A new SERS-active sandwich structure

Silver nanoparticle-treated filter paper as a highly sensitive surface-enhanced Raman scattering (SERS) substrate for detection of tyrosine in aqueous solution

Highly sensitive SERS substrates based on deposition of silver nanoparticles on commercially available filter paper were prepared in this work, and used to overcome problems found in analyses of aqueous samples. To prepare silver nanoparticle- (AgNP) doped filter substrates, a silver mirror reaction was used. The procedures for substrate preparation were systematically optimized. Pretreatment of filter paper, reaction time, temperature, and concentration of reagents for silver mirror reactions were studied. The morphologies of the resulting substrates were characterized by field-emission scanning electron microscopy (FE-SEM) and correlated with the SERS signals by probing with p-nitrothiophenol (pNTP). Filter papers with different pretreatments were found to have different sizes and distributions of AgNPs. The best performance was found when filter paper was pre-treated with ammonia solution before growth of AgNPs. Based on the SEM images, the resulting AgNPs had roughly spherical shape with a high degree of uniformity. The silver-coated filter paper substrates provide much higher SERS signals compared to glass substrates and the reproducibility was improved significantly. Based on statistical analyses, the relative standard deviations for substrate-to-substrate and spot-to-spot were both were less than 8% and the enhancement factors for the substrates were, in general, higher than 107. The SERS substrates were used to selectively detect tyrosine in aqueous solution. Results indicate that filter-based SERS substrates are highly suited to detection of tyrosine. Compared to glass-based SERS substrates, 50 times more SERS signal was observed in detection of tyrosine. The linear range can be up to 100 μM with a detection limit of 625 nM (SN(-1)=3).

Quantitative surface enhanced Raman scattering detection based on the "sandwich" structure substrate

A sandwich structured substrate was designed for quantitative molecular detection using surface enhanced Raman scattering (SERS), in which the probe molecule was sandwiched between silver nanoparticles (SNPs) and silver nanoarrays. The SNPs was prepared using Lee-Meisel method, and the silver nanoarrays was fabricated on porous anodic aluminum oxide (AAO) using electrodepositing method. The SERS studies show that the sandwich structured substrate exhibits good stability and reproducibility, and the detection sensitivity of Rhodamine 6G (R6G) and Melamine can respectively reach up to 10(-19) M and 10(-9) M, which is improved greatly as compared to other SERS substrates. The improved SERS sensitivity is closely associated with the stronger electromagnetic field enhancement, which stems from localized surface plasmon (LSP) coupling between the two silver nanostructures. Furthermore, the SERS intensity increased almost linearly as the mother concentration increased, which indicates that such a sandwich structure may be used as a good SERS substrate for quantitative analysis.

SERS spectroscopy and SERS imaging of Shewanella oneidensis using silver nanoparticles and nanowires

Facile and reproducible SERS signals from Shewanella oneidensis were obtained utilizing silver nanoparticles (AgNPs) and silver nanowires (AgNWs). Additionally, SERS images identify the distribution of SERS hot-spots. One important observation is the synergistically enhanced SERS signal when AgNPs and AgNWs are used in conjunction, due to constructively enhanced electromagnetic field.

Influences of composition on electroless deposition of silver nanoparticles on glass substrates for surface-enhanced Raman scattering measurements

A silver-mirror reaction was used to prepare active substrates for surface-enhanced Raman scattering (SERS). Glass plates were surface treated with a thin layer of silver nanoparticles (Ag-NPs). The factors influencing the performance of the SERS substrates were systematically studied. Factors included concentrations, species of complexing agents, and reducing agents. p-Nitrothiophenol (pNTP) was used to test the surfaces with Ag-NPs, with the observed signals used to compare the performance resulting from different reducing and complexing agents. The morphologies of the Ag-NPs formed by different reaction conditions were also examined by scanning electron microscope (SEM) and correlated with the SERS signals. Reducing agents included formaldehyde, sodium tartrate, and several carbohydrates. The results indicate that the use of glucose as a reducing agent produced the most suitable Ag-NPs for SERS measurements. Complexing agents of ammonia and ethyl amine offered the best performances. The optimal concentration of complexing agent was found to be approximately six times the concentration of silver ions. With a reaction time of 2 min, the optimized concentrations of glucose and silver nitrate were 0.5 M and 50 mM, respectively. In general, the enhancement factor was on the order of 10(5) to 10(6) for the substrates prepared in this work.

Stable and efficient silver substrates for SERS spectroscopy

Silver substrates have been obtained, by depositing silver colloidal nanoparticles on a roughened silver plate treated with 1,10-phenanthroline, and checked by means of AFM microscopy and Raman spectroscopy. The ligand molecules are located between two silver substrates and undergo the SERS (Surface Enhanced Raman Scattering) enhancement of both the roughened silver plate and the silver colloidal layer deposited on it. These SERS-active substrates, which show the advantages of being stable with respect to the metal colloidal suspensions, along with an easy and reproducible preparation, can be very useful for catalytic and analytical applications of the SERS spectroscopy.