Effect of the incorporation of hydroxyapatite on the diametral tensile strength of conventional and hybrid glass ionomer cements

Evaluating antimicrobial, cytotoxic and immunomodulatory effects of glass ionomer cement modified by chitosan and hydroxyapatite

OBJECTIVES

This study aimed to assess antimicrobial efficacy, cytotoxicity, and cytokine release (IL-1b, IL-6, IL-10, TNF-α) from human dental pulp stem cells (hDPSCs) of chitosan (CH) and hydroxyapatite (HAp)-modified glass ionomer cements (GIC).

METHODS

GICs with varied CH and HAp concentrations (0 %, 0.16 %, 2 %, 5 %, 10 %) were tested against S. mutans for 24 h or 7 days. Antimicrobial activity was measured using an MTT test. Cytotoxicity evaluation followed for optimal concentrations, analyzing mitochondrial activity and apoptosis in hDPSCs. Cytokine release was assessed with MAGPIX. Antimicrobial analysis used Shapiro-Wilk, Kruskal-Wallis, and Dunnett tests. Two-way ANOVA, Tukey, and Dunnett tests were applied for hDP metabolism and cytokine release.

RESULTS

CH 2 % and HAp 5 % significantly enhanced GIC antimicrobial activity, especially after seven days. In immediate analysis, all materials showed reduced mitochondrial activity compared to the control. After 24 h, CH demonstrated mitochondrial metabolism similar to the control. All groups exhibited mild cytotoxicity (∼30 % cell death). Only IL-6 was influenced, with reduced release in experimental groups.

SIGNIFICANCE

CH 2 % and HAp 5 % were most effective for antibacterial effects. GIC-CH 2 % emerged as the most promising formula, displaying significant antibacterial effects with reduced hDPSC toxicity.

Glass ionomer cement with calcium-releasing particles: Effect on dentin mineral content and mechanical properties

OBJECTIVE

to evaluate the effect a glass ionomer cement (GIC) containing hydroxyapatite (HAp) or calcium silicate (CaSi) particles on mineral content and mechanical properties of demineralized dentin. Ion release and compressive strength (CS) of the cements were also evaluated.

METHODS

GIC (Fuji 9 Gold Label, GC), GIC+ 5%HAp and GIC+ 5%CaSi (by mass) were evaluated. Ion release was determined by induced coupled plasma optical emission spectroscopy (Ca2+/Sr2+) or ion-specific electrode (F-) (n = 3). A composite (Filtek Z250, 3 M ESPE) was used as control in remineralization tests. Demineralized dentin discs were kept in contact with materials in simulated body fluid (SBF) at 37 °C for eight weeks. Mineral:matrix ratio (MMR) was determined by ATR-FTIR spectroscopy (n = 5). Dentin hardness (H) and elastic modulus (E) were determined by nanoindentation (n = 10). CS was tested after 24 h and 7d in deionized water (n = 12). Data were analyzed by ANOVA/Tukey test (α = 0.05).

RESULTS

Ca2+ and Sr2+ release was higher for the modified materials (p < 0.05). Only GIC+ 5%HAp showed higher F- release than the control (p < 0.05). All groups showed statistically significant increases in MMR, with no differences among them after 8 weeks (p > 0.05). No differences in dentin H or E were observed among groups (p > 0.05). HAp-modified GIC showed increased initial CS, while adding CaSi had the opposite effect (p < 0.05). After 7 days, GIC+ 5%CaSi presented lower CS in relation to control and GIC+ 5%HAp (p < 0.05).

SIGNIFICANCE

GIC modification with HAp or CaSi affected CS and increased ion release; however, none of the groups showed evidence of dentin remineralization in comparison to the negative control.

Evaluation of the Mechanical Properties of Three Resin-Modified Glass-Ionomer Materials

This study is aimed at evaluating the flexural strength (FS), fracture toughness (FT), and diametral tensile strength (DTS) of three resin-modified glass-ionomer cements (RMGICs): Ketac Nano, Riva Light Cure, and Fuji II LC. One hundred twenty specimens were prepared from the RMGIC materials ( $n=10$ ). The cements were mixed and inserted into different mould sizes according to the test performed: FS: rectangular Teflon mould ( $32\text{mm}\times 3.15\text{mm}\times 2\text{mm}$ ); FT: notchless triangular prism (NTP) Teflon mould ( $6\text{mm}\times 6\text{mm}\times 6\text{mm}\times 12\text{mm}$ ); and DTS: ring road stainless steel mould ( $6\text{mm}\times 3\text{mm}$ ). Specimens were light cured for 20 seconds on each surface and stored in distilled water at ${37}^{°}\text{C}\pm 2^{°}\text{C}$ for seven days prior to tests. To evaluate the influence of storage in the mechanical properties of the RMGIs, specimens tested for DTS were stored in distilled water at ${37}^{°}\text{C}\pm 2^{°}\text{C}$ for 32 days prior to test. Data were analyzed by ANOVA and Tukey’s test ( $\alpha =0.05$ ). Fuji II LC presented significantly higher values for all tests employed when compared to Ketac Nano and Riva LC RMGIs. There was no significant difference on DTS before and after the 32-day storage for each material. Fuji II LC presented superior mechanical properties when compared to Ketac Nano, and Riva LC storage showed no influence on the mechanical properties of the RMGI materials tested.