Development of an in vivo tissue-engineered valved conduit (type S biovalve) using a slitted mold

Application of Biosheets as Right Ventricular Outflow Tract Repair Materials in a Rat Model

Purposes

We report the experimental use of completely autologous biomaterials (Biosheets) made by “in-body tissue architecture” that could resolve problems in artificial materials and autologous pericardium. Here, Biosheets were implanted into full-thickness right ventricular outflow tract defects in a rat model. Their feasibility as a reparative material for cardiac defects was evaluated.

Methods

As the evaluation of mechanical properties of the biosheets, the elastic moduli of the biosheets and RVOT-free walls of rats were examined using a tensile tester. Biosheets and expanded polytetrafluoroethylene sheet were used to repair transmural defects surgically created in the right ventricular outflow tracts of adult rat hearts (n = 9, each patch group). At 4 and 12 weeks after the operation, the hearts were resected and histologically examined.

Results

The strength and elastic moduli of the biosheets were 421.3 ± 140.7 g and 2919 ± 728.9 kPa, respectively, which were significantly higher than those of the native RVOT-free walls (93.5 ± 26.2 g and 778.6 ± 137.7 kPa, respectively; P < 0.005 and P < 0.001, respectively). All patches were successfully implanted into the right ventricular outflow tract-free wall of rats. Dense fibrous adhesions to the sternum on the epicardial surface were also observed in 7 of 9 rats with ePTFE grafts, whereas 2 of 9 rats with biosheets. Histologically, the vascular-constructing cells were infiltrated into Biosheets. The luminal surfaces were completely endothelialized in all groups at each time point. There was also no accumulation of inflammatory cells.

Conclusions

Biosheets can be formed easily and have sufficient strength and good biocompatibility as a patch for right ventricular outflow tract repair in rats. Therefore, Biosheet may be a suitable material for reconstructive surgery of the right ventricular outflow tract.

Development of a stent-biovalve with round-shaped leaflets: in vitro hydrodynamic evaluation for transcatheter pulmonary valve implantation (TPVI)

This study evaluates a newly designed autologous heart valve-shaped tissue with a stent [stent-biovalve (SBV)] for transcatheter pulmonary valve implantation using the "in-body tissue architecture" technology. In the previously developed SBV with flat-shaped leaflets (FS-SBV), the valve could not close rapidly, because the leaflets were fixed in the open position, which induced regurgitant volume in the closing phase. Therefore, a novel mold to fabricate an SBV with round-shaped leaflets (RS-SBV) was developed, and its hydrodynamic performance with different valve diameters was evaluated in this study. A specially designed, self-expandable, stent-mounted, acrylic mold, which has 3 hemispheres, was placed in dorsal subcutaneous pouches of goats for 2 months. After extraction, the acrylic mold was removed from the implant, and a tubular tissue impregnated with the stent strut was obtained. Half of the tubular tissue with 3 hemispheres was completely folded in half inwards. The acrylic mold was designed, such that the folded half of the tubular tissue became the round-shaped leaflets. The 3 commissure parts were connected to form 3 leaflets, resulting in the preparation of the RS-SBV (internal diameter 25 mm). The RS-SBV closed more rapidly than the FS-SBV in a pulsatile mock circulation circuit under the pulmonary circulation conditions. The regurgitant fraction of the RS-SBV was approximately 6 %, which was lower than that of the FS-SBV. The appropriate pulmonary annulus diameter of the RS-SBV was from 24 to 25 mm based on the pressure difference and effective orifice area.