Repair bond strength of different CAD-CAM ceramics after various surface treatments combined with laser irradiation

Repair protocols for indirect monolithic restorations: a literature review

Despite the advancements in indirect monolithic restorations, technical complications may occur during function. To overcome this issues, intraoral repair using resin composite is a practical and low-cost procedure, being able to increase the restoration's longevity. This review aimed to evaluate the need for repair and suggest a standardized repair protocol to the main indirect restorative materials. For this, studies were surveyed from PubMed with no language or date restriction, to investigate the scientific evidence of indirect monolithic restoration repair with direct resin composite. A classification to guide clinical decisions was made based on the FDI World Dental Federation criteria about defective indirect restorations considering esthetic and functional standards, along with the patient's view, to decide when polishing, repairing or replacing a defective restoration. Based on 38 surveyed studies, different resin composite intraoral repair protocols, that included mechanical and chemical aspects, were defined depending on the substrate considering resin-based, glass-ceramic or zirconia restorations. The presented criteria and protocols were developed to guide the clinician's decision-making process regarding defective indirect monolithic restorations, prolonging longevity and increasing clinical success.

Repair of monolithic zirconia restorations with different direct resin composites: effect on the fatigue bonding and mechanical performance

OBJECTIVE

The study aims to evaluate the shear bond and flexural strength fatigue behavior of yttrium-stabilized zirconia (4YSZ) repaired using different resin composites.

MATERIALS AND METHODS

Cylindric specimens of 4YSZ were obtained for the bond strength (Ø = 6 mm, 1.5 mm of thickness) and biaxial flexural strength (Ø = 15 mm, 1 mm of thickness) fatigue tests and divided into 3 groups according to the repair resin composite: EVO (nanohybrid), BULK (bulk-fill), and FLOW (flowable). The zirconia surface was air-abraded with alumina particles, a 10-methacryloyloxydecyl dihydrogen phosphate (10-MDP) primer was applied, and the resin composite was build-up over the zirconia. Fatigue shear bond strength and flexural fatigue strength tests were performed (n = 15). One-way ANOVA and Tukey post hoc tests were carried out for both outcomes, besides scanning electron microscopy and finite element analysis.

RESULTS

The repair material affected the fatigue shear bond strength of zirconia ceramic. The BULK group (18.9 MPa) depicted higher bond strength values than FLOW (14.8 MPa) (p = 0.04), while EVO (18.0 MPa) showed similar results to both groups. No effect was observed for the mechanical behavior (p = 0.53). The stress distribution was similar for all groups.

CONCLUSION

The repair of yttrium-stabilized zirconia (4YSZ) ceramics with bulk-fill resin composites was the best option for high fatigue bond strength. However, the fatigue mechanical performance was similar regardless of the applied repair material.

CLINICAL RELEVANCE

The repair of yttrium-stabilized zirconia (4YSZ) monolithic restorations may be performed with nanohybrid and bulk-fill resin composites in order to promote longevity in the treatment.

Zirconia-Reinforced Lithium Silicate Ceramic in Digital Dentistry: A Comprehensive Literature Review of Our Current Understanding

Zirconia-reinforced lithium silicate (ZLS) ceramic is a new innovative dental material with unique a chemical composition that is designed to combine harmoniously with the appropriate optical properties of lithium disilicate and the enhanced mechanical strength of zirconia. A thorough understanding of ZLS materials is essential for both clinicians and dental technicians. At present, the mechanical behavior and optical properties of the ZLS ceramic system have not been extensively researched, and there is still a lack of consensus regarding the fabrication process and clinical behavior of ZLS all-ceramic restorations. The aim of the present study was to present a selection of comprehensive information concerning zirconia-reinforced lithium silicate ceramics and their optical and mechanical properties, as well as to assess data regarding cementation procedures and clinical outcomes for ZLS all-ceramic restorations. Three electronic databases (PubMed, Web of Science, and the Cochrane Library) were used for the research by two independent reviewers. The search was limited to articles published in the English language, as well as clinical and in vitro studies of color and studies on mechanical behavior and the cementation procedures of ZLS restorations. The exclusion criteria comprised abstracts, questionnaire-based studies, case reports, literature reviews, and studies that were not available in English. Zirconia-reinforced lithium-silicate-based ceramic presents a unique and complex microstructure that increases mechanical resistance but decreases aesthetic appearance, especially its translucency, due to tetragonal zirconia content. A material's thickness, the color of the underlying tooth structure, and the resin cement shade are important factors that influence the final shade and aesthetic appearance of ZLS restorations. Mechanical properties, which are defined by the fracture toughness, flexural strength, elastic modulus, and hardness of ZLS ceramic are higher compared to feldspathic, lithium disilicate, and hybrid ceramics, as well as resin nanoceramics; however, they are lower than translucent or high-translucency zirconia. Acid etching, sandblasting, and laser etching represent the most used methods to prepare the ZLS restoration surfaces for proper bonding procedures.