Laser Nd:YAG patterning enhance human osteoblast behavior on zirconia implants

Cell Biological and Antibacterial Evaluation of a New Approach to Zirconia Implant Surfaces Modified with MTA

Peri-implantitis continues to be one of the major reasons for implant failure. We propose a new approach to the incorporation of MTA into zirconia implant surfaces with Nd:YAG laser and investigate the biological and the microbiological responses of peri-implant cells. Discs of zirconia stabilized with yttria and titanium were produced according to the following four study groups: Nd:YAG laser-textured zirconia coated with MTA (Zr MTA), Nd:YAG laser-textured zirconia (Zr textured), polished zirconia discs, and polished titanium discs (Zr and Ti). Surface roughness was evaluated by contact profilometry. Human osteoblasts (hFOB), gingival fibroblasts (HGF hTERT) and S. oralis were cultured on discs. Cell adhesion and morphology, cell differentiation markers and bacterial growth were evaluated. Zr textured roughness was significantly higher than all other groups. SEM images reveal cellular adhesion at 1 day in all samples in both cell lines. Osteoblasts viability was lower in the Zr MTA group, unlike fibroblasts viability, which was shown to be higher in the Zr MTA group compared with the Zr textured group at 3 and 7 days. Osteocalcin and IL-8 secretion by osteoblasts were higher in Zr MTA. The Zr textured group showed higher IL-8 values released by fibroblasts. No differences in S. oralis CFUs were observed between groups. The present study suggests that zirconia implant surfaces coated with MTA induced fibroblast proliferation and osteoblast differentiation; however, they did not present antibacterial properties.

Influence of nanosecond laser surface patterning on dental 3Y-TZP: Effects on the topography, hydrothermal degradation and cell response

OBJECTIVES

Laser surface micropatterning of dental-grade zirconia (3Y-TZP) was explored with the objective of providing defined linear patterns capable of guiding bone-cell response.

METHODS

A nanosecond (ns-) laser was employed to fabricate microgrooves on the surface of 3Y-TZP discs, yielding three different groove periodicities (i.e., 30, 50 and 100 µm). The resulting topography and surface damage were characterized by confocal laser scanning microscopy (CLSM) and scanning electron microscopy (SEM). X-Ray diffraction (XRD) and Raman spectroscopy techniques were employed to assess the hydrothermal degradation resistance of the modified topographies. Preliminary biological studies were conducted to evaluate adhesion (6 h) of human mesenchymal stem cells (hMSC) to the patterns in terms of cell number and morphology. Finally, Staphylococcus aureus adhesion (4 h) to the microgrooves was investigated.

RESULTS

The surface analysis showed grooves of approximately 1.8 µm height that exhibited surface damage in the form of pile-up at the edge of the microgrooves, microcracks and cavities. Accelerated aging tests revealed a slight decrease of the hydrothermal degradation resistance after laser patterning, and the Raman mapping showed the presence of monoclinic phase heterogeneously distributed along the patterned surfaces. An increase of the hMSC area was identified on all the microgrooved surfaces, although only the 50 µm periodicity, which is closer to the cell size, significantly favored cell elongation and alignment along the grooves. A decrease in Staphylococcus aureus adhesion was observed on the investigated micropatterns.

SIGNIFICANCE

The study suggests that linear microgrooves of 50 µm periodicity may help in promoting hMSC adhesion and alignment, while reducing bacterial cell attachment.

Nd:YAG laser therapy on postoperative pain, swelling, and trismus after mandibular third molar surgery: a randomized double-blinded clinical study

This study aims to evaluate the effect of Nd:YAG laser therapy (NdLT) on postoperative pain, swelling, and trismus after mandibular third molar (M3) surgery. Three hundred patients were randomly divided into the Nd group (n = 100), medication group (n = 100), and Nd+medication (Nd+m) group (n = 100). The WHARFE classification system was used to assess surgical difficulty. After surgery, the Nd group was irradiated by the Nd:YAG laser in very long-pulsed mode (VLP, pulse duration 1 ms, 20 Hz, 4 W, R21-C3) in 6 regions of the extraction socket with a total energy of 300 J. For the medication group, dexamethasone 0.75 mg and loxoprofen 60 mg were prescribed immediately and every 12 h thereafter for 3 days. The Nd+m group received both treatments mentioned above. Pain assessment was performed at 6, 24, 48, and 72 h postoperatively using the visual analog scale (VAS). Swelling was evaluated by changes in the distance from (1) the tragus to the labial commissure, (2) the tragus to the pogonion, and (3) the mandibular angle to the lateral canthus preoperatively and 72 h postoperatively. Trismus was assessed by the change in maximum mouth opening. Groups Nd and Nd+m had lower VAS scores at 6 h, 24 h, and 48 h (F = 13.80, p = 0.00), but the difference between the two groups was not significant (F = 1.34, p = 0.11). However, no significant difference was observed at 72 h (p = 0.10). There was no significant difference in swelling or trismus among the three groups (p > 0.05). NdLT is an effective approach to improve complications after M3 surgery.

Bio-Piezoelectric Ceramic Composites for Electroactive Implants-Biological Performance

Barium titanate (BaTiO3) piezoelectric ceramic may be a potential alternative for promoting osseointegration due to its piezoelectric properties similar to bone electric potentials generated in loading function. In this sense, the aim of this in vitro study was to evaluate the cellular response of human osteoblasts and gingival fibroblasts as well as the impact on S. oralis when in contact with BaTiO3 functionalized zirconia implant surfaces with piezoelectric properties. Zirconia discs with BaTiO3 were produced and contact poling (piezo activation) was performed. Osteoblasts (hFOB 1.19), fibroblasts (HGF hTERT) and S. oralis were culture on discs. Cell viability and morphology, cell differentiation markers, bacterial adhesion and growth were evaluated. The present study suggests that zirconia composite surfaces with the addition of piezoelectric BaTiO3 are not cytotoxic to peri-implant cells. Also, they seem to promote a faster initial osteoblast differentiation. Moreover, these surfaces may inhibit the growth of S. oralis by acting as a bacteriostatic agent over time. Although the piezoelectric properties do not affect the cellular inflammatory profile, they appear to enable the initial adhesion of bacteria, however this is not significant over the entire testing period. Furthermore, the addition of non-poled BaTiO3 to zirconia may have a potential reduction effect on IL-6 mediated-inflammatory activity in fibroblasts.

Human Gingival Fibroblast and Osteoblast Behavior on Groove-Milled Zirconia Implant Surfaces

Two type of cells representing periodontal hard tissues (osteoblasts) and soft tissues (fibroblasts) were evaluated in response to microgroove-milled zirconia surfaces. A total of 90 zirconia discs were randomly assigned to four width-standardized milling microgroove-textured groups and a control group without grooves (UT). The sandblast and acid-etch protocol were applied to all samples. Both cell lines were cultured on zirconia discs from 1 day up to 14 days. Cell morphology and adhesion were evaluated after 1 day of culturing. Cell viability and proliferation of the cells were measured. Alkaline phosphatase activity, collagen I, osteopontin, interleukin 1β and interleukin 8 secretions were assessed at predefined times. The results obtained were presented in the form of bar graphs as means and standard deviations. Multi comparisons between groups were evaluated using two-away ANOVA or Mann−Whitney tests, and a p-value < 0.05 was established. Group comparisons with regard to cell viability, proliferation and secretion of collagen I, interleukin-1β and interleukin 8 revealed no statistically significant differences. The alkaline phosphatase activity and osteopontin secretion were significantly higher in the group with a large groove compared to the small one and the control group. Nevertheless, the viability of gingival and bone cells did not appear to be affected by the milled microgroove texture compared to the conventional sandblasted and acid-etched texture, but they seem to influence osteoblasts’ cellular differentiation.

Rare earth smart nanomaterials for bone tissue engineering and implantology: Advances, challenges, and prospects

Bone grafts or prosthetic implant designing for clinical application is challenging due to the complexity of integrated physiological processes. The revolutionary advances of nanotechnology in the biomaterial field expedite and endorse the current unresolved complexity in functional bone graft and implant design. Rare earth (RE) materials are emerging biomaterials in tissue engineering due to their unique biocompatibility, fluorescence upconversion, antimicrobial, antioxidants, and anti-inflammatory properties. Researchers have developed various RE smart nano-biomaterials for bone tissue engineering and implantology applications in the past two decades. Furthermore, researchers have explored the molecular mechanisms of RE material-mediated tissue regeneration. Recent advances in biomedical applications of micro or nano-scale RE materials have provided a foundation for developing novel, cost-effective bone tissue engineering strategies. This review attempted to provide an overview of RE nanomaterials' technological innovations in bone tissue engineering and implantology and summarized the osteogenic, angiogenic, immunomodulatory, antioxidant, in vivo bone tissue imaging, and antimicrobial properties of various RE nanomaterials, as well as the molecular mechanisms involved in these biological events. Further, we extend to discuss the challenges and prospects of RE smart nano-biomaterials in the field of bone tissue engineering and implantology.