The effect of different pretreatment methods of PMMA-based crowns on the long-term tensile bond strength to dentin abutments

Bond strength between temporary 3D printable resin and conventional resin composite: influence of cleaning methods and air-abrasion parameters

OBJECTIVES

The influence of different cleaning methods, air-abrasion parameters, and aging on shear bond strength (SBS) and tensile bond strength (TBS) of 3D resin luted to composite resin.

MATERIALS AND METHODS

Nine hundred resin substrates were 3D printed (D20II, Rapid Shape) and cleaned with either isopropanol (ISO), butyldiglycol-based solution (BUT), or centrifugation (CEN). After 24-h storage in 37 °C water, specimens were air-abraded (mean particle size 50 µm; n = 60) with either alumina at 0.1 MPa (AL0.1) or 0.4 MPa (AL0.4) and glass pearls at 0.1 MPa (GP0.1) and 0.4 MPa (GP0.4) or conditioned with visio.link (control) and luted with PanaviaV5. Initially (24 h, 37 °C water storage) or after aging (10,000 thermal cycles), SBS and TBS were measured, and fracture types were examined. Surface free energy (SFE) and roughness (Ra) were determined after air-abrasion. Kolmogorov-Smirnov, Kruskal-Wallis H, Mann-Whitney U, chi-square, and partial eta-squared were computed.

RESULTS

SBS measurements presented higher values than TBS (p < 0.001-0.033). Within the pretreatment groups, CEN showed the highest SBS and TBS values compared to cleaning with ISO or BUT (p < 0.001-0.040). Pretreatment with GP0.1 displayed the lowest bond strength values (p < 0.001-0.049), and mostly adhesive fractures occurred. The highest Ra values (p < 0.001) were observed for AL0.4 pretreatment.

CONCLUSIONS

Pretreatment with AL0.4 and the control group mainly presented the highest bond strength values. Thermocycling had a positive effect on the bond strength.

CLINICAL RELEVANCE

According to this study, 3D-printed restorations should be pretreated with AL0.4 or with visio.link before adhesive luting, regardless of their cleaning.

Bond strength between titanium and polymer-based materials adhesively cemented

The aim was to evaluate the bond strength between titanium and polymer-based materials for prosthetic restorations, cemented with different adhesive cement systems. Eight groups with 13 specimens in each group were included. Each specimen consisted of two parts: a cylinder of titanium resembling a titanium base, and a cylinder of one of two polymer-based materials Micro Filled Hybrid (MFH) or Telio CAD and cemented with one of four adhesive cement systems, namely Multilink Hybrid Abutment, Panavia V5, RelyX Ultimate and G-Cem LinkAce. The titanium was sandblasted with 50 µm Al₂O₃ and treated according to each cement manufacturer's recommendations. The polymer-based materials were pre-treated according to the manufacturer's instructions including sandblasting for MFH. After cementation, the groups were water stored for one day before thermocycling: 5000 cycles in 5–55 °C. A shear bond strength test was performed (crosshead speed 0.5 mm/min) and data was analysed with one-way ANOVA, Tukey's test. Telio CAD cemented with Panavia V5 and G-Cem LinkAce showed significantly lower bond strength compared to all other groups, due to spontaneous debonding. The highest numerical bond strength was found in the group of MFH cemented with RelyX Ultimate or with G-Cem LinkAce. Generally, the Telio CAD groups showed lower bond strength values than the MFH groups. The conclusions are that pre-treatment methods and choice of cement system are of importance for polymer-based materials for prosthetic restorations. The bond strength is adequate for provisional cementation irrespective of cement system when pre-treating by sandblasting, but cement dependent without sandblasting.

Effectiveness of current adhesive systems when bonding to CAD/CAM indirect resin materials: A review of 32 publications

The purpose of this review was to assess the available literature regarding bonding between current adhesive systems and computer-aided design/computer-aided manufacturing (CAD/CAM) indirect resin materials, to provide clinicians with a comparative overview of the relevant bonding procedures. An electronic search was performed through PubMed based on the keywords CAD/CAM and dental bonding. Additional relevant literature was obtained from the citations in the articles. A total of 313 papers were identified, of which 281 were excluded as being unsuitable, and an additional 3 papers were identified, giving a total of 32 articles that are included in this review. Based on this survey, it is recommended that microretentive surfaces should be generated by either blasting or hydrofluoric acid etching. This initial process should be followed by silanization to ensure chemical adhesion prior to bonding to CAD/CAM indirect resin composite materials (including Lava Ultimet, KATANA AVENCIA block, Gradia Block, Cerasmart, Paradigm, and Block HC) and CAD/CAM polymer-infiltrated ceramics (such as Vita Enamic). The use of materials containing methyl methacrylate (MMA) also appears to improve the bonding of CAD/CAM poly(methyl methacrylate) (PMMA) resin materials (including XHIPC-CAD/CAM, artBloc Temp, and Telio).

Load-bearing capacity of novel resin-based fixed dental prosthesis materials

To evaluate the influence of different materials on the load-bearing-capacity of inlay-retained fixed-dental-prosthesis (FDP). Ten types of FDPs were evaluated (n=7/group): Group PEEK: CAD-CAM polyetheretherketone (PEEK-TechnoMed), Group RC, made of discontinuous-fiber-composite (EverX Posterior); Group FRC1, made of discontinuous-fiber-composite (EverX Posterior) with two-bundles of continuous-unidirectional fiber-reinforced-composite (FRC) (Everstick C&B); Group FRC2, made of discontinuous-fiber-composite (EverX Posterior) with two-bundles of continuous-unidirectional-FRC (Everstick C&B) covered by two-pieces of short-unidirectional-FRC (Everstick C&B) placed perpendicular to the main-framework; Group FB, CAD-CAM fiber-block (Fibra-Composite Bio-C); Group PMMA, CAD-CAM polymethyl methacrylate block (Temp basic); Group RP, resin-paste; Group FRP1, made of resin-paste (G-Fix) with two-bundles of continuous-unidirectional-FRC (Everstick C&B); Group FRP2, made of resin-paste (G-Fix) two-bundles of continuous-unidirectional-FRC covered by two-pieces of short unidirectional-FRC placed perpendicular to the main-framework and Group exp-FRC, experimental CAD-CAM FRC. The bridges were statically-loaded until fracture. Fracture modes were visually examined. ANOVA revealed that significant differences were observed between FDP-materials (p<0.05). In addition, fiber addition to the framework significantly affected load-bearing-capacity (p<0.05).

Retention Strength of PMMA/UDMA-Based Crowns Bonded to Dentin: Impact of Different Coupling Agents for Pretreatment

Computer aided design/computer aided manufacturing (CAD/CAM) polymers for long-term dental restorations benefit from enhanced mechanical properties. However, the quantification of their bonding properties on teeth is lacking. Therefore, the aim of this study was to determine the retention strength (RS) of differently pretreated new developed polymethylmethacrylate/urethanedimethacrylate-based CAD/CAM polymer bonded on dentin. In summary, 120 human caries-free molars were prepared, and polymeric crowns were milled and pretreated (n = 20): visio.link (VL), Scotchbond Universal (SU), Monobond Plus/Heliobond (MH), Margin Bond (MB), Margin Bond mixed with acetone (1:1) (MBA) or not pretreated (CG). Half of the specimens were cemented using Variolink II and the other half with RelyX Ultimate. Specimens were stored for 24 h in distilled water and thermal cycled (5000 ×, 5 °C/55 °C). The retention load was measured and failure types were defined. RS was calculated and analyzed using both two- and one-way ANOVA with a post-hoc Scheffé-test, unpaired t-test, Kaplan–Meier with Breslow–Gehan test and chi-squared test (p < 0.05). Crowns bonded using RelyX Ultimate showed higher RS than those bonded using Variolink II. The pretreatment showed no impact on the RS. However, survival analysis within Variolink II found an impact of pretreatment. The median RS for MH was the lowest and statistically different from MB, MBA and CG. For Variolink II MH had the poorest survival as the estimated cumulative failure function of the debonded crown increased very quickly with increasing TBS. Within the RelyX Ultimate groups, no significant differences were determined. The newly developed CAD/CAM polymer showed the highest bonding properties after cementation using RelyX Ultimate.

First clinical experiences with CAD/CAM-fabricated PMMA-based fixed dental prostheses as long-term temporaries

OBJECTIVE

The clinical performance of polymethylmethacrylate (PMMA)-based fixed dental prostheses (FDP) was evaluated in the indication of long-term temporaries.

MATERIALS AND METHODS

In the current indication of the applied machinable PMMA-based material (Vita CAD-Temp), i.e. temporary crowns and FDPs, 27 patients with compromised dentitions (uncertain dental prognosis or postponement of a removable treatment option) were recruited and 45 FDPs (3 or 4 units, 37 terminal-retained, 8 cantilevered) were inserted. Frameworks were computer-aided design (CAD)/computer-aided manufacturing (CAM)-manufactured after conventional impression taking and labside scanning of stone master casts. A resin-modified hybrid cement material (RelyX Unicem) was used for luting in a conventional protocol. Clinical follow-up was performed biannually.

RESULTS

Over an observation time from 2 to 26 months (median 13 months), 11 complications were found in 9 out of 45 PMMA restorations: 4 losses of retention, 5 complete fractures; two of these subsequent to a trepanation for endodontic treatment. Thereby, 3 out of 8 cantilevered FDPs had to be removed within 8 months. Thus, the statistical evaluation included FDPs with abutment at end, only. These standard design FDPs (n = 37) showed a 90.4 % survival rate with a complication-free rate of 88.3 % estimated for an observation time of 16 months.

CONCLUSION

Cantilevered FDPs and reconstructions on abutment teeth with markedly reduced biological prognosis or endodontic intervention yielded a high-failure rate. Terminal-retained FDPs performed clinically well in cases without compromised abutment teeth.

CLINICAL RELEVANCE

PMMA-based material might be used successfully for long-term temporization with 3- to 4-unit FDPs in a standard design over at least one year.