Physical and chemical aspects of the interaction of chitosan and cellulose acetate with ions Ca2+ and K+ using DFT methods

Chitosan-based adsorptive membrane modified by carboxymethyl cellulose for heavy metal ion adsorption: Experimental and density functional theory investigations

Low adsorption capacity and weak mechanical stability are the main drawbacks of chitosan (CS)-based adsorptive membranes for heavy metal ion removal. Polyvinyl alcohol (PVA) has been used to improve the mechanical stability of CS membranes, but adsorption capacity is disregarded. In the current study, the surface of the chitosan/polyvinyl alcohol (CP) membrane was modified using carboxymethyl cellulose (CMC) to increase its heavy metal ion adsorption capacity. Experimental and density functional theory (DFT) calculations were used to evaluate the heavy metal ion (As3+ and Cr3+) adsorption capabilities of CP and carboxymethyl cellulose-functionalized CP (CMC-CP) membranes. The batch adsorption process presented a higher heavy metal adsorption capacity of the CMC-CP membrane (As3+/CMC-CP = 234.78 mg/g and Cr3+/CMC-CP = 230.12 mg/g) compared to the CP membrane (As3+/CP = 89.02 mg/g and Cr3+/CP = 75.61 mg/g). The heavy metal/CMC-CP complexes confirmed higher adsorption energies (As3+/CMC-CP = -23.62 kcal/mol and Cr3+/CMC-CP = -23.21 kcal/mol) than the heavy metal/CP complexes (As3+/CP = -3.47 kcal/mol and Cr3+/CP = -2.92 kcal/mol). The electronic band structure was higher for CMC-CP (5.42 eV) compared to CP (4.43 eV). Experimental and theoretical findings were close, implying that the CMC-CP membrane has superior heavy metal adsorption capability than the CP membrane.

N-acylhydrazone Derivative-Loaded Cellulose Acetate Films: Thermoanalytical, Spectroscopic, Mechanical and Morphological Characterization

Cellulose acetate (ACT) is one of the most important cellulose derivatives due to its biodegradability and low toxicity, presenting itself as one of the main substitutes for synthetic materials in the development of wound dressing films. The incorporation of a N-acylhydrazonic derivative (JR19), with its promising anti-inflammatory activity, may represent an alternative for the treatment of skin wounds. This work aims to develop and to physicochemically and mechanically characterize ACT films containing JR19. The films were prepared using the ‘casting’ method and further characterized by thermoanalytical and spectroscopic techniques. In addition, mechanical tests and morphological analysis were performed. Thermogravimetry (TG) and differential scanning calorimetry (DSC) analyses showed that the thermal events attributed to excipients and films were similar, indicating the absence of physical incompatibilities between ACT and JR19. Infrared spectroscopy showed that JR19 was incorporated into ACT films. The characteristic band attributed to C≡N (2279 to 2264 cm⁻¹) was observed in the spectra of JR19, in that of the physical mixture of JR19/ACT, and, to a lesser extent, in the spectra of JR19 incorporated into the ACT film, suggesting some interaction between JR19 and ACT. X-ray diffraction (XRD) evidenced the suppression of the crystallinity of JR19 (diffraction peaks at 8.54°, 12.80°, 14.09°, 16.08°, 18.19°, 22.65°, 23.59°, 24.53°, 25.70°, 28.16° and 30.27°2θ) after incorporation into ACT films. The mechanical tests indicated the adequate integrity of the films and their resistance to bending. The morphological characterization showed JR19 crystals along with a homogeneously distributed porous structure throughout the surface of the films with an average diameter of 21.34 µm and 22.65 µm of the films alone and of those incorporating JR19F, respectively. This study was able to characterize the ACT films incorporating JR19, showing their potential to be further developed as wound healing dressings.