Dentin anti-demineralization potential of surface reaction-type pre-reacted glass-ionomer filler containing self-adhesive resin cement

Effect of borate, fluoride and strontium ions on biomimetic nucleation of calcium phosphate studied using solid-state nuclear magnetic resonance and X-ray diffraction

OBJECTIVES

Apatite minerals can have various anions and cations in their crystal structure in addition to phosphate ion (PO₄³⁻) and calcium ion (Ca2+). The aim of this study is to investigate effects of the borate, fluoride and strontium ions on biomimetic nucleation of calcium phosphate.

METHODS

Nano-crystalline hydroxyapatite (H-Ap) was obtained from a supersaturated buffered solution containing 4.12 mM HPO42- and 5.88 mM Ca2+ (H-Ap). Four additives were used in solid solution methods: (i) 0.588 mM F- (F-Ap), (ii) 5.88 mM Sr2+ (Sr-Ap), (iii) 4.12 mM BO33- (BO3-Ap), and (iv) a surface pre-reacted glass ionomer (S-PRG) filler eluate that contained 0.17 mM Sr2+, 0.588 mM F-, 11.1 mM BO33-- (SPRG-Ap). Apatite crystallization was investigated using a solid-state magic-angle spinning NMR spectroscopy and X-ray diffraction (XRD) with the Rietveld analysis.

RESULTS

A 2D 1H-31P heteronuclear-correlation NMR showed F- ion incorporation in the apatite structure of the F-Ap and SPRG-Ap. The peaks on the 31P axis of the F-Ap, Sr-Ap, and BO3-Ap were different from that of the H-Ap, and the full width at half maximum increased in the following order: H-Ap∼F-Ap∼BO3-Ap< SPRG-Ap< Sr-Ap, suggesting the incorporation of the F-, Sr2+ and BO33-. The incorporation of F and BO3 was further confirmed by 19F and 11B NMR. The XRD revealed that Sr2+ was preferentially incorporated into the CaII site.

SIGNIFICANCE

The F-, Sr2+ and BO33-ions might be involved in modifying the crystallization of apatite precipitation, producing a variety of apatite. S-PRG filler that release these ions may have an effect on remineralization, i.e., the reformation of apatite lost due to caries.

Influence of surface pre-reacted glass-ionomer (S-PRG) filler eluate on collagen morphology, remineralization, and ultimate tensile strength of demineralized dentin

OBJECTIVE

To evaluate the effect of ions released from surface pre-reacted glass-ionomer (S-PRG) filler on collagen morphology, remineralization, and ultimate tensile strength (UTS) of demineralized dentin.

MATERIALS AND METHODS

Bovine incisor root dentins were demineralized with EDTA and divided into three treatment groups: 1) water (control); 2) S-PRG filler eluate; 3) 125 ppm sodium fluoride (NaF). After a 3-min treatment, the specimens were stored in simulated body fluid (SBF) for 3 months. Collagen morphology and remineralization were assessed using transmission electron microscopy (TEM), scanning electron microscopy (SEM), and Fourier-transform infrared spectroscopy (FTIR). Additionally, ultimate tensile strength (UTS) was measured.

RESULTS

TEM and SEM demonstrated that S-PRG induced more effective remineralization compared to NaF, while the control group exhibited faint mineral deposition with collagen degradation. S-PRG displayed the most homogenous mineral deposition in collagen fibrils, along with closure of interfibrillar spaces. Extensive mineral precipitation was observed within dentinal tubules in the S-PRG group. In addition, S-PRG filler eluate demonstrated significantly higher phosphate-to-amide ratio and UTS compared to NaF and control groups (p < 0.05).

CONCLUSIONS

Ion released from S-PRG filler positively influenced collagen morphology, remineralization, and ultimate tensile strength of demineralized dentin.

CLINICAL SIGNIFICANCE

S-PRG filler enhances remineralization and improve the biomechanics of demineralized dentin.

Recent Advances in Direct Adhesive Restoration Resin-Based Dental Materials With Remineralizing Agents

Resin-based dental materials are popular restorative materials especially in direct adhesive restoration because of the excellent mechanical and esthetic properties. Toward the realization of minimally invasive dental procedures, direct composite resin adhesive restoration has become the main treatment for dental defects. In addition, for caries-affected dentin close to the pulp, conservation remineralization has been advocated to save the living pulp. However, the resin–dentin interface can be destabilized by various factors, especially the enzymatic degradation of collagen fibrils within the hybrid layer and polymer hydrolysis. Furthermore, for resin-based restorative materials, the marginal gap remains a major problem that can lead to the occurrence of secondary caries. To address these issues, research efforts have focused on the remineralization of mineral-depleted dental hard tissues using remineralizing bioactive substances. In this review, we first described various bioactive agents with remineralizing properties. Furthermore, we discussed recent advances in resin-based dental materials for enamel or dentin remineralization. Finally, we examined the current challenges and prospects of these emerging materials. This work aims to provide a theoretical foundation for the future development of resin-based dental materials in direct adhesive restoration with remineralizing agents.