3, 1, 2, respectively. Group 3 exhibited the greatest and group 2 displayed the least corrosion tendencies. An increase in corrosion rates was observed after heat treatment/cycle state. Post-corrosion SEM photographs were also consistent with the test results.

CONCLUSION

Within the parameters of this study, a single heat treatment is insufficient to cause upheaval in corrosion behavior of a Ni-Cr alloy subjected to 10% hydrogen peroxide.

Electrochemical corrosion and surface analyses of a ni-cr alloy in bleaching agents

PURPOSE

The aim of this study was to evaluate the corrosion behavior of a Ni-Cr dental casting alloy subjected to 10% hydrogen peroxide (HP) and 10% carbamide peroxide (CP) bleaching solutions and to determine the composition of the surface oxide layer formed on the alloy specimens.

MATERIALS AND METHODS

Ten cylindrical specimens (4 mm in diameter × 25 mm in height) were cast from a Ni-Cr alloy (Wiron 99) and divided into two groups (n = 5). A potentiodynamic polarization test was used to compare the corrosion rates of specimens in HP and CP (pH = 6.5). Before cyclic polarization tests, all alloy specimens were allowed to reach a steady open circuit potential (Ecorr ) for a period of 1 hour. Then tests were initiated at 100 mV versus standard calomel electrode (SCE) below Ecorr and scanned at a rate of 1 mV/s in the anodic direction until reaching 1000 mV over the Ecorr value. The scan then was reversed back to the Ecorr of the specimens. The open circuit potentials (Ecorr ) and the current densities (Icorr ) were determined using the anodic Tafel regions extrapolating from the curves. Differences in Ecorr and Icorr were determined using one-way ANOVA (α = 0.05). In addition, corrosion rates were calculated from these curves. Before and after polarization tests, a scanning electron microscope (SEM) examination accompanied by energy dispersive X-ray spectroscopy (EDS) was used to analyze the surface morphology. The surface characterization of the passive film formed on alloy specimens was also performed by using X-ray photoelectron spectroscopy (XPS).

RESULTS

In this study, bleaching agents had an effect on the anodic process for two groups. Although no statistical difference was identified between the groups for both corrosion parameters, results indicated that the effect of CP on the corrosion behavior was less than that of HP. These results agreed with the SEM observations. XPS data showed that oxide layers formed on all groups contained mainly Cr2 O3 , NiO, and MoO3 , and the amounts of oxides formed on CP-treated specimens were higher than HP treated ones. Also, molybdenum rates were increased with CP application compared to HP.

CONCLUSIONS

The comparison of the effects of the two bleaching agents at 10% showed that the alloy suffered less corrosion with CP than HP. This result was also confirmed by the SEM and XPS data. The presence of Mo on the oxide layer affected the oxide layer, leading to lower corrosion rates.