Effect of Nd:YAG laser parameters on the penetration depth of a representative Ni-Cr dental casting alloy

An in vitro study using confocal laser scanning microscopy to evaluate the marginal misfits of different implant-supported frameworks

PURPOSE

This study aimed to develop and evaluate a simple, non-destructive method for assessing the misfit and passivity of implant-retained prostheses frameworks.

MATERIALS AND METHODS

To simulate the rehabilitation of a mandible posterior partially edentulous area using 3-unit screw-retained frameworks supported by two implants were fabricated and divided into the following five groups (n = 10 in each group): OP = one-piece framework cast in Co-Cr with the conventional method (control-group); Co-Cr frameworks sectioned and welded by laser (=LAS) or tungsten inert gas (=TIG); Co-Cr CAD-CAM = milled Co-Cr framework; Zir CAD-CAM = milled zirconia framework. The horizontal |X| and vertical |Y| misfits were measured using confocal laser scanning microscopy with one or both screws tightened. Data were analyzed by a two-way ANOVA with repeated measures and Bonferroni correction (α = 0.05).

RESULTS

The greatest |X| misfit was observed in the OP group with both screws tightened (290 µm) and one screw tightened (388 and 340 µm). The conventional casting groups sectioned and welded by laser or TIG had lower mean values (235.35 µm, both screws tightened; and 275 µm, one screw tightened) than the OP framework. However, these values still exceeded those of the milled Co-Cr and zirconia frameworks (190 and 216 µm with both screws tightened). Across all reading conditions, every framework subjected to testing consistently maintained vertical |Y| misfit levels below the threshold of 53 µm; however, the milled frameworks exhibited higher vertical misfits than the frameworks obtained by the conventional cast method.

CONCLUSIONS

The frameworks, whether cast and sectioned with laser welding or milled from Co-Cr, exhibit improved marginal misfit and enhanced passive fit when compared to other fabrication methods. Additionally, the use of confocal laser scanning microscopy is highly effective for passivity and misfit analysis.

Evaluation of misfit and stress distribution in implant-retained prosthesis obtained by different methods

This study evaluated the vertical misfit, passivity, and stress distribution after tightening the screws of different prosthesis. Two implants were used to simulate the rehabilitation of partially edentulous mandible space from the second premolar to the second molar. 40 three-element screw-retained fixed dental prosthesis with distal cantilever were fabricated and divided into four groups according to the method of production of framework (n = 10): G1 = conventional casting one-piece framework, G2 = conventional casting sectioned and laser welding, G3 = conventional casting sectioned and tungsten inert gas (TIG) welding and G4 = framework obtained by CAD/CAM (computer-aided design/computer-aided manufacturing) system. The vertical misfits (both screws tightened) and the passive fit (one screw tightened) were measured under a comparator optical microscope. The data was submitted to Shapiro-Wilk test to enable comparison with ANOVA followed by Tukey with Bonferroni adjust (α = .05). The qualitative analysis of the stress distribution was performed by the photoelastic method. The vertical misfit (both screws tightened) of the G2 (24 μm) and G3 (27 μm) were significantly higher than G4 (10 μm) (p = 0,006). The passive fit (for the non-tightened) of the G1(64 μm) and G3 (61 μm) were significantly higher than the G4 (32 μm) (p=0,009). G1 showed high stress between the implants in the photoelastic analysis and G4 presented lower stress. In conclusion, CAD/CAM method results in less vertical misfit, more passivity, and consequently better stress distribution to the bone.

Mechanical and interfacial characterization of laser welded Co-Cr alloy with different joint configurations

PURPOSE

The mechanical and interfacial characterization of laser welded Co-Cr alloy with two different joint designs.

MATERIALS AND METHODS

Dumbbell cast specimens (n=30) were divided into 3 groups (R, I, K, n=10). Group R consisted of intact specimens, group I of specimens sectioned with a straight cut, and group K of specimens with a 45° bevel made at the one welding edge. The microstructure and the elemental distributions of alloy and welding regions were examined by an SEM/EDX analysis and then specimens were loaded in tension up to fracture. The tensile strength (TS) and elongation (ε) were determined and statistically compared among groups employing 1-way ANOVA, SNK multiple comparison test (α=.05) and Weibull analysis where Weibull modulus m and characteristic strength σ_ο were identified. Fractured surfaces were imaged by a SEM.

RESULTS

SEM/EDX analysis showed that cast alloy consists of two phases with differences in mean atomic number contrast, while no mean atomic number was identified for welded regions. EDX analysis revealed an increased Cr and Mo content at the alloy-joint interface. All mechanical properties of group I (TS, ε, m and σ_ο) were found inferior to R while group K showed intermediated values without significant differences to R and I, apart from elongation with group R. The fractured surfaces of all groups showed extensive dendritic pattern although with a finer structure in the case of welded groups.

CONCLUSION

The K shape joint configuration should be preferred over the I, as it demonstrates improved mechanical strength and survival probability.